Influence of various types of damage on the fracture strength of ceramic femoral heads

Abstract Ceramic-on-ceramic articulations are a frequently used bearing for total hip replacements. This success mainly is due to their excellent tribological properties. Ceramics can withstand high pressure loads due to its brittleness but only low bending stresses. A ceramic ball head fracture is the result of subcritical crack growth. This kind of fracture in vivo can abet by damage or contamination of the stem cone. The main goal of this work is to provide a risk assessment of different possible damage mechanisms and contaminations that may result in lower fracture strength of a ceramic ball head. To simulate potential causes, different types and dimensions of metal wire, foils, hair, and lubricants were inserted between the ceramic ball head and the metal cone of the stem. The test results clearly show that fracture strength is negatively influenced by most of the inhomogeneities between the cone and the head because they increase the peak stresses acting on a part of the ceramic ball head. The results of this article clearly confirm the demand for an undamaged taper fit “free of contamination” between the ceramic head and the metal cone during implantation.

[1]  F. Martos,et al.  Fracture of the ceramic head in total hip arthroplasty. Report of two cases. , 1991, The Journal of arthroplasty.

[2]  U. Boenick,et al.  Einfluß von Härte und Oberflächenqualität von Metallkonen auf die Bruchlast von keramischen Kugelköpfen bei Hüftendoprothesen. The Effects of Hardness and Surface Quality of Metal Tapers on the Fracture Load of Ceramic Ball Heads in Hip Endoprostheses , 1994 .

[3]  F. Higuchi,et al.  Fracture of an alumina ceramic head in total hip arthroplasty. , 1995, The Journal of arthroplasty.

[4]  A. Kurth,et al.  Fracture of ceramic heads in total hip replacement , 2006, Archives of Orthopaedic and Trauma Surgery.

[5]  E. Lambiris,et al.  Ceramic femoral head fracture with massive metallosis and severe wear of the cone: a case report and review of the literature , 2006, European Journal of Orthopaedic Surgery & Traumatology.

[6]  G. Willmann.  Ceramics for total hip replacement--what a surgeon should know. , 1998, Orthopedics.

[7]  P Griss,et al.  Five years experience with ceramic-metal-composite hip endoprostheses , 2004, Archives of orthopaedic and traumatic surgery.

[8]  G. Heimke.  The safety of ceramic balls on metal stems in hip arthroplasty , 1994 .

[9]  H. G. Richter,et al.  Fractography of Bioceramics , 2002 .

[10]  G. Terrasi,et al.  Failure analysis of in vivo fractured ceramic femoral heads , 2009 .

[11]  F. Roudot-thoraval,et al.  Revision Total Hip Arthroplasty Performed After Fracture of a Ceramic Femoral Head: A Multicenter Survivorship Study , 2003, The Journal of bone and joint surgery. American volume.

[12]  G. Willmann,et al.  Ceramic Femoral Head Retrieval Data , 2000, Clinical orthopaedics and related research.

[13]  A. Schreiber,et al.  Keramikkopfbruch - Eine seltene Komplikation in der Hüftendoprothetik , 2008 .

[14]  P. T. Nielsen,et al.  Fracture of ceramic femoral heads in total hip arthroplasty. , 1993, The Journal of arthroplasty.

[15]  Dürr Hr.  The problem of fractures of ceramic heads. What should be done , 2009 .

[16]  U. Boenick,et al.  Einfluß von Härte und Oberflächenqualität auf die Bruchlast von keramischen Kugelköpfen bei Hüftendoprothesen , 1994 .

[17]  G. Willmann,et al.  Das Prinzip der Konus-Steckverbindung für keramische Kugelköpfe bei Hüftendoprothesen , 1993 .

[18]  Laurent Sedel,et al.  Fractures of Ceramic Bearings: History and Present Status , 2003, Clinical orthopaedics and related research.

[19]  S. Krikler,et al.  Ceramic head failure. , 1995, The Journal of arthroplasty.

[20]  M. Gleitz,et al.  Ceramic Femoral Head Fractures in Total Hip Arthroplasty , 1996, Clinical orthopaedics and related research.