Facile and green synthesis of (La0.95Eu0.05)2O2S red phosphors with sulfate-ion pillared layered hydroxides as a new type of precursor: controlled hydrothermal processing, phase evolution and photoluminescence

Abstract This study presents a facile and green route for the synthesis of (La0.95Eu0.05)2O2S red phosphors of controllable morphologies, with the sulfate-type layered hydroxides of Ln2(OH)4SO4·2H2O (Ln = La and Eu) as a new type of precursor. The technique takes advantage of the fact that the precursor has had the exact Ln:S molar ratio of the targeted phosphor, thus saving the hazardous sulfurization reagents indispensable to traditional synthesis. Controlled hydrothermal processing at 120 °C yielded phase-pure Ln2(OH)4SO4·2H2O crystallites in the form of either nanoplates or microprisms, which can both be converted into Ln2O2S phosphor via a Ln2O2SO4 intermediate upon annealing in flowing H2 at a minimum temperature of ∼ 700 °C. The nanoplates collapse into relatively rounded Ln2O2S particles while the microprisms retain well their initial morphologies at 1 200 °C, thus yielding two types of red phosphors. Photoluminescence excitation (PLE) studies found two distinct charge transfer (CT) excitation bands of O2− → Eu3+ at ∼ 270 nm and S2− → Eu3+ at ∼ 340 nm for the Ln2O2S phosphors, with the latter being stronger and both significantly stronger than the intrinsic intra-f transitions of Eu3+. The two types of phosphors share high similarities in the positions of PLE/PL (photoluminescence) bands and both show the strongest red emission at 627 nm (5D0 → 7F2 transition of Eu3+) under S2− → Eu3+ CT excitation at 340 nm. The PLE/PL intensities show clear dependence on particle morphology and calcination temperature, which were investigated in detail. Fluorescence decay analysis reveals that the 627 nm red emission has a lifetime of ∼ 0.5 ms for both types of the phosphors.

[1]  Y. Sakka,et al.  Luminescent metal nanoclusters: controlled synthesis and functional applications , 2013, Science and technology of advanced materials.

[2]  E. Mihóková,et al.  Luminescent materials: probing the excited state of emission centers by spectroscopic methods , 2014 .

[3]  Y. Sakka,et al.  Layered rare-earth hydroxide and oxide nanoplates of the Y/Tb/Eu system: phase-controlled processing, structure characterization and color-tunable photoluminescence via selective excitation and efficient energy transfer , 2013, Science and technology of advanced materials.

[4]  Y. Sakka,et al.  Effective lattice stabilization of gadolinium aluminate garnet (GdAG) via Lu3+ doping and development of highly efficient (Gd,Lu)AG:Eu3+ red phosphors , 2012, Science and technology of advanced materials.

[5]  Y. Sakka,et al.  Monodisperse colloidal spheres for (Y,Eu)2O3 red-emitting phosphors: establishment of processing window and size-dependent luminescence behavior , 2011, Science and technology of advanced materials.

[6]  Kristin N. Johnson,et al.  Effect of inclining strain on the crystal lattice along an extended series of lanthanide hydroxysulfates Ln(OH)SO4 (Ln = Pr-Yb, except Pm). , 2011, Inorganic chemistry.

[7]  R. Ma,et al.  Ln2(OH)4SO4·nH2O (Ln = Pr to Tb; n ∼ 2): A New Family of Layered Rare-Earth Hydroxides Rigidly Pillared by Sulfate Ions , 2010 .

[8]  R. Ma,et al.  Synthesis and properties of well-crystallized layered rare-earth hydroxide nitrates from homogeneous precipitation. , 2009, Inorganic chemistry.

[9]  W. Cranton,et al.  Temperature dependent characteristics of La2O2S: Ln [Ln = Eu, Tb] with various Ln concentrations over 5-60 °C , 2009 .

[10]  T. Prior,et al.  Synthesis and Crystal Structures of New Lanthanide Hydroxyhalide Anion Exchange Materials, Ln2(OH)5X·1.5H2O (X = Cl, Br; Ln = Y, Dy, Er, Yb) , 2008 .

[11]  Hongwei Song,et al.  Size and Concentration Effects on the Photoluminescence of La2O2S:Eu3+ Nanocrystals , 2008 .

[12]  R. Ma,et al.  General synthesis and structural evolution of a layered family of Ln8(OH)20Cl4 x nH2O (Ln = Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and Y). , 2008, Journal of the American Chemical Society.

[13]  Shihong Zhou,et al.  Combustion synthesis and luminescent properties of the Eu3+-doped yttrium oxysulfide nanocrystalline , 2008 .

[14]  Xiaodong Li,et al.  Tb3+- and Eu3+-Doped Lanthanum Oxysulfide Nanocrystals. Gelatin-Templated Synthesis and Luminescence Properties , 2008 .

[15]  L. Cao,et al.  Preparation and surface effect analysis of trivalent europium-doped nanocrystalline La2O2S. , 2005, The journal of physical chemistry. B.

[16]  Emil Indrea,et al.  Synthesis and characterisation of rare earth oxysulphide phosphors. I. Studies on the preparation of Gd2O2S:Tb phosphor by the flux method , 2004 .

[17]  M. Davolos,et al.  Yttrium oxysulfide nanosized spherical particles doped with Yb and Er or Yb and Tm: efficient materials for up-converting phosphor technology field , 2004 .

[18]  M. Meneses-Nava,et al.  Preparation, photo- and thermo-luminescence characterization of Tb3+ and Ce3+ doped nanocrystalline Y3Al5O12 exposed to UV-irradiation , 2004 .

[19]  R. Jagannathan,et al.  Eu3+ doped yttrium oxysulfide nanocrystals – crystallite size and luminescence transition(s) , 2004 .

[20]  Ru‐Shi Liu,et al.  Synthesis and luminescent properties of a new yellowish-orange afterglow phosphor Y2O2S :Ti, Mg , 2003 .

[21]  J. Llanos,et al.  Synthesis, physical and optical properties, and electronic structure of the rare-earth oxysulfides Ln2O2S (Ln=Sm, Eu) , 2002 .

[22]  Y. Hatanaka,et al.  Synthesis and Characterization of Fine Particle Y 2 O 2 S : Eu Red Phosphor at Low‐Voltage Excitation , 2000 .

[23]  Jian Yang,et al.  Synthesis and Formation Mechanism of La2O2S via a Novel Solvothermal Pressure-Relief Process , 1999 .

[24]  S. Cho,et al.  A New Synthetic Method to Prepare Spherical Phosphors for Emissive Screen Applications , 1998 .

[25]  G. Blasse,et al.  Energy transfer between Eu3+ ions in a lattice with two different crystallographic sites: Y2O3:Eu3+, Gd2O3:Eu3+ and Eu2O3 , 1987 .

[26]  L. Thompson Chapter 25 Complexes , 1979 .

[27]  V. Pecharsky,et al.  Handbook on the physics and chemistry of rare earths , 1979 .

[28]  R. D. Shannon Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides , 1976 .

[29]  J. A. Gadsden Infrared Spectra of Minerals and Related Inorganic Compounds , 1975 .

[30]  B. Judd,et al.  OPTICAL ABSORPTION INTENSITIES OF RARE-EARTH IONS , 1962 .

[31]  G. S. Ofelt Intensities of Crystal Spectra of Rare‐Earth Ions , 1962 .