Influence of sample geometry and microstructure on the hydrogen induced cracking characteristics under uniaxial load

Abstract The present work evaluates hydrogen induced cracking in a TRIP (transformation induced plasticity) assisted steel and pure iron. The goal of this work is to understand the effect of the macroscopic stress distribution in the material on the hydrogen induced cracking phenomenon. Additionally, the effect of a complex multiphase microstructure on the characteristics of hydrogen induced cracking was investigated by comparing results for TRIP-assisted steel and pure iron as reference material. Tensile tests on notched and unnotched samples combined with in-situ electrochemical hydrogen charging were conducted. Tests were performed until the tensile strength was reached and until fracture. The resulting hydrogen induced cracks were studied by optical microscopy and scanning electron microscopy (SEM). Hydrogen induced cracks showed a typical S-shape and crack propagation was mainly transgranular, independently of the presence of a notch or the material's microstructure. This was also the case for the V-shaped secondary crack network and resulting stepped crack morphology characteristic for hydrogen induced damage. These observations indicate that the stress state surrounding the crack tip has a very large impact on the hydrogen induced cracking characteristics. The use of a notch or the presence of a different microstructure did not influence the overall hydrogen induced cracking features, but did change the kinetics of the hydrogen induced cracking process.

[1]  K. Verbeken,et al.  Fractographic analysis of the role of hydrogen diffusion on the hydrogen embrittlement susceptibility of DP steel , 2016 .

[2]  Kim Verbeken,et al.  Characterization of hydrogen induced cracking in TRIP-assisted steels , 2015 .

[3]  K. Verbeken,et al.  On the synergy of diffusible hydrogen content and hydrogen diffusivity in the mechanical degradation of laboratory cast Fe-C alloys , 2016 .

[4]  R. Mclellan,et al.  The solubility and diffusivity of hydrogen in well-annealed and deformed iron , 1983 .

[5]  K. Tsuzaki,et al.  Effect of hydrogen on the fracture behavior of high strength steel during slow strain rate test , 2007 .

[6]  A. Bakker,et al.  Hydrogen transport near a blunting crack tip , 1999 .

[7]  P. Doig,et al.  A model for the initiation of hydrogen embrittlement cracking at notches in gaseous hydrogen environments , 1977 .

[8]  K. Verbeken,et al.  Hydrogen trapping and hydrogen induced mechanical degradation in lab cast Fe-C-Cr alloys , 2016 .

[9]  C. Thaulow,et al.  Modelling of hydrogen diffusion and hydrogen induced cracking in supermartensitic and duplex stainless steels , 2008 .

[10]  B. L. D. Silva,et al.  Hydrogen induced stress cracking in UNS S32750 super duplex stainless steel tube weld joint , 2015 .

[11]  K. Verbeken,et al.  Combined thermal desorption spectroscopy, differential scanning calorimetry, scanning electron microscopy and X-ray diffraction study of hydrogen trapping in cold deformed TRIP steel , 2012 .

[12]  R. A. Oriani,et al.  Effect of tensile and compressive elastic stress on equilibrium hydrogen solubility in a solid , 1970 .

[13]  S. Ramamurthy.  Influence of the Applied Stress Rate on the Stress Corrosion Cracking of 4340 and 3.5NiCrMoV Steels , 2011 .

[14]  K. Verbeken,et al.  Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging , 2011 .

[15]  J. Hirth,et al.  Effects of hydrogen on the properties of iron and steel , 1980 .

[16]  S. Barnett,et al.  Linking the microstructure, performance and durability of Ni-yttria-stabilized zirconia solid oxide fuel cell anodes using three-dimensional focused ion beam–scanning electron microscopy imaging , 2011 .

[17]  K. Verbeken,et al.  Evaluation of hydrogen trapping in high strength steels by thermal desorption spectroscopy , 2012 .

[18]  D. Hardie,et al.  The effect of stress concentration on hydrogen embrittlement of a low alloy steel , 1996 .

[19]  William D. Callister,et al.  Materials Science and Engineering: An Introduction , 1985 .

[20]  L. Marchetti,et al.  Hydrogen embrittlement susceptibility of tempered 9%Cr–1%Mo steel , 2011 .

[21]  P. Sofronis,et al.  Hydrogen transport and large strain elastoplasticity near a notch in alloy X-750 , 1998 .

[22]  K. Verbeken,et al.  Microstructural characterization of hydrogen induced cracking in TRIP-assisted steel by EBSD , 2016 .

[23]  R. Kirchheim.  Revisiting hydrogen embrittlement models and hydrogen-induced homogeneous nucleation of dislocations , 2010 .

[24]  A. Nagao,et al.  Visualization of hydrogen transport in high strength steels affected by stress fields and hydrogen trapping , 2001 .

[25]  K. Verbeken,et al.  Evaluation of the effect of V4C3 precipitates on the hydrogen induced mechanical degradation in Fe-C-V alloys , 2016 .

[26]  K. Tsuzaki,et al.  Effect of hydrogen and stress concentration on the notch tensile strength of AISI 4135 steel , 2005 .

[27]  H. H. Johnson,et al.  Deep trapping states for hydrogen in deformed iron , 1980 .

[28]  R. McMeeking,et al.  Numerical analysis of hydrogen transport near a blunting crack tip , 1989 .

[29]  L. Tsay,et al.  Effect of hydrogen environment on the notched tensile properties of T-250 maraging steel annealed by laser treatment , 2002 .

[30]  P. Sofronis,et al.  Enhanced hydrogen concentrations ahead of rounded notches and cracks-competition between plastic strain and hydrostatic stress , 1998 .