Impact damage characterisation of carbon fibre/epoxy composites with multi-layer reinforcement

Low-velocity impact tests were performed to investigate the impact behaviour of carbon fibre/epoxy composite laminates reinforced by short fibres and other interleaving materials. Characterisation techniques, such as cross-sectional fractography and scanning acoustic microscopy, were employed quantitatively to assess the internal damage of some composite laminates at the sub-surface under impact. Scanning electron microscopy was used to observe impact fractures and damage modes at the fracture surfaces of the laminate specimens. The results show that composite laminates experience various types of fracture; delamination, intra-ply cracking, matrix cracking, fibre breakage and damage depending on the interlayer materials. The trade-off between impact resistance and residual strength is minimised for composites reinforced by Zylon fibres, while that for composites interleaved by poly(ethylene-co-acrylic acid) (PEEA) film is substantial because of deteriorating residual strength, even though the damaged area is significantly reduced. Damages produced on the front and back surfaces of impact were also observed and compared for some laminates.

[1]  X. Hu,et al.  Impact and high strain rate delamination characteristics of carbon fibre epoxy composites , 1996 .

[2]  Xiaozhi Hu,et al.  Comparative Study of Dynamic and Static Delamination Behaviour of Carbon Fibre-Epoxy Composite Laminates , 1995 .

[3]  P. Hogg,et al.  High-temperature damage tolerance of carbon fibre-reinforced plastics: Part 1: Impact characteristics , 1994 .

[4]  L. Carlsson,et al.  Plastic zone estimates in mode I interlaminar fracture of interleaved composites , 1992 .

[5]  C. Sun,et al.  Prediction of Delamination in Composite Laminates Subjected to Low Velocity Impact , 1993 .

[6]  J. Masters,et al.  A New Generation of Epoxy Composites for Primary Structural Applications: Materials and Mechanics , 1987 .

[7]  George S. Springer,et al.  Measurements of Matrix Cracking and Delamination Caused by Impact on Composite Plates , 1988 .

[8]  H. Hamada,et al.  Impact response of woven glass-fabric composites - II. Effect of temperature , 1998 .

[9]  Jang-Kyo Kim,et al.  Scanning acoustic microscopy as a tool for quantitative characterisation of damage in CFRPs , 1999 .

[10]  John E. Masters,et al.  Improved Impact and Delamination Resistance through Interleafing , 1991 .

[11]  G. R. Sidey,et al.  Impact properties of carbon fibre/Kevlar 49 fibre hydrid composites , 1978 .

[12]  Low velocity impact behavior of glass/epoxy cross-ply laminates with different fiber treatments , 1999 .

[13]  D. Purslow,et al.  Some fundamental aspects of composites fractography , 1981 .

[14]  Jang-Kyo Kim,et al.  Drop-weight impact damage tolerance of CFRP with rubber-modified epoxy matrix , 1993 .

[15]  W. Bascom,et al.  A microscopy study of impact damage of epoxy-matrix carbon-fibre composites , 1986 .

[16]  O. Ishai,et al.  Effect of selective adhesive interleaving on interlaminar fracture toughness of graphite/epoxy composite laminates , 1988 .

[17]  J. C. Prichard,et al.  The role of impact damage in post-impact compression testing , 1990 .

[18]  E. Altus,et al.  The effect of soft interleaved layers on the combined transverse cracking/delamination mechanisms in composite laminates , 1990 .

[19]  Leslie Banks-Sills,et al.  The effect of adhesive thickness on interlaminar fracture toughness of interleaved cfrp specimens , 1989 .

[20]  Hiroyuki Hamada,et al.  Impact response of woven glass-fabric composites - I. Effect of fibre surface treatment , 1998 .

[21]  S. Hong,et al.  On the relationship between impact energy and delamination area , 1989 .

[22]  Rhys Jones,et al.  Residual strength of composites with multiple impact damage , 1994 .

[23]  Jang‐Kyo Kim,et al.  Impact Performance of a Woven Fabric CFRP Laminate , 1996, Engineering Plastics.

[24]  P. Hogg,et al.  High-temperature damage tolerance of carbon fibre-reinforced plastics , 1995 .

[25]  A. C. Roulin-moloney.  Fractography and failure mechanisms of polymers and composites , 1989 .

[26]  C. Z. Wang,et al.  Impact resistance and energy absorption mechanisms in hybrid composites , 1989 .

[27]  C. Sun,et al.  Optimal Use of Adhesive Layers in Reducing Impact Damage in Composite Laminates , 1990 .

[28]  John Morton,et al.  The impact resistance of composite materials — a review , 1991 .

[29]  A. Su,et al.  Effect of interleaving on the impact response of a unidirectional carbon/epoxy composite , 1995 .

[30]  S. Abrate.  Impact on Laminated Composite Materials , 1991 .

[31]  J. Jang,et al.  Impact behavior of carbon fiber/ultra-high modulus polyethylene fiber hybrid composites , 1995 .

[32]  J. Hearle,et al.  The tensile fatigue behavior of para‐oriented aramid fibers and their fracture morphology , 1977 .