Effects of ionizing radiation on properties of monolayer and multilayer flexible food packaging materials

Abstract Volatile compounds produced in flexible food packaging materials (LDPE, EVAc, PET/PE/EVOH/PE) during electron beam irradiation were isolated by purge and trap technique and identified by combined gas chromatography–mass spectrometry (GC/MS), after thermal desorption and concentration. For comparison purposes non-irradiated films were also studied. Film samples were irradiated at low (5 kGy, corresponding to cold pasteurization), intermediate (20 kGy, corresponding to cold sterilization) and high (100 kGy) doses. It was observed that a number of volatile compounds are produced after irradiation in all cases. Furthermore the amounts of all volatile compounds increase with increasing irradiation dose. Both primary (methyl-derivatives etc.) as well as secondary i.e. oxidation products (ketones, aldehydes, alcohols, carboxylic acids etc.) are produced upon irradiation. These products may affect organoleptic properties and thus shelf-life of prepackaged irradiated foods. No significant changes were observed in the structure of polymer matrices as exhibited by IR spectra after irradiation of the materials at doses tested. Likewise, no significant changes were observed in O 2 , H 2 O and CO 2 permeability values of plastic packaging materials after irradiation.

[1]  T. Acree,et al.  Identification of odor-active compounds resulting from thermal oxidation of polyethylene , 1992 .

[2]  E. Hegazy,et al.  Radiation‐induced oxidative degradation of isotactic polypropylene , 1981 .

[3]  J. Fortin,et al.  Irradiation of a barrier film: Analysis of some mass transfer aspects , 1995 .

[4]  S. G. Gilbert,et al.  Isolation and Identification of Potential Migrants in Gamma-Irradiated Plastic Laminates by Using GC/MS and GC/IR , 1991 .

[5]  Yoshikazu Tanaka,et al.  Identification of the volatiles from low density polyethylene film irradiated with an electron beam , 1983 .

[6]  Yoshikazu Tanaka,et al.  Effects of Film Variety on the Amounts of Carboxylic Acids from Electron Beam Irradiated Polyethylene Film , 1984 .

[7]  C. Jr. Merritt.  Qualitative and quantitative aspects of trace volatile components in irradiated foods and food substances , 1972 .

[8]  J. Killoran.  Chemical and physical changes in food packaging materials exposed to ionizing radiation , 1972 .

[9]  E. Hegazy,et al.  Radiation‐induced oxidative degradation of poly(vinyl chloride) , 1981 .

[10]  R. Buchalla,et al.  Effects of Ionizing Radiation on Plastic Food Packaging Materials: A Review. , 1993, Journal of food protection.

[11]  T. Grünewald,et al.  Untersuchung der Einwirkung ionisierender Strahlung auf die Gas- und Wasserdampf-Durchlässigkeit von Verpackungs-Folien , 1961 .

[12]  Y. Hama,et al.  The effect of irradiation on polyethylene double-laminated by ethylene-vinyl alcohol copolymer , 1991 .

[13]  R. Buchalla,et al.  Effects of Ionizing Radiation on Plastic Food Packaging Materials: A Review. , 1993, Journal of food protection.

[14]  H. LeClair,et al.  Effects of Radiation on Plastic Packaging Films , 1958 .

[15]  B. Pascat,et al.  Effects of B‐ionizing radiation on the properties of flexible packaging materials , 1990 .

[16]  J. Killoran.  PACKAGING OF IRRADIATED FOODS. , 1967 .

[17]  P. Swoboda,et al.  Volatile odorous compounds responsible for metallic, fishy taint formed in butterfat by selective oxidation , 1977 .

[18]  Yoshikazu Tanaka,et al.  Effects of the conditions for electron beam irradiation on the amounts of volatiles from irradiated polyethylene film. , 1984 .