Effect of surface mechanical attrition treatment (SMAT) on microhardness, surface roughness and wettability of AISI 316L

Abstract Surface roughness and wettability are among the surface properties which determine the service lifetime of materials. Mechanical treatments subjected to the surface layer of materials are often performed to obtain the desired surface properties and to enhance the mechanical strength of materials. In this paper, the surface microhardness, roughness and wettability of AISI 316L stainless steel resulting from surface mechanical attrition treatment (SMAT) are discussed. The SMAT was conducted with various processing parameters, including the duration of treatment, the number and diameter of milling ball, and the motor speed of the SMAT machine. The result indicates an increasing surface microhardness due to the SMAT. A harder surface is yielded by the SMAT with a longer duration, a bigger and a larger number of milling balls, and a higher vibration frequency. The SMAT also creates craters on the steel surfaces which correspond to the increasing roughness from 0.046 μm to the values in ranging from 0.681 to 0.909 μm. The change on the surface roughness by the SMAT does not only depend on the duration of treatment, but also the other processing parameters. In addition, the wettability of AISI 316L surface slightly increases by the SMAT as seen on the decreasing droplet contact angle from 88.6° to the values ranging from 74.4° to 87.0°. Such a droplet contact angle reduction is related to the increasing surface roughness after the SMAT. In conclusion, this study reveals the possibility of the SMAT to be used for surface properties optimization in addition to the strength enhancement of stainless steel.

[1]  H C van der Mei,et al.  Physico-chemistry of initial microbial adhesive interactions--its mechanisms and methods for study. , 1999, FEMS microbiology reviews.

[2]  Carlos Nelson Elias,et al.  Relationship between surface properties (roughness, wettability and morphology) of titanium and dental implant removal torque. , 2008, Journal of the mechanical behavior of biomedical materials.

[3]  A. Scarano,et al.  Direct bone formation on sand-blasted titanium implants: an experimental study. , 1996, Biomaterials.

[4]  H. C. van der Mei,et al.  Retention of bacteria on a substratum surface with micro-patterned hydrophobicity. , 2000, FEMS microbiology letters.

[5]  Jian Lu,et al.  Tensile properties of a nanocrystalline 316L austenitic stainless steel , 2005 .

[6]  Y. Oshida,et al.  Effects of shot-peening on surface contact angles of biomaterials , 1993 .

[7]  Robert J. Asaro,et al.  Toward a quantitative understanding of mechanical behavior of nanocrystalline metals , 2007 .

[8]  H. W. Zhang,et al.  Development of Nanostructures in Metallic Materials with Low Stacking Fault Energies During Surface Mechanical Attrition Treatment (SMAT) , 2003 .

[9]  Jian Lu,et al.  Surface nanocrystallization of 316L stainless steel induced by ultrasonic shot peening , 2000 .

[10]  V. Azar,et al.  The effect of shot peening on fatigue and corrosion behavior of 316L stainless steel in Ringer's solution , 2010 .

[11]  Leon L. Shaw,et al.  An analytical model of the surface roughness of an aluminum alloy treated with a surface nanocrystallization and hardening process , 2005 .

[12]  Yiming Jiang,et al.  Effect of surface mechanical attrition treatment on corrosion behavior of 316 stainless steel , 2009 .

[13]  Leon L. Shaw,et al.  Finite element modeling of the surface roughness of 5052 Al alloy subjected to a surface severe plastic deformation process , 2004 .

[14]  Gang Liu,et al.  Formation of nanostructured surface layer on AISI 304 stainless steel by means of surface mechanical attrition treatment , 2003 .

[15]  Liang Hao,et al.  The wettability modification of bio-grade stainless steel in contact with simulated physiological liquids by the means of laser irradiation , 2005 .

[16]  S. Nam,et al.  Effect of surface roughness on low-cycle fatigue life of CrMoV steel at 550 °C , 1989 .

[17]  Masaki Nakajima,et al.  Effect of surface roughness on step-wise S–N characteristics in high strength steel , 2003 .

[18]  J. Jiménez,et al.  Influence of the sandblasting on the subsurface microstructure of 316LVM stainless steel: Implications on the magnetic and mechanical properties , 2009 .

[19]  V. Selladurai,et al.  Experimental investigation on corrosion and hardness of ion implanted AISI 316L stainless steel , 2010 .

[20]  G. I. Prokopenko,et al.  Ultrasonic impact peening for the surface properties’ management , 2007 .

[21]  Jörg Müller,et al.  Wettability enhancement by rough surfaces generated by thin film technology , 2003 .

[22]  Y. Yang,et al.  Effect of nanotubular-micro-roughened titanium surface on cell response in vitro and osseointegration in vivo , 2010 .

[23]  Thomas J Webster,et al.  The role of nanometer and sub-micron surface features on vascular and bone cell adhesion on titanium. , 2008, Biomaterials.

[24]  J. Amédée,et al.  Effect of surface roughness of the titanium alloy Ti-6Al-4V on human bone marrow cell response and on protein adsorption. , 2001, Biomaterials.

[25]  A. Borruto,et al.  Influence of surface wettability on friction and wear tests , 1998 .

[26]  Minoru Umemoto,et al.  Comparison of Nanocrystalline Surface Layer in Steels Formed by Air Blast and Ultrasonic Shot Peening , 2004 .

[27]  Jian Lu,et al.  Nanostructured surface layer on metallic materials induced by surface mechanical attrition treatment , 2004 .

[28]  Delphine Retraint,et al.  ENHANCED MECHANICAL BEHAVIOR OF A NANOCRYSTALLISED STAINLESS STEEL AND ITS THERMAL STABILITY , 2007 .

[29]  F Rupp,et al.  Roughness induced dynamic changes of wettability of acid etched titanium implant modifications. , 2004, Biomaterials.

[30]  Conrado Aparicio,et al.  Corrosion behaviour of commercially pure titanium shot blasted with different materials and sizes of shot particles for dental implant applications. , 2003, Biomaterials.

[31]  Jian Lu,et al.  An experimental study of residual stress induced by ultrasonic shot peening , 2004 .

[32]  Cameron J Wilson,et al.  Mediation of biomaterial-cell interactions by adsorbed proteins: a review. , 2005, Tissue engineering.

[33]  Jian Lu,et al.  Fatigue life improvement through surface nanostructuring of stainless steel by means of surface mechanical attrition treatment , 2006 .