Self-healing performance of GGBFS based cementitious mortar with granulated activators exposed to a seawater environment

Abstract Concrete structures exposed to marine environments are susceptible to attack by harmful ions such as chloride, sulfate, etc. Ground granulated blast furnace slag (GGBFS) blended cementitious materials are used as a binder in coastal concrete structures. Cracks are generated at young ages due to shrinkage or other factors, which allow the ingress of harmful ions. Therefore, repair and maintenance of such structures is necessary to increase the service lives of these structures. Autogenous self-healing of the cement composites has proved to be an effective alternative method. It occurs when water comes in contact with the unhydrated cement particles and forms additional hydration products. In this study, cement mortar was prepared by replacing cement with GGBFS up to 50%. Granules of activators Ca(OH)2 and Na2SO4 were made and incorporated at different dosages. Physical and self-healing performance of the mortar specimens were evaluated via compressive strength, relative dynamic modulus of elasticity, ultrasonic pulse velocity and water permeability tests. The healing products were examined via electron microscopy, energy dispersive X-ray spectrometry, and microhardness tests. The results indicated that the specimens incorporating granulated Na2SO4 showed minimal self-healing performance while the self-healing efficiency of the specimens with Ca(OH)2 granules was significantly enhanced.

[1]  C. Shi,et al.  New cements for the 21st century: The pursuit of an alternative to Portland cement , 2011 .

[2]  Carola Edvardsen,et al.  Water Permeability and Autogenous Healing of Cracks in Concrete , 1999 .

[3]  Didier Snoeck,et al.  From straw in bricks to modern use of microfibers in cementitious composites for improved autogenous healing – A review , 2015 .

[4]  M. Zain,et al.  Effects of mineral and chemical admixtures on high-strength concrete in seawater , 2002 .

[5]  Weiping Ma,et al.  Hydrothermal reactions of fly ash with Ca(OH)2 and CaSO4·2H2O , 1997 .

[6]  Erick Ringot,et al.  Mineral admixtures in mortars Effect of inert materials on short-term hydration , 2003 .

[7]  Nele De Belie,et al.  Chloride penetration in cracked mortar and the influence of autogenous crack healing , 2016 .

[8]  Hans Beushausen,et al.  Chloride-induced corrosion of steel in cracked concrete – Part I: Experimental studies under accelerated and natural marine environments , 2016 .

[9]  Yong-Soo Lee,et al.  Self healing behavior for crack closing of expansive agent via granulation/film coating method , 2014 .

[10]  Keun-Hyeok Yang,et al.  Hydration products and strength development of calcium hydroxide-based alkali-activated slag mortars , 2012 .

[11]  Paul E. Stutzman,et al.  Petrographic Methods of Examining Hardened Concrete: A Petrographic Manual. Revised 2004 , 1997 .

[12]  Frank Winnefeld,et al.  Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast-furnace slags , 2011 .

[13]  C. Shi,et al.  Comparison of different methods for enhancing reactivity of pozzolans , 2001 .

[14]  Björn Johannesson,et al.  A review : Self-healing in cementitious materials and engineered cementitious composite as a self-healing material , 2012 .

[15]  Yong-Soo Lee,et al.  Crack Healing Performance of PVA-Coated Granules Made of Cement, CSA, and Na2CO3 in the Cement Matrix , 2016, Materials.

[16]  H. Jonkers,et al.  Autogenous healing of marine exposed concrete: Characterization and quantification through visual crack closure , 2015 .

[17]  C. Shi,et al.  Alkali-Activated Cements and Concretes , 2003 .

[18]  Deepak Ravikumar,et al.  Effects of activator characteristics on the reaction product formation in slag binders activated using alkali silicate powder and NaOH , 2012 .

[19]  Hong-gi Kim,et al.  Influence of the surface roughness of crushed natural aggregates on the microhardness of the interfacial transition zone of concrete with mineral admixtures and polymer latex , 2018 .

[20]  Raktipong Sahamitmongkol,et al.  Self-crack closing ability of mortar with different additives , 2011 .

[21]  Stefan Jacobsen,et al.  Self healing of high strength concrete after deterioration by freeze/thaw , 1996 .

[22]  Caijun Shi,et al.  Some factors affecting early hydration of alkali-slag cements , 1996 .

[23]  V. Papadakis,et al.  Supplementary cementing materials in concrete: Part I: efficiency and design , 2002 .

[24]  J. Oh,et al.  Influence of four additional activators on hydrated-lime [Ca(OH)2] activated ground granulated blast-furnace slag , 2016 .