Microstructural Characterization of Concrete Prepared with Recycled Aggregates

Abstract Several authors have reported the workability, mechanical properties, and durability of concrete produced with construction waste replacing the natural aggregate. However, a systematic microstructural characterization of recycled aggregate concrete has not been reported. This work studies the use of fine recycled aggregate to replace fine natural aggregate in the production of concrete and reports the resulting microstructures. The used raw materials were natural aggregate, recycled aggregate obtained from a standard concrete, and Portland cement. The substitution extent was 0, 10, 50, and 100 vol%; hydration was stopped at 9, 24, and 96 h and 28 days. Microscopy was focused on the cement/aggregate interfacial transition zone, enlightening the effect of incorporating recycled aggregate on the formation and morphology of the different concrete hydration products. The results show that concretes with recycled aggregates exhibit typical microstructural features of the transition zone in normal strength concrete. Although overall porosity increases with increasing replacement, the interfacial bond is apparently stronger when recycled aggregates are used. An addition of 10 vol% results in a decrease in porosity at the interface with a corresponding increase of the material hardness. This provides an opportunity for development of increased strength Portland cement concretes using controlled amounts of concrete waste.

[1]  J. Brito,et al.  The effect of superplasticisers on the workability and compressive strength of concrete made with fine recycled concrete aggregates , 2012 .

[2]  Jorge de Brito,et al.  Structural concrete with incorporation of coarse recycled concrete and ceramic aggregates: durability performance , 2009 .

[3]  R. Detwiler,et al.  Preparation of flat-polished specimens for SEM-backscattered electron imaging and X-ray microanalysis--importance of epoxy impregnation , 2003 .

[4]  S. Diamond.  The microstructure of cement paste and concrete - a visual primer , 2004 .

[5]  S. Mindess,et al.  Microhardness testing of cementitious materials , 1996 .

[6]  Katrin Rübner,et al.  Characterization of Mineral Building Materials by Mercury‐Intrusion Porosimetry , 2006 .

[7]  A. Hussin,et al.  Petrography evidence of the interfacial transition zone (ITZ) in the normal strength concrete containing granitic and limestone aggregates , 2011 .

[8]  K. Scrivener,et al.  The Interfacial Transition Zone (ITZ) Between Cement Paste and Aggregate in Concrete , 2004 .

[9]  P. Lura,et al.  Modelling of Transport Phenomena at Cement Matrix—Aggregate Interfaces , 2004 .

[10]  J. Brito,et al.  Mechanical behaviour of concrete made with fine recycled concrete aggregates , 2007 .

[11]  Karen L. Scrivener,et al.  Backscattered electron imaging of cementitious microstructures: Understanding and quantification , 2004 .

[12]  S. Diamond.  Considerations in image analysis as applied to investigations of the ITZ in concrete , 2001 .

[13]  Qiang Du,et al.  Concrete with recycled concrete aggregate and crushed clay bricks , 2011 .

[14]  Chi Sun Poon,et al.  Effect of microstructure of ITZ on compressive strength of concrete prepared with recycled aggregates , 2004 .

[15]  P. Cachim.  Mechanical properties of brick aggregate concrete , 2009 .

[16]  Bishwajit Bhattacharjee,et al.  Porosity, pore size distribution and in situ strength of concrete , 2003 .

[17]  A. J. Valdés,et al.  Re-use of construction and demolition residues and industrial wastes for the elaboration or recycled eco-efficient concretes , 2010 .

[18]  C. Medina,et al.  Microstructure and properties of recycled concretes using ceramic sanitary ware industry waste as coarse aggregate , 2012 .

[19]  S. Kenai,et al.  The use of coarse and fine crushed bricks as aggregate in concrete , 2008 .