T-stress and crack path stability of DCDC specimens

The T-stress term of DCDC specimens is computed using the Boundary Collocation procedure and limit case consideratons. This parameter allows to understand path stability as found in literature for subcritical crack growth in galss.

Theo Fett | Dietrich Munz

[1] J. E. Ritter,et al. Further analysis of the DCDC specimen with an offset hole , 2001 .

[2] Solveig Melin,et al. The influence of the T-stress on the directional stability of cracks , 2002 .

[3] S. Melin. On the directional stability of wedging , 1991, International Journal of Fracture.

[4] P. Leevers,et al. Inherent stress biaxiality in various fracture specimen geometries , 1982 .

[5] A. Evans,et al. Analysis of the double cleavage drilled compression specimen for interface fracture energy measurements over a range of mode mixities , 1995 .

[6] J. Rice,et al. Slightly curved or kinked cracks , 1980 .

[7] J. E. Ritter,et al. Subcritical Crack Growth in Soda–Lime Glass under Mixed‐Mode Loading , 2004 .