Metal gate work function tuning by Al incorporation in TiN

Titanium nitride (TiN) films have been used as gate electrode on metal-oxide-semiconductor (MOS) devices. TiN effective work function (EWF) values have been often reported as suitable for pMOS. For nMOS devices, a gate electrode with sufficient low EWF value with a similar robustness as TiN is a challenge. Thus, in this work, aluminum (Al) is incorporated into the TiN layer to reduce the EWF values, which allows the use of this electrode in nMOS devices. Titanium aluminum (TiAl), Al, and aluminum nitride (AlN) layers were introduced between the high-k (HfO2) dielectric and TiN electrode as Al diffusion sources. Pt/TiN (with Al diffusion) and Pt/TiN/TiAl/TiN structures were obtained and TiN EWF values were reduced of 0.37 eV and 1.09 eV, respectively. The study of TiN/AlN/HfO2/SiO2/Si/Al structures demonstrated that AlN layer can be used as an alternative film for TiN EWF tuning. A decrease of 0.26 eV and 0.45 eV on TiN EWF values were extracted from AlN/TiN stack and AlN/TiN laminate stack, respectively. AlN/TiN laminate structures have been shown to be more effective to reduce the TiN work function than just increasing the AlN thickness.

[1]  S. Stemmer,et al.  Influence of AlN layers on the interface stability of HfO2 gate dielectric stacks , 2006 .

[2]  B. Lee,et al.  Metal gate work function engineering using AlNx interfacial layers , 2006 .

[3]  E. Suzuki,et al.  Nitrogen Gas Flow Ratio and Rapid Thermal Annealing Temperature Dependences of Sputtered Titanium Nitride Gate Work Function and Their Effect on Device Characteristics , 2008 .

[4]  M. Stoker,et al.  Oxidation of the Pt∕HfO2 interface: The role of the oxygen chemical potential , 2007 .

[5]  G. Dewey,et al.  Application of high-κ gate dielectrics and metal gate electrodes to enable silicon and non-silicon logic nanotechnology , 2005 .

[6]  S. De Gendt,et al.  Estimation of fixed charge densities in hafnium-silicate gate dielectrics , 2006, IEEE Transactions on Electron Devices.

[7]  J. Kavalieros,et al.  Advanced CMOS transistors in the nanotechnology era for high-performance, low-power logic applications , 2004, Proceedings. 7th International Conference on Solid-State and Integrated Circuits Technology, 2004..

[8]  C. Detavernier,et al.  Annealing effect on the metal gate effective work function modulation for the Al/TiN/SiO2/p-Si structure , 2011 .

[9]  Yong Ju Lee,et al.  Controlling the composition of Ti1−xAlxN thin films by modifying the number of TiN and AlN subcycles in atomic layer deposition , 2003 .

[10]  K. Endo,et al.  Suppressing Vt and Gm variability of FinFETs using amorphous metal gates for 14 nm and beyond , 2012, 2012 International Electron Devices Meeting.

[11]  G. Huang,et al.  Triangular-channel Ge NFETs on Si with (111) sidewall-enhanced Ion and nearly defect-free channels , 2012, 2012 International Electron Devices Meeting.

[12]  D. Mangelinck,et al.  Three-dimensional distribution of Al in high-k metal gate: Impact on transistor voltage threshold , 2012 .

[13]  J.R. Hauser,et al.  Estimating oxide thickness of tunnel oxides down to 1.4 nm using conventional capacitance-voltage measurements on MOS capacitors , 1999, IEEE Electron Device Letters.

[14]  Influence of Al/TiN/SiO2 structure on MOS capacitor, Schottky diode, and fin field effect transistors devices , 2013 .

[15]  H. Hwang,et al.  Dual-Metal-Gate Work Function by Controlling Metal Gate Thickness and Composition , 2008 .

[16]  Gate-last TiN/HfO2 band edge effective work functions using low-temperature anneals and selective cladding to control interface composition , 2012 .

[17]  S. Chew,et al.  Effective Work Function Engineering for Aggressively Scaled Planar and Multi-Gate Fin Field-Effect Transistor-Based Devices with High-k Last Replacement Metal Gate Technology , 2013 .

[18]  Chenming Hu,et al.  Dual work function metal gate CMOS technology using metal interdiffusion , 2001, IEEE Electron Device Letters.

[19]  J. A. Diniz,et al.  Titanium nitride as electrode for MOS technology and Schottky diode: Alternative extraction method of titanium nitride work function , 2012 .