Reduction of fine iron ore via a two-step fluidized bed direct reduction process

The industrial application of fluidized bed direct reduction (DR) process for fine iron ore is hampered by the sticking of direct reduction iron (DRI) particles. In the present study, the carbon precipitation reaction is coupled with the reduction reaction of fine iron ore to modify the cohesive force among DRI particles. The competition between the reduction reaction of fine iron ore and the carbon precipitation reaction leads to three types of fluidization behaviors: fluidization, unstable fluidization and defluidization. The carbon precipitation reaction is dominant at the temperature below 600-675 degrees C, and the presence of H-2 could retard the growth of iron whiskers and promote carbon precipitation. A new type of DRI particle covered with carbon shell is therefore constructed and named as DR!, particle. The growth of iron and carbon gasification can destroy the carbon shell, and lead to the increase of stickiness; however, the presence of CO can retard or prevent the destroying. The C/Fe mass ratio on the surface has significant influence on the stickiness and also the fluidization behavior of DRIc particles. The lower limit of C/Fe mass ratio, below which defluidization occurs, increases sharply with increasing temperature. Based on these findings, a two-step fluidized bed DR process for fine iron ore is proposed and proved feasible, and the operating lines of the fluidization zones are indicated as maps. (C) 2014 Elsevier B.V. All rights reserved.

[1]  E. T. Turkdogan,et al.  Catalytic effect of iron on decomposition of carbon monoxide: I. carbon deposition in H2-CO Mixtures , 1974, Metallurgical and Materials Transactions B.

[2]  Hong-zhong Li,et al.  Direct reduction of hematite powders in a fluidized bed reactor , 2013 .

[3]  J. Gransden,et al.  The sticking of iron ore during reduction by hydrogen in a fluidized bed , 1974 .

[4]  A. A. Omar,et al.  Carbon Monoxide Reduction and Accompanying Swelling of Iron Oxide Compacts , 1996 .

[5]  M. Warzée,et al.  The solid reaction products of the catalytic decomposition of carbon monoxide on iron at 550°C , 1969 .

[6]  J. Schenk.  Recent status of fluidized bed technologies for producing iron input materials for steelmaking , 2011 .

[7]  R. Fruehan.  The rate of reduction of iron oxides by carbon , 1977 .

[8]  Mirko S. Komatina,et al.  The sticking problem during direct reduction of fine iron ore in the fluidized bed , 2004 .

[9]  Y. Iguchi,et al.  Relation between Sulfur Pressure and Sticking of Fine Iron Ores in Fluidized Bed Reduction , 1990 .

[10]  P. Harriott,et al.  Reactivity of Deposited Carbon , 1954 .

[11]  G. Krauss.  Steels: Processing, Structure, And Performance , 2005 .

[12]  J. Szekely,et al.  The influence of carbon deposition on the reduction kinetics of commercial grade hematite pellets with CO, H2, and N2 , 1983 .

[13]  H. A. Mashhadi,et al.  An Investigation on the Reduction of Iron Ore Pellets in Fixed Bed of Domestic Non-Coking Coals , 2008 .

[14]  R. Snow,et al.  Influence of Impurities and Role of Iron Carbides in Deposition of Carbon from Carbon Monoxide , 1956 .

[15]  J. Schenk,et al.  Fluidized-bed technology for the production of iron products for steelmaking , 2009 .

[16]  Zhi Wang,et al.  A comparative study of influence of fluidized conditions on sticking time during reduction of Fe2O3 particles with CO , 2012 .

[17]  E. T. Turkdogan,et al.  Catalytic effect of iron on decomposition of carbon monoxide: II. Effect of additions of H2, H2O, CO2, SO2 and H2S , 1974, Metallurgical and Materials Transactions B.

[18]  Philip L. Walker,et al.  Gas Reactions of Carbon , 1975 .

[19]  Y. Iguchi,et al.  Factors Affecting the Sticking of Fine Iron Ores during Fluidized Bed Reduction , 1992 .

[20]  Zhi Wang,et al.  Prevention of agglomeration/defluidization in fluidized bed reduction of Fe2O3 by CO: The role of magnesium and calcium oxide , 2013 .

[21]  Hyungsun Kim,et al.  Sticking behaviour in direct reduction of iron ore , 1999 .

[22]  Jc Jaap Schouten,et al.  Monitoring the quality of fluidization using the short-term predictability of pressure fluctuations , 1998 .

[23]  D. Neuschütz.  Sticking prevention during fine‐ore metallization in two‐stage smelting‐reduction processes , 1991 .

[24]  Zhi Wang,et al.  Defluidization behavior of iron powders at elevated temperature: Influence of fluidizing gas and particle adhesion , 2012 .

[25]  P. Walker,et al.  Carbon Formation from Carbon Monoxide-Hydrogen Mixtures over Iron Catalysts.I. Properties of Carbon Formed , 1959 .

[26]  Jesse J. Brown,et al.  Mechanism of Iron Catalysis of Carbon Monoxide Decomposition in Refractories , 1989 .

[27]  R. Schenck,et al.  Ueber die Spaltung des Kohlenoxyds und das Hochofengleichgewicht , 1903 .

[28]  H. Gudenau,et al.  Fluidized bed reduction as the prestep of smelting reduction , 1989 .