Modelling the simulation of impact induced damage onset and evolution in composites

Abstract This paper presents two modelling strategies for the simulation of low velocity impact induced damage onset and evolution in composite plates. Both the strategies use a global–local technique to refine the mesh in the impact zone in order to increase the accuracy in predicting the impact phenomena without affecting the computational cost. Cohesive elements are used to simulate the inter-lamina damage behaviour (delaminations) and Hashin’s failure criteria are adopted to predict the intra-lamina failure mechanisms. The two modelling strategies differ in terms of input parameters for the inter-lamina and intra-lamina damage evolution laws and in terms of modelling solutions in the impacted area. Comparisons between numerical and experimental results on composite plates subjected to different impact energies, according to the ASTM D7136 requirements, have been used to assess the peculiarities and the fields of application for the two proposed modelling strategies. Both the strategies have been tested by adopting the finite element code ABAQUS®. The different approaches to set the parameters of cohesive elements’ constitutive laws and Hashin’s criteria and the different choices made in quantifying the dependence of failure criteria on the finite elements’ average size have been taken into account.

[1]  Francesco Caputo,et al.  Application of the Mesh Superposition Technique to the Study of Delaminations in Composites Thin Plates , 2012 .

[2]  Egidio Rizzi,et al.  On the formulation of anisotropic elastic degradation. I. Theory based on a pseudo-logarithmic damage tensor rate , 2001 .

[3]  K. Volokh.  Comparison between cohesive zone models , 2004 .

[4]  Romesh C. Batra,et al.  Response of fiber reinforced composites to underwater explosive loads , 2007 .

[5]  Francesco Caputo,et al.  Kinematic Approach for a Global-Local Coupling: Compressive Behaviour of a Delaminated Panel: , 2011 .

[6]  Pierre Ladevèze,et al.  A damage computational method for composite structures , 1992 .

[7]  Aniello Riccio,et al.  A Global/Local Finite Element Approach for Predicting Interlaminar and Intralaminar Damage Evolution in Composite Stiffened Panels Under Compressive Load , 2011 .

[8]  Aniello Riccio,et al.  Finite Element Analysis of the Stability (Buckling and Post-Buckling) of Composite Laminated Structures: Well Established Procedures and Challenges , 2012, Applied Composite Materials.

[9]  Francesco Caputo,et al.  Intra-laminar Damage Evolution in a Composite Grid Structure Representative Volume Element under Compression Load , 2013 .

[10]  E. Antonucci,et al.  A Global–Local Numerical Model for the Prediction of Impact Induced Damage in Composite Laminates , 2014, Applied Composite Materials.

[11]  Aniello Riccio,et al.  Delamination buckling and growth phenomena in stiffened composite panels under compression. Part I: An experimental study , 2014 .

[12]  Aniello Riccio,et al.  Skin Stringer Debonding Evolution in Stiffened Composite Panels under Compressive Load: A Novel Numerical Approach , 2013 .

[13]  Aniello Riccio,et al.  On the robustness of finite element procedures based on Virtual Crack Closure Technique and fail release approach for delamination growth phenomena. Definition and assessment of a novel methodology , 2010 .

[14]  Francesco Caputo,et al.  Global-Local FE Simulation of a Plate LVI Test , 2013 .

[15]  P. Perugini,et al.  Numerical–experimental investigation on post-buckled stiffened composite panels , 2002 .

[16]  Ramesh Talreja,et al.  A continuum mechanics characterization of damage in composite materials , 1985, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[17]  Serge Abrate,et al.  Impact on Composite Structures , 1998 .

[18]  Dan Zenkert,et al.  Testing and analysis of ultra thick composites , 2010 .

[19]  Romesh C. Batra,et al.  Blast resistance of unidirectional fiber reinforced composites , 2008 .

[20]  Z. Hashin.  Failure Criteria for Unidirectional Fiber Composites , 1980 .

[21]  Aniello Riccio,et al.  A Study on Skin Delaminations Growth in Stiffened Composite Panels by a Novel Numerical Approach , 2013, Applied Composite Materials.

[22]  A. Riccio,et al.  Impact Damage Management of Composite Laminated Structures by a Probabilistic Approach , 2013 .

[23]  Francesco Caputo,et al.  Numerical Procedures for Damage Mechanisms Analysis in CFRP Composites , 2013 .

[24]  Z. Hashin,et al.  A Fatigue Failure Criterion for Fiber Reinforced Materials , 1973 .

[25]  Aniello Riccio,et al.  Effects of Geometrical and Material Features on Damage Onset and Propagation in Single-lap Bolted Composite Joints under Tensile Load: Part I – Experimental Studies , 2005 .

[26]  Dusan Krajcinovic,et al.  The Continuous Damage Theory of Brittle Materials, Part 1: General Theory , 1981 .

[27]  Aniello Riccio,et al.  Formulation and assessment of an enhanced finite element procedure for the analysis of delamination growth phenomena in composite structures , 2011 .

[28]  R. Citarella,et al.  Three-Dimensional BEM and FEM Submodelling in a Cracked FML Full Scale Aeronautic Panel , 2014, Applied Composite Materials.

[29]  Pierluigi Perugini,et al.  Influence of contact phenomena on embedded delaminations growth in composites , 2003 .

[30]  Francesco Caputo,et al.  Evaluation of energy release rate for delamination defects at the skin/stringer interface of a stiffened composite panel , 2004 .

[31]  U. Mercurio,et al.  Numerical Simulations of Inter-laminar Damage Evolution in a Composite Wing Box , 2014, Applied Composite Materials.

[32]  P. Camanho,et al.  Mixed-Mode Decohesion Finite Elements for the Simulation of Delamination in Composite Materials , 2002 .

[33]  Francesco Caputo,et al.  Damage Propagation in Composite Structures using an Embedded Global-Local Approach , 2013 .