Surface modification of coconut shell based activated carbon for the improvement of hydrophobic VOC removal.

In this study, coconut shell based carbons were chemically treated by ammonia, sodium hydroxide, nitric acid, sulphuric acid, and phosphoric acid to determine suitable modification for improving adsorption ability of hydrophobic volatile organic compounds (VOCs) on granular activated carbons (GAC). The saturated adsorption capacities of o-xylene, a hydrophobic volatile organic compound, were measured and adsorption effects of the original and modified activated carbons were compared. Results showed that GAC modified by alkalis had better o-xylene adsorption capacity. Uptake amount was enhanced by 26.5% and reduced by 21.6% after modification by NH(3)H(2)O and H(2)SO(4), respectively. Compared with the original, GAC modified by acid had less adsorption capacity. Both SEM/EDAX and BET were used to identify the structural characteristics of the tested GAC, while IR spectroscopy and Boehm's titration were applied to analysis the surface functional groups. Relationships between physicochemical characteristics of GAC and their adsorption performances demonstrated that o-xylene adsorption capacity was related to surface area, pore volume, and functional groups of the GAC surface. Removing surface oxygen groups, which constitute the source of surface acidity, and reducing hydrophilic carbon surface favors adsorption capacity of hydrophobic VOCs on carbons. The performances of modified GACs were also investigated in the purification of gases containing complex components (o-xylene and steam) in the stream.

[1]  S. Batterman,et al.  Effect of VOC loading on the ozone removal efficiency of activated carbon filters. , 2006, Chemosphere.

[2]  Wenming Qiao,et al.  Preparation of an activated carbon artifact: oxidative modification of coconut shell-based carbon to improve the strength , 2002 .

[3]  J. Shim,et al.  Studies on pore structures and surface functional groups of pitch-based activated carbon fibers. , 2003, Journal of colloid and interface science.

[4]  Takuji Yamamoto,et al.  Characterization of carbon cryogel microspheres as adsorbents for VOC. , 2010, Journal of hazardous materials.

[5]  D. Choi,et al.  Adsorption of Benzene and Toluene Vapors on Activated Carbon Fiber at 298, 323, and 348 K , 1998 .

[6]  Ki-Joong Kim,et al.  Adsorption–desorption characteristics of VOCs over impregnated activated carbons , 2006 .

[7]  J. Figueiredo,et al.  Adsorption of simple aromatic compounds on activated carbons. , 2006, Journal of colloid and interface science.

[8]  G. J. McDougall,et al.  The physical nature and manufacture of activated carbon , 1991 .

[9]  B. Girgis,et al.  Impact of surface characteristics of activated carbon on adsorption of BTEX , 2003 .

[10]  P. Carrott,et al.  Adsorption of volatile organic compounds onto activated carbon cloths derived from a novel regenerated cellulosic precursor. , 2010, Journal of hazardous materials.

[11]  B. Girgis,et al.  Modification in adsorption characteristics of activated carbon produced by H3PO4 under flowing gases , 2007 .

[12]  Ashutosh Sharma,et al.  Comparative study of removal of volatile organic compounds by cryogenic condensation and adsorption by activated carbon fiber , 2004 .

[13]  W. Su,et al.  Effect of microstructure and surface modification on the hydrogen adsorption capacity of active carbons , 2007 .

[14]  D. Cazorla-Amorós,et al.  Behaviour of activated carbons with different pore size distributions and surface oxygen groups for benzene and toluene adsorption at low concentrations , 2005 .

[15]  K. László,et al.  Analysis of Active Sites on Synthetic Carbon Surfaces by Various Methods , 2002 .

[16]  D. Fairen-jimenez,et al.  Carbon aerogels from gallic acid–resorcinol mixtures as adsorbents of benzene, toluene and xylenes from dry and wet air under dynamic conditions , 2009 .

[17]  J. Tsai,et al.  Adsorption characteristics of acetone, chloroform and acetonitrile on sludge-derived adsorbent, commercial granular activated carbon and activated carbon fibers. , 2008, Journal of hazardous materials.

[18]  P. Chiang,et al.  The surface characteristics of activated carbon as affected by ozone and alkaline treatment. , 2002, Chemosphere.

[19]  S. H. Kim,et al.  Equilibria and dynamics for mixed vapors of BTX in an activated carbon bed , 1999 .

[20]  W. E. Marshall,et al.  Adsorption of volatile organic compounds by pecan shell- and almond shell-based granular activated carbons. , 2003, Bioresource technology.

[21]  P. Samaras,et al.  Effect of activated carbons modification on porosity, surface structure and phenol adsorption. , 2008, Journal of hazardous materials.

[22]  T. García,et al.  Role of the activated carbon surface chemistry in the adsorption of phenanthrene , 2004 .

[23]  N. Verma,et al.  Removal of volatile organic compound by activated carbon fiber , 2004 .

[24]  H. Boehm.,et al.  Surface oxides on carbon and their analysis: a critical assessment , 2002 .

[25]  Artur P. Terzyk,et al.  The influence of activated carbon surface chemical composition on the adsorption of acetaminophen (paracetamol) in vitro , 2000 .

[26]  D. Mohan,et al.  Vapor-Phase Adsorption of Hexane and Benzene on Activated Carbon Fabric Cloth: Equilibria and Rate Studies† , 2002 .

[27]  Michael H. Abraham,et al.  The characterization of an active carbon in terms of selectivity towards volatile organic compounds using an LSER approach , 2000 .

[28]  C. Hsieh,et al.  Adsorption energy distribution model for VOCs onto activated carbons. , 2002, Journal of colloid and interface science.

[29]  W. Shen,et al.  Surface Chemical Functional Groups Modification of Porous Carbon , 2008 .

[30]  I. Faengmark,et al.  Modeling the influence of physico-chemical properties of volatile organic compounds on activated carbon adsorption capacity , 2003 .