Fractographic observations on delamination growth and the subsequent migration through the laminate

This paper describes fractographic observations from the detailed examination of delamination fracture surfaces and offers an interpretation of the key growth mechanisms. Firstly, the relationship between toughness, delamination failure criteria and fracture morphology is presented and the influence of cusp formation and deformation on toughness is discussed. Observations regarding delaminations migrating through the lamina at multidirectional ply interfaces are then discussed. It is demonstrated how this migration process can be avoided in fracture toughness coupons and consequently the toughness of multidirectional ply interfaces can be characterised. The influence of migration on delamination growth from embedded defects in laminates under compression is presented, and these results are extended to demonstrate how migration influences damage growth in structures. The paper concludes by making recommendations for realistic modelling of migration, and suggests how it can be exploited in damage tolerant structural design.

[1]  E. Greenhalgh,et al.  Developing a Mode II Fracture Model for Composite Laminates , 2008 .

[2]  D. Purslow.  Matrix fractography of fibre-reinforced epoxy composites , 1986 .

[3]  S. Singh,et al.  Delamination resistance, failure criteria and fracture morphology of 0°/0°, 0°/5° and 0°/90° ply interfaces , 1999 .

[4]  W L Bradley,et al.  Matrix Deformation and Fracture in Graphite-Reinforced Epoxies , 1985 .

[5]  Norman A. Fleck,et al.  Compression Failure Mechanisms in Unidirectional Composites , 1992 .

[6]  T. Johannesson,et al.  The detailed structure of delamination fracture surfaces in graphite/epoxy laminates , 1984 .

[7]  E. Greenhalgh.  Characterisation of mixed-mode delamination growth in carbon-fibre composites , 1998 .

[8]  J. Reeder,et al.  An Evaluation of Mixed-Mode Delamination Failure Criteria , 1992 .

[9]  Lorenzo Iannucci,et al.  Formulation and implementation of decohesion elements in an explicit finite element code , 2006 .

[10]  Emile S. Greenhalgh,et al.  The effect of defects on the performance of post-buckled CFRP stringer-stiffened panels , 2003 .

[11]  N. Fleck.  Brittle fracture due to an array of microcracks , 1991, Proceedings of the Royal Society of London. Series A: Mathematical and Physical Sciences.

[12]  J. G. Williams,et al.  The mixed-mode delamination of fibre composite materials , 1993 .

[13]  J. G. Williams,et al.  On the analysis of mixed-mode failure , 1992, International Journal of Fracture.

[14]  Emile S. Greenhalgh,et al.  Failure Analysis and Fractography of Polymer Composites , 2009 .

[15]  P. Robinson,et al.  A Modified DCB Specimen for Mode I Testing of Multidirectional Laminates , 1992 .

[16]  J. Andersons,et al.  Dependence of fracture toughness of composite laminates on interface ply orientations and delamination growth direction , 2004 .