Fracture toughness master-curve analysis of the tempered martensitic steel Eurofer97

We report fracture toughness data for the reduced activation tempered martensitic steel Eurofer97 in the lower to middle transition region. The fracture toughness was measured from tests carried out on 0.35T and 0.87T pre-cracked compact tension specimens. The data were first analyzed using the ASTM E1921 standard. The toughness-temperature behavior and scatter were shown to deviate from the ASTM E1921 standard predictions near the lower shelf. Using the method of maximum likelihood, the athermal component of the master-curve was calculated to better fit the data from the lower to the middle transition region. We showed that these master-curve adjustments are necessary to make the T-o values obtained near the lower shelf with 0.35T C(T) specimens consistent with those obtained in the middle transition region with 0.87T C(T) specimens. (C) 2008 Elsevier B.V. All rights reserved.

[1]  Mikio Enoeda,et al.  Reduced activation martensitic steels as a structural material for ITER test blanket , 2004 .

[2]  M. He,et al.  Influence of statistical and constraint loss size effects on cleavage fracture toughness in the transition – A model based analysis , 2006 .

[3]  N. Baluc,et al.  Fracture toughness properties in the transition region of the Eurofer97 tempered martensitic steel , 2007 .

[4]  H. Matsui,et al.  Evaluation of fracture toughness master curve shifts for JMTR irradiated F82H using small specimens , 2007 .

[5]  J. Rensman,et al.  Tensile properties and transition behaviour of RAFM steel plate and welds irradiated up to 10 dpa at 300 °C , 2002 .

[6]  E. Lucon.  A closer look at the fracture toughness of ferritic/martensitic steels , 2007 .

[7]  R. Klueh,et al.  High-Chromium Ferritic and Martensitic Steels for Nuclear Applications , 2001 .

[8]  G. R. Odette,et al.  Cleavage fracture and irradiation embrittlement of fusion reactor alloys: mechanisms, multiscale models, toughness measurements and implications to structural integrity assessment , 2003 .

[9]  Kim Wallin,et al.  The scatter in KIC-results , 1984 .

[10]  K. Wallin,et al.  Irradiation damage effects on the fracture toughness transition curve shape for reactor pressure vessel steels , 1993 .

[11]  Mikhail A. Sokolov,et al.  A master curve analysis of F82H using statistical and constraint loss size adjustments of small specimen data , 2004 .

[12]  G. Odette,et al.  Plastic flow properties and fracture toughness characterization of unirradiated and irradiated tempered martensitic steels , 2007 .

[13]  Narendra J. Sheth,et al.  Statistical Design and Analysis of Engineering Experiments , 1973 .

[14]  Philippe Spätig,et al.  Fracture toughness behavior in the ductile–brittle transition region of the tempered martensitic Eurofer97 steel: Experiments and modeling , 2008 .