A number of blocks of the high-strength alpha–beta titanium alloy Ti–6Al–2Sn–4Zr–6Mo (Ti-6246) were manufactured using direct laser fabrication. Two processing methods were investigated; one of which used a high-power (18 kW) CO2 laser, the other using a (4 kW) Nd-YAG laser. Following manufacture, the blocks were sectioned and mechanically tested to compare the properties of material produced using the two processes. The mechanical assessment involved a combination of room temperature tensile testing and fracture toughness measurements.
The results revealed that the Ti-6246 produced using both processing routes exhibited a low ductility (<3% elongation). The fracture toughness figures were, however, acceptable. The low ductility was thought to be linked to the presence of a large transformed beta grain size together with the presence of grain boundary alpha.
[1]
Xinhua Wu,et al.
Direct laser fabrication and microstructure of a burn-resistant Ti alloy
,
2002
.
[2]
M. L. Griffith,et al.
Solidification in direct metal deposition by LENS processing
,
2001
.
[3]
L. Xue,et al.
Free-form laser consolidation for producing metallurgically sound and functional components
,
2000
.
[4]
S. L. Semiatin,et al.
The laser additive manufacture of Ti-6Al-4V
,
2001
.
[5]
Francis H. Froes,et al.
Producing titanium aerospace components from powder using laser forming
,
2000
.