UV Nd:YAG laser ablation of copper: Chemical states in both crater and halo studied by XPS

Abstract Laser ablation of pure copper was performed using a pulsed Nd:YAG laser operating at 355 nm in air. Oxide nanoparticles redeposited near the edge of the crater results in the formation of the halo. Chemical states in both crater and halo were measured by X-ray photoelectron spectroscopy (XPS). After UV laser ablation, there are an obvious shoulder around 934.4 eV and a shake up satellite around 942.5 eV for the Cu 2p3/2 spectra in both crater and halo. Deconvoluting the Cu 2p3/2 spectra, a component was detected at 933.7 eV corresponding to CuO in both crater and halo as expected. Also, another component at 935.1 eV can be assigned to Cu(OH)2. The formation of CuO and Cu(OH)2 is probably due to the reactions of copper with O2 and water vapor in air. This suggest that the ablation atmosphere plays an important role for the formation of chemical species in both crater and halo. Moreover, an enhanced oxidation in the halo was found at higher fluence: the FWHM of the Cu 2p3/2 spectra and the peak areas of CuO and Cu(OH)2 were significantly higher than those in the crater. This is probably due to the formation of the laser-induced plasma. In addition, peak areas of CuO and Cu(OH)2 in the halo markedly increase with increasing the laser fluence.

[1]  D. P. Norton,et al.  Synthesis of Novel Thin-Film Materials by Pulsed Laser Deposition , 1996, Science.

[2]  Yunrong Wei,et al.  Ablation of cobalt with pulsed UV laser radiation , 2001 .

[3]  T. L. Thiem,et al.  Interaction of an Excimer-Laser Beam with Metals. Part III: The Effect of a Controlled Atmosphere in Laser-Ablated Plasma Emission , 1992 .

[4]  Plummer,et al.  Can pulsed laser excitation of surfaces be described by a thermal model? , 1988, Physical review letters.

[5]  P. Burck,et al.  Laser machining of Si3N4 ceramics , 1995 .

[6]  W. W. Duley,et al.  UV Lasers: Effects and Applications in Materials Science , 1996 .

[7]  Joshua E. Rothenberg,et al.  Laser sputtering: Part III. The mechanism of the sputtering of metals low energy densities , 1985 .

[8]  J. Gottmann,et al.  Material removal and chemical and structural changes induced by irradiation of polymer surfaces with KrF-excimer laser radiation , 1999 .

[9]  T. M. Yue,et al.  XPS investigation of Upilex-S polyimide ablated by 355 nm Nd:YAG laser irradiation , 2001 .

[10]  R. Russo,et al.  Temperature and Emission Spatial Profiles of Laser-Induced Plasmas during Ablation Using Time-Integrated Emission Spectroscopy , 1995 .

[11]  Yong‐Ill Lee,et al.  Influence of Atmosphere and Irradiation Wavelength on Copper Plasma Emission Induced by Excimer and Q-Switched Nd:YAG Laser Ablation , 1997 .

[12]  Brent C. Stuart,et al.  Ultrashort-pulse laser machining of dielectric materials , 1999 .

[13]  Charles M. Lieber,et al.  A laser ablation method for the synthesis of crystalline semiconductor nanowires , 1998, Science.

[14]  M. Stuke,et al.  Sub-picosecond UV-laser ablation of Ni films , 1994 .

[15]  Changsheng Xie,et al.  XPS investigation of the chemical characteristics of Kapton films ablated by a pulsed TEA CO2 laser , 2002 .

[16]  K. C. Yung,et al.  Laser ablation of Upilex-S polyimide: influence of laser wavelength on chemical structure and composition in both ablated area and halo , 2001 .

[17]  R. Kötz,et al.  X-ray photoelectron spectroscopy imaging of laser ablated poly(ether imide) , 1999 .

[18]  Anirban Mitra,et al.  Diagnostics of laser ablated plasmas using fast photography , 1999 .