Effect of length of thinning area on the failure behavior of carbon steel pipe containing a defect of wall thinning

Abstract The present study performed pipe failure tests using 102 mm-Sch. 80 carbon steel pipe with various simulated wall thinning defects, to investigate the effect of axial length of wall thinning and internal pressure on the failure behavior of pipe thinned by flow accelerated corrosion (FAC). The tests were conducted under loading conditions of four-point bending with and without internal pressure. The results showed that a failure mode of pipe with a defect depended on the magnitude of internal pressure and axial thinning length as well as stress type and thinning depth and circumferential angle. Both load carrying capability (LCC) and deformation capability (DC) were depended on stress type in the thinning area and dimensions of thinning defect. For applying tensile stress to the thinned area, the dependence of LCC on the axial length of wall thinning was determined by circumferential thinning angle, and the DC was proportionally increased with increase in axial length of wall thinning regardless of the circumferential angle. For applying compressive stress to thinned area, however, the LCC was decreased with increase in axial length of the thinned area. Also, the effect of internal pressure on failure behavior was characterized by failure mode of thinned pipe, and it promoted crack occurrence and mitigated a local buckling of the thinned area.