Correlation between hot carrier stress, oxide breakdown and gate leakage current for monitoring plasma processing induced damage on gate oxide

In this paper, we compare the hot carrier (HC) stress and oxide breakdown results with the fast and commonly used gate leakage current measurement. A clear correlation is found between low levels of gate leakage and both HC degradation and oxide breakdown. We, for the first time, demonstrate that the value of the gate leakage current is not only a failure indicator but also a good indicator of the reliability of the devices. A new testing method was developed to reveal latent as well as actual plasma damage, for a wide range of gate oxide quality in a very fast way. The gate oxide was stressed to break down using a ramping voltage. Moreover, oxide time-to-breakdown (t/sub bd/) was measured with constant voltage stress. These two testing methods have been compared.

[1]  Impact of reactor- and transistor-type on electron shading effects , 1999, 1999 4th International Symposium on Plasma Process-Induced Damage (IEEE Cat. No.99TH8395).

[2]  A model for channel hot carrier reliability degradation due to plasma damage in MOS devices , 1999, 1999 IEEE International Reliability Physics Symposium Proceedings. 37th Annual (Cat. No.99CH36296).

[3]  Koichi Hashimoto,et al.  New Phenomena of Charge Damage in Plasma Etching: Heavy Damage Only through Dense-Line Antenna , 1993 .

[4]  J. McVittie,et al.  Direct Measurement of Surface Charging during Plasma Etching , 1994 .

[5]  Chenming Hu,et al.  Monitoring plasma-process induced damage in thin oxide , 1993 .

[6]  C. Hu,et al.  Thin oxide charging current during plasma etching of aluminum , 1991, IEEE Electron Device Letters.

[7]  J. Educato,et al.  Application Of Damage Measurement Techniques To A Study Of Antenna Structure Charging , 1997, 2nd International Symposium on Plasma Process-Induced Damage.

[9]  Sychyi Fang,et al.  A new model for thin oxide degradation from wafer charging in plasma etching , 1992, 1992 International Technical Digest on Electron Devices Meeting.

[10]  J. Ackaert,et al.  Prevention of plasma induced damage on thin gate oxide of HDP oxide deposition, metal etch, Ar preclean processing in BEOL sub-half micron CMOS processing , 2000, 2000 5th International Symposium on Plasma Process-Induced Damage (IEEE Cat. No.00TH8479).

[11]  K. Nojiri,et al.  The Effect of Charge Build-up on Gate Oxide Breakdown during Dry Etching , 1987 .

[12]  Direction of topography dependent damage current during plasma etching , 1998, 1998 3rd International Symposium on Plasma Process-Induced Damage (Cat. No.98EX100).

[13]  Koichi Hashimoto,et al.  Charge Damage Caused by Electron Shading Effect , 1994 .

[14]  E. J. Lloyd,et al.  Fast hot-carrier aging method of charging damage measurement , 1999, 1999 4th International Symposium on Plasma Process-Induced Damage (IEEE Cat. No.99TH8395).

[15]  Qiang Guo,et al.  Hot-carrier degradation study of high-density plasma (HDP) oxide deposition process in deep-submicron NMOSFETs , 1999, Advanced Lithography.