Nucleation of misfit and threading dislocations during epitaxial growth of GaSb on GaAs(001) substrates

The initial stages of molecular beam epitaxy of GaSb on highly mismatched GaAs(001) substrates were investigated. Transmission electron microscopy was used to analyze the defect structure in GaSb islands and at their interfaces with GaAs(001) at different stages of growth. Based on experimental observations, we propose that the semiperiodic net of 90° misfit dislocations at the GaSb/GaAs(001) interface nucleate homogeneously at the leading edges of advancing {111} planes. After nucleation, they glide inwards along the interface plane to reach their equilibrium position. Threading dislocations in GaSb layers were directly correlated with the misfit dislocation net. We demonstrate that there are no threading defects in GaSb islands when their interfaces consist solely of 90° misfit dislocations, and that threading dislocations in the GaSb epilayer are all associated with minority 60° misfit dislocations nucleated in growing islands. The number of threading dislocations per unit area of the GaSb film is found to be independent of GaSb coverage, indicating that island coalescence does not substantially increase the number of 60° dislocations.

[1]  J. W. Matthews,et al.  Defects in epitaxial multilayers: II. Dislocation pile-ups, threading dislocations, slip lines and cracks , 1975 .

[2]  Jens Lothe John Price Hirth,et al.  Theory of Dislocations , 1968 .

[3]  L. Lassabatère,et al.  Accommodation of lattice mismatch and threading of dislocations in GaSb films grown at different temperatures on GaAs (001) , 1994 .

[4]  J. W. Matthews,et al.  Defects in epitaxial multilayers , 1974 .

[5]  J. W. Matthews,et al.  Defects in epitaxial multilayers: III. Preparation of almost perfect multilayers , 1976 .

[6]  J. W. Matthews.  Defects associated with the accommodation of misfit between crystals , 1975 .

[7]  N. El-Masry,et al.  Interactions of dislocations in GaAs grown on Si substrates with InGaAs-GaAsP strained layered superlattices , 1988 .

[8]  L. Lassabatère,et al.  GASB/GAAS HETEROEPITAXY CHARACTERIZED AS A STRESS-FREE SYSTEM , 1991 .

[9]  P. Fuoss,et al.  X-Ray Diffraction From Buried GaAs/GaSb Interfaces , 1990 .

[10]  Hadis Morkoç,et al.  Gallium arsenide and other compound semiconductors on silicon , 1990 .

[11]  A. Howie,et al.  Electron Microscopy of Thin Crystals , 1977, Nature.

[12]  C. Barry Carter,et al.  60° dislocations in (001) GaAs/Si interfaces , 1990 .

[13]  D. W. Pashley,et al.  Moiré patterns on electron micrographs, and their application to the study of dislocations in metals , 1958, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[14]  J. Werner,et al.  Polycrystalline Semiconductors II , 1991 .

[15]  Joongoo Kang,et al.  Lomer Dislocations in (0 0 1) GaSb/GaAs Heterostructure. , 1991 .

[16]  N. Thompson.  Dislocation Nodes in Face-Centred Cubic Lattices , 1953 .