An efficient approach for superconducting joint of YBCO coated conductors

Superconducting joints are crucial for second generation high-temperature superconducting (2G HTS) closed-loop coils that work in the persistent current mode (PCM) operation. Here, we report an efficient approach for superconducting joints of YBa2Cu3O7-σ (YBCO) coated conductors (CCs). The YBCO layer is etched to and from some microchannels, which serve as oxygen diffusion paths during oxygenation annealing (OA), to accelerate the recovery of critical current (I c) of the joined two YBCO layers. The I c of the superconducting joint is 118 A at 77 K with an optimized joining temperature and a short OA time (10 h), which is about 82% I c of the joined YBCO CCs. The persistent field decay of the closed-loop coil shows a joint resistance (R j) of less than 2.2 × 10−13 Ω at 77 K. Two YBCO films epitaxially grown along the c-axis diffuse into each other at the interface and form a dense joining, enabling superconducting current path. This superconducting joint technique can promote the achievement of the PCM operation in 2G HTS magnet applications, such as magnetic resonance imaging and nuclear magnetic resonance.

[1]  J. MacManus‐Driscoll,et al.  Improvement of the value and anisotropy of critical current density in GdBa2Cu3O7-δ coated conductors with self-assembled 3-dimensional BaZrO3 nanostructure , 2021 .

[2]  H. Shang,et al.  Achievement of Low-Resistivity Diffusion Joint of REBCO Coated Conductors by Improving the Interface Connection of Ag Stabilizer , 2021, IEEE Transactions on Applied Superconductivity.

[3]  J. MacManus‐Driscoll,et al.  Processing and application of high-temperature superconducting coated conductors , 2021, Nature Reviews Materials.

[4]  M. Yoshikawa,et al.  Development of a persistent-mode NMR magnet with superconducting joints between high-temperature superconductors , 2021, Superconductor Science and Technology.

[5]  H. Shang,et al.  Study on Electromechanical Properties of Solder Jointed YBCO Coated Conductors With Etched Copper Stabilizer Under Axial Tension , 2020, IEEE Transactions on Applied Superconductivity.

[6]  I. Chernykh,et al.  Superconducting joint fabrication for HTS second generation GdBCO/YBCO tapes , 2019, Superconductors Science and Technology.

[7]  H. Gu,et al.  Bending properties of solder joint of YBCO coated conductors by etching copper stabilizer , 2019, Physica C: Superconductivity and its Applications.

[8]  I. Chernykh,et al.  A Superconducting Joint for 2G HTS Tapes , 2019, Technical Physics Letters.

[9]  S. Awaji,et al.  Microstructures of superconducting joint between GdBa2Cu3Oy-coated conductors via additionally deposited precursor films , 2019, Japanese Journal of Applied Physics.

[10]  Y. Yanagisawa,et al.  Superconducting joint between multi-filamentary Bi2Sr2Ca2Cu3O10+δ tapes based on incongruent melting for NMR and MRI applications , 2019, Superconductor Science and Technology.

[11]  Y. Yanagisawa,et al.  Measurement of Persistent Current in a Gd123 Coil With a Superconducting Joint Fabricated by the CJMB Method , 2018, IEEE Transactions on Applied Superconductivity.

[12]  T. Takao,et al.  Fabrication, microstructure and persistent current measurement of an intermediate grown superconducting (iGS) joint between REBCO-coated conductors , 2017 .

[13]  P. Feng,et al.  Critical current survival in the YBCO superconducting layer of a delaminated coated conductor , 2016, 1612.08553.

[14]  C. Grovenor,et al.  Persistent current joints between technological superconductors , 2015 .

[15]  Y. Yanagisawa,et al.  Development of a superconducting joint between a GdBa2Cu3O7-δ-coated conductor and YBa2Cu3O7−δ bulk: towards a superconducting joint between RE (Rare Earth) Ba2Cu3O7−δ-coated conductors , 2015 .

[16]  M. Dedicatoria,et al.  Joining of REBCO Coated Conductor Tapes Using Ultrasonic Welding Method , 2015, IEEE Transactions on Applied Superconductivity.

[17]  Jongmin Kim,et al.  Pursuing low joint resistivity in Cu-stabilized REBa2Cu3Oδ coated conductor tapes by the ultrasonic weld–solder hybrid method , 2015 .

[18]  C. Senatore,et al.  Progresses and challenges in the development of high-field solenoidal magnets based on RE123 coated conductors , 2014, Superconductor science & technology.

[19]  Haigun Lee,et al.  Laser drilling: enhancing superconducting joint of GdBa2Cu3O7 − δ coated conductors , 2014 .

[20]  S. Yoo,et al.  Stability phase diagram of GdBa2Cu3O7−δ in low oxygen pressures , 2014 .

[21]  Xavier Obradors,et al.  Coated conductors for power applications: materials challenges , 2014 .

[22]  Haigun Lee,et al.  The influence of heat-treatment and oxygenation annealing on the superconducting properties of YBCO coated conductors , 2009 .

[23]  Q. Jia,et al.  Materials science challenges for high-temperature superconducting wire. , 2007, Nature materials.

[24]  J. Kato,et al.  Diffusion joint of YBCO coated conductors using stabilizing silver layers , 2006 .

[25]  Y. Masuda,et al.  Production of YBa2Cu3O7-x Thick Films on Ag Metal Substrate Controlled by Oxygen , 1992 .

[26]  Baker,et al.  Anisotropy of oxygen tracer diffusion in single-crystal YBa2Cu3O7- delta. , 1991, Physical review. B, Condensed matter.

[27]  D. Ginley,et al.  Orthorhombic‐tetragonal phase transition in high‐temperature superconductor YBa2Cu3O7 , 1987 .