The effect of through-thickness compressive stress on mode II interlaminar fracture toughness

Abstract The effect of through-thickness compressive stress on mode II interlaminar fracture toughness is investigated experimentally and replicated numerically. The modified Transverse Crack Tensile specimen recently proposed by the authors is used, together with an experimental device designed to apply a constant transverse compressive stress on the surface of the specimen. Experiments are conducted using IM7/8552 specimens for different compressive stresses, ranging from 0 to 100 MPa, covering all the practical applications commonly encountered in the aeronautical industry (e.g., tightened filled holes or bolted joints). It is shown that mode II interlaminar fracture toughness increases with the applied compressive through-thickness stress. Finally, experiments are replicated using appropriate numerical models based on cohesive elements that take into account frictional effects. A good agreement between numerical predictions and experiments is found.

[1]  H. Schürmann,et al.  FAILURE ANALYSIS OF FRP LAMINATES BY MEANS OF PHYSICALLY BASED PHENOMENOLOGICAL MODELS , 1998 .

[2]  Fu-Kuo Chang,et al.  Experimental study on clamping effects on the tensile strength of composite plates with a bolt-filled hole , 1999 .

[3]  P. Camanho,et al.  Numerical Simulation of Mixed-Mode Progressive Delamination in Composite Materials , 2003 .

[4]  Endel Iarve,et al.  Mesh‐independent matrix cracking and delamination modeling in laminated composites , 2011 .

[5]  Pedro P. Camanho,et al.  Accurate simulation of delamination growth under mixed-mode loading using cohesive elements: Definition of interlaminar strengths and elastic stiffness , 2010 .

[6]  Pedro P. Camanho,et al.  Three-dimensional invariant-based failure criteria for fibre-reinforced composites , 2015 .

[7]  K. Rhee.  Hydrostatic Pressure Effect on the Fracture Toughness of Unidirectional (0-deg) Graphite/Epoxy Laminated Composites , 2000 .

[8]  L. Hart-Smith.  Design and Analysis of Bolted and Riveted Joints in Fibrous Composite Structures , 2003 .

[9]  P. Camanho,et al.  Simulation of delamination by means of cohesive elements using an explicit finite element code , 2009 .

[10]  P. Linde,et al.  A finite fracture mechanics model for the prediction of the open-hole strength of composite laminates , 2012 .

[11]  L. Sluys,et al.  A numerical investigation into the size effect in the transverse crack tension test for mode II delamination , 2013 .

[12]  P. Camanho,et al.  Three-dimensional failure criteria for fiber-reinforced laminates , 2013 .

[13]  Pedro P. Camanho,et al.  A semi-analytical method to predict net-tension failure of mechanically fastened joints in composite laminates , 2013 .

[14]  L. J. Sluys,et al.  Computational analysis of progressive failure in a notched laminate including shear nonlinearity and fiber failure , 2010 .

[15]  Seung Goo Lee,et al.  Effect of hydrostatic pressure on the elastic work factor, ηel and fracture toughness determination of unidirectional composites using ηel , 2003 .

[16]  Pedro P. Camanho,et al.  A damage model for the simulation of delamination in advanced composites under variable-mode loading , 2006 .

[17]  K. Rhee,et al.  Experimental investigation on the compressive characteristics of multi-directional graphite/epoxy composites under hydrostatic pressure environment , 2003 .

[18]  Pedro P. Camanho,et al.  Measurement of the compressive crack resistance curve of composites using the size effect law , 2014 .

[19]  Bruno Castanié,et al.  Experimental analysis of failures in filled hole compression tests of carbon/epoxy laminate , 2010 .

[20]  M. A. Crisfield,et al.  Progressive Delamination Using Interface Elements , 1998 .

[21]  M. Benzeggagh,et al.  Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus , 1996 .

[22]  Pierre Ladevèze,et al.  On the validation of a damage mesomodel for laminated composites by means of open-hole tensile tests on quasi-isotropic laminates , 2011 .

[23]  Pedro P. Camanho,et al.  An engineering solution for mesh size effects in the simulation of delamination using cohesive zone models , 2007 .

[24]  Vincent B. C. Tan,et al.  Damage progression by the element-failure method (EFM) and strain invariant failure theory (SIFT) , 2005 .

[25]  P. Camanho,et al.  Prediction of size effects in notched laminates using continuum damage mechanics , 2007 .

[26]  J. Whitney,et al.  Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations , 1974 .

[27]  C. Sun,et al.  Effect of compressive transverse normal stress on mode II fracture toughness in polymeric composites , 2007 .

[28]  R. Girard,et al.  Numerical analysis of composite systems by using interphase/interface models , 1997 .

[29]  Jaehong Lee,et al.  On the application of η-factor approach to determine compressive fracture toughness of fiber-reinforced composites under hydrostatic pressure environment , 2003 .

[30]  Giulio Alfano,et al.  An interface element formulation for the simulation of delamination with buckling , 2001 .

[31]  Albert Turon,et al.  Accurate simulation of delamination under mixed-mode loading using a cohesive model with a mode-dependent penalty stiffness , 2018 .

[32]  Raimund Rolfes,et al.  Modeling the inelastic deformation and fracture of polymer composites – Part II: Smeared crack model , 2013 .

[33]  Giulio Alfano,et al.  Combining interface damage and friction in a cohesive‐zone model , 2006 .

[34]  N. Sottos,et al.  Simulation of fiber debonding with friction in a model composite pushout test , 2001 .

[35]  M. Wisnom,et al.  Predicting the effect of through-thickness compressive stress on delamination using interface elements , 2008 .

[36]  Brian Falzon,et al.  Numerical analysis of intralaminar failure mechanisms in composite structures, Part II: Applications , 2011 .

[37]  F. L. Matthews,et al.  The strength of bolted joints in glass fibre/epoxy laminates , 1985 .

[38]  Pedro P. Camanho,et al.  A continuum damage model for composite laminates: Part I - Constitutive model , 2007 .

[39]  V. Tvergaard.  Effect of fibre debonding in a whisker-reinforced metal , 1990 .

[40]  F. P. van der Meer,et al.  The Transverse Crack Tension test revisited: An experimental and numerical study , 2016 .

[41]  P. Davies,et al.  The influence of hydrostatic pressure on the interlaminar fracture toughness of carbon/epoxy composites , 2006 .

[42]  Albert Turon,et al.  Cohesive zone length of orthotropic materials undergoing delamination , 2016 .

[43]  V. Goyal.  Analytical Modeling of the Mechanics of Nucleation and Growth of Cracks , 2002 .

[44]  Michael R Wisnom,et al.  Modelling discrete failures in composites with interface elements , 2010 .

[45]  Brian Falzon,et al.  Numerical analysis of intralaminar failure mechanisms in composite structures, Part I: FE implementation , 2011 .

[46]  Heinz E. Pettermann,et al.  A continuum damage model for fiber reinforced laminates based on ply failure mechanisms , 2006 .

[47]  J.-F. Maire,et al.  A multiscale progressive failure approach for composite laminates based on thermodynamical viscoelastic and damage models , 2007 .

[48]  T. A. Collings,et al.  The strength of bolted joints in multi-directional cfrp laminates , 1977 .

[49]  Pedro P. Camanho,et al.  A continuum damage model for composite laminates: Part II – Computational implementation and validation , 2007 .

[50]  K. Rhee,et al.  Delamination characteristics of multi‐directional carbon fiber/epoxy composites under high pressure , 2001 .