Naturally occurring limestone and dolomite samples, originating from different geographical locations, were tested as potential sorbents for carbonation/calcination based CO2 capture from combustion flue gases. Samples have been studied in a thermogravimetric analyzer under simulated flue gas conditions at three calcination temperatures,viz., 750textdegreeC, 875textdegreeC, and 930textdegreeC for four carbonation calcination reaction (CCR) cycles. The dolomite sample exhibited the highest rate of carbonation than the tested limestones.At the third cycle, its CO2 capture capacity per kilogram of the sample was nearly equal to that of Gotland, the highest reacting limestone tested. At the fourth cycle it surpassed Gotland, despite the fact that the CaCO3 content of the Sibbo dolomite was only 2/3 of that of the Gotland. Decay coefficients were calculated by a curve fitting exercise and its value is lowest for the Sibbo dolomite. That means, most probably its capture capacity per kilogram of the sample would remain higher, well beyond the fourth cycle. There was a strong correlation between the calcination temperature, the specific surface area of the calcined samples, and the degree of carbonation. It was observed that the higher the calcination temperature, the lower the sorbent reactivity. The Brunauer?Emmett?Teller measurements and scanning electron microscope images provided quantitative and qualitative evidences to prove this. For a given limestone/dolomite sample, sorbent?s CO2 capture capacity depended on the number of CCR cycles and the calcination temperature.In a CCR loop, if the sorbent is utilized only for a certain small number of cycles 20, the CO2 capture capacity could be increased by lowering the calcination temperature.According to the equilibrium thermodynamics, the CO2 partial pressure in the calciner should be lowered to lower the calcination temperature. This can be achieved by additional steam supply into the calciner. Steam could then be condensed in an external condenser to single out the CO2 stream from the exit gas mixture of the calciner. A calciner design based on this concept is illustrated.
[1]
D. P. Harrison,et al.
HIGH TEMPERATURE CAPTURE OF CARBON DIOXIDE: CHARACTERISTICS OF THE REVERSIBLE REACTION BETWEEN CaO(s) and CO2(g)
,
1995
.
[2]
T. Shimizu,et al.
A twin fluid-bed reactor for removal of CO2 from combustion processes
,
1999
.
[3]
H. Herzog.
Peer Reviewed: What Future for Carbon Capture and Sequestration?
,
2001
.
[4]
L. Fan,et al.
Carbonation−Calcination Cycle Using High Reactivity Calcium Oxide for Carbon Dioxide Separation from Flue Gas
,
2002
.
[5]
J. C. Abanades.
The maximum capture efficiency of CO2 using a carbonation/calcination cycle of CaO/CaCO3
,
2002
.
[6]
J. C. Abanades,et al.
Conversion Limits in the Reaction of CO2 with Lime
,
2003
.
[7]
E. J. Anthony,et al.
Capture of CO2 from combustion gases in a fluidized bed of CaO
,
2004
.
[8]
E. Rubin,et al.
Sorbent Cost and Performance in CO2 Capture Systems
,
2004
.
[9]
E. J. Anthony,et al.
Fluidized bed combustion systems integrating CO2 capture with CaO.
,
2005,
Environmental science & technology.
[10]
J. Carlos Abanades,et al.
Pore-Size and Shape Effects on the Recarbonation Performance of Calcium Oxide Submitted to Repeated Calcination/Recarbonation Cycles
,
2005
.
[11]
J. Carlos Abanades,et al.
Determination of the Critical Product Layer Thickness in the Reaction of CaO with CO2
,
2005
.
[12]
Edward J. Anthony,et al.
On the Decay Behavior of the CO2 Absorption Capacity of CaO-Based Sorbents
,
2005
.
[13]
J. Carlos Abanades,et al.
CO2 Capture Capacity of CaO in Long Series of Carbonation/Calcination Cycles
,
2006
.