Effect of build orientation on the surface quality, microstructure and mechanical properties of selective laser melting 316L stainless steel

Purpose The purpose of this paper is to investigate the density, surface quality, microstructure and mechanical properties of the components of the selective laser melting (SLM) parts made at different building orientations. SLM is an additive manufacturing technique for three-dimensional parts. The process parameters are known to affect the properties of the eventual part. In this study, process parameters were investigated in the building of 316L structures at a variety of building orientations and for which the fracture toughness was measured. Design/methodology/approach Hardness and tensile tests were carried out to evaluate the effect of consolidation on the mechanical performance of specimens. Optical and electron microscopy were used to characterise the microstructure of the SLM specimens and their effects on properties relating to fracture and the mechanics. It was found that the density of built samples is 96 per cent, and the hardness is similar in comparison to conventional material. Findings The highest fracture toughness value was found to be 176 MPa m^(1/2) in the oz. building direction, and the lowest value was 145 MPa m^(1/2) in the z building direction. This was due to pores and some cracks at the edge, which are slightly lower in comparison to a conventional product. The build direction does have an effect on the microstructure of parts, which subsequently has an effect upon their mechanical properties and surface quality. Dendritic grain structures were found in oz. samples due to the high temperature gradient, fast cooling rate and reduced porosity. The tensile properties of such parts were found to be better than those made from conventional material. Originality/value The relationship between the process parameters, microstructure, surface quality and toughness has not previously been reported.

[1]  Wilfried Kurz,et al.  Epitaxial laser metal forming: analysis of microstructure formation , 1999 .

[2]  Tahar Laoui,et al.  Balling processes during selective laser treatment of powders , 2004 .

[3]  K. Salonitis,et al.  Simulation of metallic powder bed additive manufacturing processes with the finite element method: A critical review , 2017 .

[4]  J. Kruth,et al.  Part and material properties in selective laser melting of metals , 2010 .

[5]  Yulin Hao,et al.  Manufacture by selective laser melting and mechanical behavior of a biomedical Ti–24Nb–4Zr–8Sn alloy , 2011 .

[6]  T. Childs,et al.  Layer Formation Studies in Selective Laser Melting of Steel Powders , 2006 .

[7]  K. Mumtaz,et al.  Selective laser melting of Inconel 625 using pulse shaping , 2010 .

[8]  Di Wang,et al.  Accuracy and density optimization in directly fabricating customized orthodontic production by selective laser melting , 2012 .

[9]  K. Osakada,et al.  Flexible manufacturing of metallic products by selective laser melting of powder , 2006 .

[10]  T. Childs,et al.  Raster scan selective laser melting of the surface layer of a tool steel powder bed , 2005 .

[11]  I. E. Kalu.  Numerical Modeling of Wellbore Instability (SHEAR Failure) using Fracture Mechanics Approach , 2013 .

[12]  Amauri Garcia,et al.  Effect of dendritic arm spacing on mechanical properties and corrosion resistance of Al 9 Wt Pct Si and Zn 27 Wt Pct Al alloys , 2006 .

[13]  R. Everson,et al.  Surface roughness analysis, modelling and prediction in selective laser melting , 2013 .

[14]  Rémy Glardon,et al.  Sintering of commercially pure titanium powder with a Nd:YAG laser source , 2003 .

[15]  Ahmed Hussein,et al.  Evaluations of cellular lattice structures manufactured using selective laser melting , 2012 .

[16]  Johann Sienz,et al.  Investigation into the effect of process parameters on microstructural and physical properties of 316L stainless steel parts by selective laser melting , 2014, The International Journal of Advanced Manufacturing Technology.

[17]  R. Reddy,et al.  Developments in the processing and properties of particulate Al-Si composites , 1997 .

[18]  D. Browne,et al.  The influence of cooling conditions on grain size, secondary phase precipitates and mechanical properties of biomedical alloy specimens produced by investment casting. , 2013, Journal of the mechanical behavior of biomedical materials.

[19]  Jean-Pierre Kruth,et al.  Microstructural investigation of Selective Laser Melting 316L stainless steel parts exposed to laser re-melting , 2011 .

[20]  Marleen Rombouts.  Selective Laser Sintering/Melting of Iron-Based Powders (Selectief laser sinteren/smelten van ijzergebaseerde poeders) , 2006 .

[21]  R. Morgan,et al.  Density analysis of direct metal laser re-melted 316L stainless steel cubic primitives , 2004 .

[22]  M. L. Hamilton,et al.  The mechanical properties of 316L/304L stainless steels, Alloy 718 and Mod 9Cr–1Mo after irradiation in a spallation environment , 2001 .

[23]  Liang Hao,et al.  Selective laser melting of a stainless steel and hydroxyapatite composite for load-bearing implant development , 2009 .

[24]  S. Sankaré,et al.  Influence of powder characteristics in laser direct metal deposition of SS316L for metallic parts manufacturing , 2012 .

[25]  P. Fox,et al.  Direct laser remelting of iron with addition of boron , 2004 .

[26]  V. Leskovšek,et al.  Relations between fracture toughness, hardness and microstructure of vacuum heat-treated high-speed steel , 2002 .

[27]  T. Takalo,et al.  Austenitic solidification mode in austenitic stainless steel welds , 1979 .

[28]  D. Soares,et al.  Sensitivity of different Al–Si alloys to centrifugal casting effect , 2010 .

[29]  Yifu Shen,et al.  Balling phenomena in direct laser sintering of stainless steel powder: Metallurgical mechanisms and control methods , 2009 .

[30]  M. Lima,et al.  Microstructure and mechanical behavior of laser additive manufactured AISI 316 stainless steel stringers , 2014 .

[31]  W. Soboyejo.  Mechanical Properties of Engineered Materials , 2019 .

[32]  T. Childs,et al.  Selective laser sintering (melting) of stainless and tool steel powders: Experiments and modelling , 2005 .