Preparation of nanostructured nitrogen-containing carbon catalysts for the oxygen reduction reaction from SiO2- and MgO-supported metal particles

Abstract Nitrogen-containing carbon was prepared from the vapor deposition of acetonitrile at 900 °C over silica- or magnesia-supported Fe, Co, and Ni particles. The byproducts of pyrolysis were monitored by mass spectrometry. The carbon formed from silica precursors was washed with KOH to remove the silica and HCl to remove metal particles, whereas the carbon formed from magnesia samples was washed with HCl to remove the support and the metal. The solid carbon product was characterized with N2 physisorption to measure surface area and pore volume distribution, X-ray diffraction to determine the crystalline phases present, and temperature-programmed oxidation to determine ash and nitrogen content. Magnesia was more readily removed from the carbon compared with silica. A significant amount of metal, encased in carbon, remained in the samples after washing. The Co particles led to a higher content of bulk nitrogen in the carbon, as high as 2.9% based on oxidation measurements. Electron microscopy imaging confirmed that all of the metal particles catalyzed the formation of various types of carbon nanofibers, with the diameter and structure of the fibers varying with different metal–support precursor combinations. A possible application for these fibers is oxygen reduction reaction catalysts for proton-exchange membrane fuel cell cathodes.

[1]  P. Bertrand,et al.  Activation and characterization of Fe-based catalysts for the reduction of oxygen in polymer electrolyte fuel cells , 1998 .

[2]  T. Nakajima,et al.  Synthesis of high crystalline carbon-nitrogen layered compounds by CVD using nickel and cobalt catalysts , 1997 .

[3]  W. Hsu,et al.  Compartmentalized CNx nanotubes: Chemistry, morphology, and growth , 2002 .

[4]  Umit S. Ozkan,et al.  Non-metal Catalysts for Dioxygen Reduction in an Acidic Electrolyte , 2006 .

[5]  T. Nakajima,et al.  Electrochemical behavior of carbon alloy CxN prepared by CVD using a nickel catalyst , 1998 .

[6]  M. Kim,et al.  The relationship between metal particle morphology and the structural characteristics of carbon deposits , 1997 .

[7]  Hardcover,et al.  Carbon: Electrochemical and Physicochemical Properties , 1988 .

[8]  Zhongfan Liu,et al.  CVD growth of N-doped carbon nanotubes on silicon substrates and its mechanism. , 2005, The journal of physical chemistry. B.

[9]  K. Stevenson,et al.  Influence of nitrogen doping on oxygen reduction electrocatalysis at carbon nanofiber electrodes. , 2005, The journal of physical chemistry. B.

[10]  J. Lahaye,et al.  Porous structure and surface chemistry of nitrogen containing carbons from polymers , 1999 .

[11]  B. Way,et al.  The Effect of Boron Substitution in Carbon on the Intercalation of Lithium in Li x ( B z C 1 − z ) 6 , 1994 .

[12]  M. Audier,et al.  Kinetic and microscopic aspects of catalytic carbon growth , 1985 .

[13]  M. Yudasaka,et al.  Radially modulated nitrogen distribution in CNx nanotubular structures prepared by CVD using Ni phthalocyanine , 2000 .

[14]  P. A. Thrower,et al.  On the mechanism of possible influence of heteroatoms of nitrogen, boron and phosphorus in a carbon matrix on the catalytic activity of carbons in electron transfer reactions , 2000 .

[15]  M. Terrones,et al.  Pyrolytically grown BxCyNz nanomaterials: nanofibres and nanotubes , 1996 .

[16]  V. Ogenko,et al.  Matrix Synthesis of N-Containing Carbon Nanotubes , 2002 .

[17]  Colin W. Park,et al.  Catalyst support effects in the growth of structured carbon from the decomposition of ethylene over nickel , 2004 .

[18]  D. Guay,et al.  Influence of Nitrogen‐Containing Precursors on the Electrocatalytic Activity of Heat‐Treated Fe ( OH ) 2 on Carbon Black for O 2 Reduction , 1998 .

[19]  N. Grobert,et al.  Carbon Nitride Nanocomposites: Formation of Aligned CxNy Nanofibers , 1999 .

[20]  Umit S. Ozkan,et al.  The role of nanostructure in nitrogen-containing carbon catalysts for the oxygen reduction reaction , 2006 .

[21]  Alan Chambers,et al.  Catalytic Engineering of Carbon Nanostructures , 1995 .

[22]  Jeunghee Park,et al.  Catalyst effect on carbon nanotubes synthesized by thermal chemical vapor deposition , 2002 .

[23]  Stephen A. Morin,et al.  Structure, composition, and chemical reactivity of carbon nanotubes by selective nitrogen doping , 2006 .

[24]  Y. Hao,et al.  The effect of hydrogen on the formation of nitrogen-doped carbon nanotubes via catalytic pyrolysis of acetonitrile , 2003 .

[25]  A. Govindaraj,et al.  B–C–N, C–N and B–N nanotubes produced by the pyrolysis of precursor molecules over Co catalysts , 1998 .

[26]  B. Way,et al.  Behavior of nitrogen-substituted carbon (N[sub z]C[sub 1[minus]z]) in Li/Li(N[sub z]C[sub 1[minus]z])[sub 6] cells , 1994 .

[27]  P. Bertrand,et al.  Is nitrogen important in the formulation of Fe-based catalysts for oxygen reduction in solid polymer fuel cells? , 1997 .

[28]  R. Baker,et al.  Catalytic growth of carbon filaments , 1989 .