The influence of compatibilizers on the structure and mechanical properties of lightweight reinforced thermoplastics

Lightweight reinforced thermoplastics (LWRT) have a low density and high rigidity. The application of LWRTs to automotive interiors, such as headliners and instrument panels, is very promising. The porous structure of LWRTs is formed in the process of deconsolidation, so pores may appear between the matrix and fibers that interrupt the transfer of stress and deteriorate the mechanical properties. In this article, maleic anhydride-grafted polypropylene (PP-g-MAH) and glycidyl methacrylate-grafted polypropylene were selected to study the influence of compatibilizers on the structural and mechanical properties of an LWRT. It was found that the modification effect of PP-g-MAH is more significant. Before the mass fraction of PP-g-MAH reaches 20%, the tensile and flexural properties of the LWRT increased with the PP-g-MAH content. The required content of PP-g-MAH in the LWRT is high compared with the voidless composites. Structures with a good matrix distribution and dispersion are anticipated in LWRTs, which are not considered in voidless composites. POLYM. COMPOS., 2016. © 2016 Society of Plastics Engineers

[1]  Ping Li,et al.  Characterization of short glass fiber reinforced polypropylene foam composites with the effect of compatibilizers: A comparison , 2015 .

[2]  Y. Wan,et al.  Deconsolidation behavior of carbon fiber reinforced thermoplastics , 2014 .

[3]  A. Pegoretti,et al.  Synergistic effect of exfoliated graphite nanoplatelets and short glass fiber on the mechanical and interfacial properties of epoxy composites , 2014 .

[4]  S. Ying,et al.  Preparation of short carbon fiber/polypropylene fine-celled foams in supercritical CO2 , 2013 .

[5]  Byoungho Lee,et al.  Bio-composites of kenaf fibers in polylactide: Role of improved interfacial adhesion in the carding process , 2009 .

[6]  S. T. Jespersen,et al.  Film stacking impregnation model for a novel net shape thermoplastic composite preforming process , 2008 .

[7]  Enamul Haque,et al.  Designing strength, stiffness and acoustics in headliner substrate material , 2006, ATZautotechnology.

[8]  S. Jeelani,et al.  Tensile and fracture behavior of polymer foams , 2006 .

[9]  V. Michaud,et al.  Deconsolidation in glass mat thermoplastic composites: Analysis of the mechanisms , 2005 .

[10]  A. Błędzki,et al.  Effects of the chemical foaming agents, injection parameters, and melt‐flow index on the microstructure and mechanical properties of microcellular injection‐molded wood‐fiber/polypropylene composites , 2005 .

[11]  Ioan I. Negulescu,et al.  Kenaf/Ramie Composite for Automotive Headliner , 2005 .

[12]  H. Karian.  Handbook of Polypropylene and Polypropylene Composites, Revised and Expanded , 2003 .

[13]  J. Vanek,et al.  The influence of surface modifications of glass on glass fiber/polyester interphase properties , 2003 .

[14]  Y. Mai,et al.  Thermal de-consolidation of thermoplastic matrix composites—I. Growth of voids , 2002 .

[15]  G. Dai,et al.  Effect of the microstructure of GMT on its mechanical properties , 2002 .

[16]  F. Cogswell.  Thermoplastic Aromatic Polymer Composites , 1996 .

[17]  J. Thomason,et al.  The influence of fibre length and concentration on the properties of glass fibre reinforced polypropylene: 2. Thermal properties , 1996 .

[18]  J. Schultz,et al.  Relationship between fibre-matrix adhesion and the interfacial shear strength in polymer-based composites , 1993 .

[19]  B. Pukánszky.  Influence of interface interaction on the ultimate tensile properties of polymer composites , 1990 .

[20]  Su-Su Wang,et al.  Fracture of fiber reinforced composites , 1976 .

[21]  B. Harris,et al.  Fracture mechanisms in glass-reinforced plastics , 1975 .

[22]  D. K. Owens,et al.  Estimation of the surface free energy of polymers , 1969 .