Needleless electrospinning of polystyrene fibers with an oriented surface line texture

We have demonstrated that polystyrene (PS) nanofibers having an ordered surface line texture can be produced on a large scale from a PS solution of acetone and N, N′-dimethylformamide (2/1, vol/vol) by a needleless electrospinning technique using a disc as fiber generator. The formation of the unusual surface feature was investigated and attributed to the voids formed on the surface of jets due to the fast evaporation of acetone at the early stage of electrospinning, and subsequent elongation and solidification turning the voids into ordered lines on fiber surface. In comparison with the nanofibers electrospun by a conventional needle electrospinning using the same solution, the disc electrospun fibers were finer with similar diameter distribution. The fiber production rate for the disc electrospinning was 62 times higher than that of the conventional electrospinning. Fourier transform infrared spectroscopy and X-ray diffractionmeasurements indicated that the PS nanofibers produced from the two electrospinning techniques showed no significant difference in chemical component, albeit slightly higher crystallinity in the disc spun nanofibers.

[1]  Younan Xia,et al.  Electrospinning of Nanofibers: Reinventing the Wheel? , 2004 .

[2]  S. Krimm,et al.  Infrared spectra of high polymers. VII. Polyacrylonitrile , 1958 .

[3]  Younan Xia,et al.  Electrospinning of polymeric and ceramic nanofibers as uniaxially aligned arrays , 2003 .

[4]  Myung-Seob Khil,et al.  Characterization of nano-structured poly(ε-caprolactone) nonwoven mats via electrospinning , 2003 .

[5]  Samuel Krimm,et al.  Infrared spectra of high polymers , 1960 .

[6]  Jayant Kumar,et al.  Electrospun Nanofibrous Membranes for Highly Sensitive Optical Sensors , 2002 .

[7]  L. Lim,et al.  Processing technologies for poly(lactic acid) , 2008 .

[8]  A. Sutti,et al.  Electrospinning of nanofibres with parallel line surface texture for improvement of nerve cell growth , 2011 .

[9]  Guangming Chen,et al.  FTIR Spectra, Thermal Properties, and Dispersibility of a Polystyrene/Montmorillonite Nanocomposite , 2001 .

[10]  N. Peppas,et al.  Use of ATR-FTIR to study interdiffusion in polystyrene and poly(vinyl methyl ether) , 1993 .

[11]  E. B. Gowd,et al.  Crystalline Transitions of the Clathrate (δ) Form of Syndiotactic Polystyrene during Heating: Studies Using High-Temperature X-ray Diffraction , 2002 .

[12]  H. Duan,et al.  Superhigh-throughput needleless electrospinning using a rotary cone as spinneret. , 2010, Small.

[13]  Darrell H. Reneker,et al.  Flat polymer ribbons and other shapes by electrospinning , 2001 .

[14]  Eyal Zussman,et al.  Upward needleless electrospinning of multiple nanofibers , 2004 .

[15]  Hongxia Wang,et al.  Self‐Crimping Bicomponent Nanofibers Electrospun from Polyacrylonitrile and Elastomeric Polyurethane , 2005 .

[16]  Andreas Greiner,et al.  Nanostructured Fibers via Electrospinning , 2001 .

[17]  S. Krimm,et al.  Infrared spectra of high polymers. VI. Polystyrene , 1958 .

[18]  Sing Yian Chew,et al.  The application of nanofibrous scaffolds in neural tissue engineering. , 2009, Advanced drug delivery reviews.

[19]  Gyula J. Vancso,et al.  Transparent Nanocomposites with Ultrathin, Electrospun Nylon-4,6 Fiber Reinforcement , 1999 .

[20]  A. Imhof.  Preparation and Characterization of Titania-Coated Polystyrene Spheres and Hollow Titania Shells , 2001 .

[21]  Seeram Ramakrishna,et al.  Electrospun Nanofibers: Solving Global Issues , 2006 .

[22]  Seeram Ramakrishna,et al.  Preparation of Core−Shell Structured PCL-r-Gelatin Bi-Component Nanofibers by Coaxial Electrospinning , 2004 .

[23]  Tong Lin,et al.  Needleless electrospinning. I. A comparison of cylinder and disk nozzles , 2009 .

[24]  Tong Lin,et al.  The charge effect of cationic surfactants on the elimination of fibre beads in the electrospinning of polystyrene , 2004 .

[25]  Chaobo Huang,et al.  Electrospun polymer nanofibres with small diameters , 2006, Nanotechnology.