Effects of processing parameters on direct laser sintering of multicomponent Cu based metal powder

Abstract Direct laser sintering of a multicomponent Cu based metal powder was successfully processed through the mechanism of liquid phase sintering with partial melting of the powder. The effects of processing parameters such as laser power, scan speed, scan line spacing and layer thickness on the densification and microstructural evolution of the laser sintered powder were investigated. It was found that with increasing laser power or decreasing scan speed, the density of the sintered parts increased and the microstructures became denser. However, the combination of higher laser powers (>400 W) and higher scan speeds (≥0·06 ms−1) gave rise to 'balling' effect. A successive transition from discontinuous scan tracks to coherently joined ones occurs with decreasing scan line spacing. Lowering the thickness of the powder layer promises an improvement in bonding coherence between sintered layers. A single factor termed 'energy density by volume' is defined to evaluate the combined effect of various processing parameters on the density of laser sintered powder. With increasing the energy density by volume up to ∼0·16 kJ mm−3, the densification rate is relatively high. However, with intensifying the energy density over ∼0·23 kJ mm−3, the mechanism of particle bonding may change into full melting/solidification, leading to a decrease in the sintered density.

[1]  I. Chang,et al.  Selective laser sintering of gas and water atomized high speed steel powders , 1999 .

[2]  I. Chang,et al.  Selective laser sintering of gas atomized M2 high speed steel powder , 2000 .

[3]  A. Simchi,et al.  Direct laser sintering of iron–graphite powder mixture , 2004 .

[4]  Tahar Laoui,et al.  Selective laser sintering of single‐ and two‐component metal powders , 2003 .

[5]  I. Chang,et al.  Instability of scan tracks of selective laser sintering of high speed steel powder , 1999 .

[6]  David L. Bourell,et al.  Direct laser freeform fabrication of high performance metal components , 1998 .

[7]  Ericka Stricklin-Parker,et al.  Ann , 2005 .

[8]  Sanjay Kumar,et al.  An experimental design approach to selective laser sintering of low carbon steel , 2003 .

[9]  Han Tong Loh,et al.  Direct laser sintering of a copper-based alloy for creating three-dimensional metal parts , 2003 .

[10]  Jerry Y. H. Fuh,et al.  Influence of binder’s liquid volume fraction on direct laser sintering of metallic powder , 2004 .

[11]  C. S. Wright,et al.  Processing conditions and mechanical properties of high-speed steel parts fabricated using direct selective laser sintering , 2003 .

[12]  Abdolreza Simchi,et al.  Effects of laser sintering processing parameters on the microstructure and densification of iron powder , 2003 .

[13]  Abdolreza Simchi,et al.  On the development of direct metal laser sintering for rapid tooling , 2003 .

[14]  J Y H Fuh,et al.  Formation of Fe—Cu metal parts using direct laser sintering , 2003 .

[15]  Y. Song,et al.  Experimental Study of the Basic Process Mechanism for Direct Selective Laser Sintering of Low-Melting Metallic Powder , 1997 .

[16]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.