Air coupled Lamb waves evaluation of the long-term thermo-oxidative ageing of carbon-epoxy plates

Abstract Thermo-oxidative ageing of carbon-epoxy plates has been done for up to 3500 h at two temperatures. Non-destructive evaluation by means of non-contact ultrasonic methods has been tested to characterize the aged plates. Experimental results obtained using Lamb waves propagation in the plates are presented here. Experimental and theoretical dispersion curves are compared. It is shown that the phase velocity of the A0 and S0 Lamb modes is decreasing when ageing duration increases. Assuming the plate to be homogeneous and orthotropic, we demonstrate that this phenomenon is related to an important decrease of the C55 elastic parameter of the plate.

[1]  L. Ye,et al.  A damage identification technique for CF/EP composite laminates using distributed piezoelectric transducers , 2002 .

[2]  M. Lafarie-Frenot,et al.  Thermal cycling of carbon/epoxy laminates in neutral and oxidative environments , 2005 .

[3]  Ramesh Talreja,et al.  A micromechanics based model for predicting fatigue life of composite laminates , 2000 .

[4]  C. Galiotis,et al.  Micromechanics of reinforcement and damage initiation in carbon fibre/epoxy composites under fatigue loading , 2001 .

[5]  Tribikram Kundu,et al.  Selection of Lamb modes for detecting internal defects in composite laminates , 1997 .

[6]  N. Toyama,et al.  Quantitative damage detection in cross-ply laminates using Lamb wave method , 2003 .

[7]  M. Castaings,et al.  Identification of composite materials elastic moduli from Lamb wave velocities measured with single sided, contactless ultrasonic method , 2001 .

[8]  M D Seale,et al.  Lamb wave characterization of the effects of long-term thermal-mechanical aging on composite stiffness. , 1999, The Journal of the Acoustical Society of America.

[9]  J. Verdu,et al.  Kinetic modelling and simulation of gravimetric curves: application to the oxidation of bismaleimide and epoxy resins , 2002 .

[10]  M. Cinquin,et al.  Monitoring of the moisture content in carbon-epoxy plates using Lamb waves , 2005 .

[11]  Lobkis,et al.  In-plane elastic property characterization in composite plates , 2000, The Journal of the Acoustical Society of America.

[12]  Christian Hochard,et al.  Damage modelling of laminated carbon/epoxy composites under static and fatigue loadings , 2002 .

[13]  Michel Castaings,et al.  FE modeling of Lamb mode diffraction by defects in anisotropic viscoelastic plates , 2006 .

[14]  T. S. Barry,et al.  Lamb Wave Assessment of Fatigue and Thermal Damage in Composites , 1998 .

[15]  B. S. Wong,et al.  Experimental evaluation of delaminations in composite plates by the use of Lamb waves , 1995 .