Thermal history and microstructure during friction stir welding of Al–Mg alloy

In this study, a commercial aluminum–magnesium alloy was friction stir welded (FSW) at a constant rotational speed of 1016 rpm and different welding speeds from 50 to 400 mm/min. Temporal thermal histories of the process were recorded at different locations from the weld line and transformed to spatial temperature distribution near the weld line. Tensile and microhardness measurements were also performed and the microstructure in the weld zone was investigated. Results of this revealed that an increase in welding speed causes a decrease in the stir zone temperature, which leads to a decrease in the stir zone grain size. As a result, both tensile strength and hardness increased with an increase in welding speed. Dynamic recrystallization and post-weld static grain growth were the controlling factors of stir zone grain size. The grain size correlated closely with the Zener–Hollomon parameter. Slow cooling resulted in larger post-weld grain size than what is normally expected.

[1]  S. L. Semiatin,et al.  Continuous dynamic recrystallization during friction stir welding of high strength aluminum alloys , 2000 .

[2]  Z. Evis.  Al3+ Doped Nano-Hydroxyapatites and their Sintering Characteristics , 2006 .

[3]  H. Kokawa,et al.  Experimental simulation of recrystallized microstructure in friction stir welded Al alloy using a plane-strain compression test , 2008 .

[4]  E. Nes,et al.  Substructure evolution during different hot deformation processes of commercial non-heat treatable aluminium alloys , 1996 .

[5]  Bo Li,et al.  Numerical simulation and experimental investigation on friction stir welding of 6061-T6 aluminum alloy , 2014 .

[6]  Hongwu Zhang,et al.  Numerical studies on controlling of process parameters in friction stir welding , 2009 .

[7]  Jie Liu,et al.  Effects of welding speed on the microstructure and hardness in friction stir welding joints of 6005A-T6 aluminum alloy , 2013 .

[8]  Yuang-Cherng Chiou,et al.  Experimental study on temperature distributions within the workpiece during friction stir welding of aluminum alloys , 2008 .

[9]  Wu Jianjun,et al.  Computational fluid dynamics studies on heat generation during friction stir welding of aluminum alloy , 2013 .

[10]  Fahrettin Ozturk,et al.  Review of warm forming of aluminum-magnesium alloys , 2008 .

[11]  I. Shigematsu,et al.  Production of Ultra-Fine Grained Aluminum Alloy using Friction Stir Process , 2003 .

[12]  F. Ozturk,et al.  Tensile deformation behavior of AA5083-H111 at cold and warm temperatures , 2010 .

[13]  Thomas H. North,et al.  Strain Rates and Grain Growth in Al 5754 and Al 6061 Friction Stir Spot Welds , 2007 .

[14]  H. Kokawa,et al.  Effect of peak temperature during friction stir welding on microstructure evolution of aluminum alloy 1050 , 2013 .

[15]  R. M. Leal,et al.  Microstructural and mechanical characterisation of 5XXX-H111 friction stir welded tailored blanks , 2011 .

[16]  N. Fredj,et al.  Recrystallization mechanisms in 5251 H14 and 5251 O aluminum friction stir welds , 2007 .

[17]  Sung-Tae Hong,et al.  Friction stir butt welding of A5052-O aluminum alloy plates , 2012 .

[18]  E. Kaluç,et al.  Comparison between microstructure characteristics and joint performance of 5086-H32 aluminium alloy welded by MIG, TIG and friction stir welding processes , 2007 .

[19]  Hiroyuki Kokawa,et al.  Post-weld formability of friction stir welded Al alloy 5052 , 2004 .

[20]  J. C. Huang,et al.  Relationship between grain size and Zener¿Holloman parameter during friction stir processing in AZ31 Mg alloys , 2004 .

[21]  A. Tavakoli,et al.  The Influence of Process Parameters on Microstructure and Mechanical Properties of Friction Stir Welded Al 5083 Alloy Lap Joint , 2012 .

[22]  Zhaodong Zhang,et al.  Numerical studies of tool diameter on strain rates, temperature rises and grain sizes in friction stir welding , 2015 .

[23]  L. M. Volpone,et al.  ALUMINIUM ALLOYS IN THIRD MILLENNIUM SHIPBUILDING: MATERIALS, TECHNOLOGIES, PERSPECTIVES. , 2005 .

[24]  E. Cerri,et al.  Influence of high temperature thermal treatment on grain stability and mechanical properties of medium strength aluminium alloy friction stir welds , 2013 .

[25]  J. Jonas,et al.  Dynamic and post-dynamic recrystallization under hot, cold and severe plastic deformation conditions , 2014 .

[26]  J. Heerens,et al.  Asymmetric mechanical properties and tensile behaviour prediction of aluminium alloy 5083 friction stir welding joints , 2013 .

[27]  G. Cui,et al.  The origin of non-uniform microstructure and its effects on the mechanical properties of a friction stir processed Al–Mg alloy , 2009 .

[28]  M. Kopyściański,et al.  A Coupled Thermal/Material Flow Model of Friction Stir Welding Applied to Sc-Modified Aluminum Alloys , 2013, Metallurgical and Materials Transactions A.