Texturization of multicrystalline silicon wafers for solar cells by chemical treatment using metallic catalyst

Abstract A new etching method for texturing multicrystalline p-type Si wafers for solar cells was developed. In this method, we used platinum or silver particles as the catalysts, which were loaded on the wafers by means of the electroless-plating technique. After deposition of the catalysts, the wafers were etched and textured in HF solution, to which in some cases chemical oxidants were added. The solar cells (4 cm 2 ) manufactured from the textured wafers showed efficiency as high as 16.6%, which was about 1% (absolute) higher than that of the cells made from the wafers treated by the conventional alkaline method.

[1]  Heinrich Kurz,et al.  Texturisation of multicrystalline silicon wafers for solar cells by reactive ion etching through colloidal masks , 2003 .

[2]  J. Szlufcik,et al.  Isotropic texturing of multicrystalline silicon wafers with acidic texturing solutions [solar cell manufacture] , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[3]  A. Rohatgi,et al.  Rie-texturing of multicrystalline silicon solar cells , 2002 .

[4]  István Bársony,et al.  Efficiency improvement by porous silicon coating of multicrystalline solar cells , 1997 .

[5]  Shinji Yae,et al.  Formation of porous silicon by metal particle enhanced chemical etching in HF solution and its application for efficient solar cells , 2003 .

[6]  Xiuling Li,et al.  Metal-assisted chemical etching in HF/H2O2 produces porous silicon , 2000 .

[7]  T. Machida,et al.  Polycrystalline silicon solar cells with V-grooved surface , 1994 .

[8]  H. Fukidome,et al.  A Very Simple Method of Flattening Si(111) Surface at an Atomic Level Using Oxygen-Free Water , 1999 .

[9]  R. Einhaus,et al.  Improved anisotropic etching process for industrial texturing of silicon solar cells , 1999 .

[10]  T. Ishihara,et al.  Investigation of Acidic Texturization for Multicrystalline Silicon Solar Cells , 1999 .

[11]  Y. Inomata,et al.  Surface texturing of large area multicrystalline silicon solar cells using reactive ion etching method , 1997 .

[12]  Piotr Panek,et al.  Double porous silicon layer on multi-crystalline Si for photovoltaic application , 2002 .

[13]  H. Fukidome,et al.  Effect of dissolved oxygen on etching process of Si(111)in 2.5% NH3 solution , 2000 .

[14]  E. V. D. Drift,et al.  Electroless Silver Deposition in 100 nm Silicon Structures , 2001 .