论文信息 - Static and fatigue delamination from discontinuous plies - Experimental and numerical investigations

Static and fatigue delamination from discontinuous plies - Experimental and numerical investigations

Cut ply specimens of IM7/8552 carbon/epoxy laminates were tested under monotonic and cyclic tensile loading. Experimental results were used to validate new cohesive interface element formulations for static and fatigue delamination. Results are presented in terms of static failure loads and fatigue crack growth rates.

[1] Aj Russell,et al. Predicting Interlaminar Fatigue Crack Growth Rates in Compressively Loaded Laminates , 1989 .

[2] Leif Asp,et al. Mixed-mode delamination growth in carbon-fibre composite laminates under cyclic loading , 2004 .

[3] Antonio Miravete,et al. Application of the Finite-Element Method to Predict the Onset of Delamination Growth , 2004 .

[4] Michael R Wisnom,et al. Specimens with Cut Central Plies An Experimental and Analytical Study of Delamination of Unidirectional , 2010 .

[5] Michael R Wisnom,et al. A concise interface constitutive law for analysis of delamination and splitting in composite materials and its application to scaled notched tensile specimens , 2007 .

[6] Jo Ann Dauzat,et al. Part V , 1997, Hydrobiologia.

[7] Paul Robinson,et al. Numerical simulation of fatigue‐driven delamination using interface elements , 2005 .

[8] Pedro P. Camanho,et al. Simulation of delamination in composites under high-cycle fatigue , 2007 .

[9] M. Wisnom,et al. Predicting the effect of through-thickness compressive stress on delamination using interface elements , 2008 .