Cluster Size Controls Branching between Water and Hydrogen Peroxide Production in Electrochemical Oxygen Reduction at Ptn/ITO

Deposition of size-selected Ptn clusters on indium tin oxide (ITO) films in ultrahigh vacuum was used to create electrodes with catalytic sites of controlled size. We report a study of the oxygen reduction reaction (ORR) in 0.1 M HClO4 at size-selected Ptn/ITO electrodes that were prepared and characterized without exposure to laboratory air. It was found that the ORR onset potential was size-dependent, varying from ∼0.66 V vs NHE for Pt1/ITO to ∼0.78 V vs NHE for Ptn (n ≥ 10). The maximum ORR currents per gram of Pt were found to be about an order of magnitude higher than that for ITO with 5 nm Pt particles. The branching ratio between the production of water and hydrogen peroxide in ORR was found to be strongly size-dependent. For 5 nm Pt particles on ITO or for polycrystalline Pt, little H2O2 was produced, but as cluster size was decreased, the H2O2 branching became large, suggesting that small Pt clusters could be useful selective catalysts for H2O2 electrosynthesis. Because there was no obvious corre...

[1]  Yongdan Li,et al.  Electrochemical promotion of CO combustion over Pt/YSZ under high vacuum conditions , 2012 .

[2]  Christophe Coutanceau,et al.  Development of anode catalysts for a direct ethanol fuel cell , 2004 .

[3]  R. Adzic,et al.  Electrocatalysis of oxygen on single crystal gold electrodes , 1989 .

[4]  Hubert A. Gasteiger,et al.  Oxygen reduction of platinum low-index single-crystal surfaces in alkaline solution: Rotating ring disk{sub Pt(hkl)} studies , 1996 .

[5]  P. Ross,et al.  Structure-relationships in electrocatalysis: oxygen reduction and hydrogen oxidation reactions on Pt(111) and Pt(100) in solutions containing chloride ions , 2001 .

[6]  Kimihisa Yamamoto,et al.  Size-specific catalytic activity of platinum clusters enhances oxygen reduction reactions. , 2009, Nature chemistry.

[7]  Yunzhi Gao,et al.  Oxygen reduction on platinum single-crystal electrodes in acidic solutions , 1994 .

[8]  M. Arenz,et al.  Size-selected clusters as heterogeneous model catalysts under applied reaction conditions. , 2010, Physical chemistry chemical physics : PCCP.

[9]  R. Crooks,et al.  Effect of particle size on the kinetics of the electrocatalytic oxygen reduction reaction catalyzed by Pt dendrimer-encapsulated nanoparticles. , 2007, Langmuir : the ACS journal of surfaces and colloids.

[10]  Tianpin Wu,et al.  Electronic Structure Controls Reactivity of Size-Selected Pd Clusters Adsorbed on TiO2 Surfaces , 2009, Science.

[11]  R. Durand,et al.  Electrochemical reduction of molecular oxygen on platinum single crystals , 1991 .

[12]  M. Arenz,et al.  Electrochemically induced nanocluster migration , 2010 .

[13]  R. Adzic,et al.  The influence of OH− chemisorption on the catalytic properties of gold single crystal surfaces for oxygen reduction in alkaline solutions , 1996 .

[14]  Ib Chorkendorff,et al.  The effect of size on the oxygen electroreduction activity of mass-selected platinum nanoparticles. , 2012, Angewandte Chemie.

[15]  H. White,et al.  Strong effects of cluster size and air exposure on oxygen reduction and carbon oxidation electrocatalysis by size-selected Pt(n) (n ≤ 11) on glassy carbon electrodes. , 2013, Journal of the American Chemical Society.

[16]  Weidong Cao,et al.  Microchip capillary electrophoresis with an integrated indium tin oxide electrode-based electrochemiluminescence detector. , 2003, Analytical chemistry.

[17]  J. Nørskov,et al.  Theoretical Trends in Particle Size Effects for the Oxygen Reduction Reaction , 2007 .

[18]  S. Anderson,et al.  CO adsorption and desorption on size-selected Pd(n)/TiO2(110) model catalysts: size dependence of binding sites and energies, and support-mediated adsorption. , 2012, The Journal of chemical physics.

[19]  N. Marković,et al.  Oxygen reduction and hydrogen evolution–oxidation reactions on Cu(hkl) surfaces , 2000 .

[20]  K. Mayrhofer,et al.  The impact of spectator species on the interaction of H2O2 with platinum--implications for the oxygen reduction reaction pathways. , 2013, Physical chemistry chemical physics : PCCP.

[21]  V. Vesovic,et al.  Structural effects in electrocatalysis: Oxygen reduction on the gold single crystal electrodes with (110) and (111) orientations , 1984 .

[22]  R. Crooks,et al.  Dendrimer‐Encapsulated Pt Nanoparticles: Synthesis, Characterization, and Applications to Catalysis , 1999 .

[23]  E. Gonzalez,et al.  Structure sensitivity of oxygen reduction on platinum single crystal electrodes in acid solutions , 1997 .

[24]  Ib Chorkendorff,et al.  Trends in the electrochemical synthesis of H2O2: enhancing activity and selectivity by electrocatalytic site engineering. , 2014, Nano letters.

[25]  Stefan Vajda,et al.  Size-dependent subnanometer Pd cluster (Pd4, Pd6, and Pd17) water oxidation electrocatalysis. , 2013, ACS nano.

[26]  K. Hirao,et al.  In situ chemical reductive growth of platinum nanoparticles on indium tin oxide surfaces and their electrochemical applications. , 2006, The journal of physical chemistry. B.

[27]  K. Kinoshita,et al.  Particle Size Effects for Oxygen Reduction on Highly Dispersed Platinum in Acid Electrolytes , 1990 .

[28]  M. Inaba,et al.  Effect of Agglomeration of Pt/C Catalyst on Hydrogen Peroxide Formation , 2004 .

[29]  Yang-Kook Sun,et al.  Effect of the size-selective silver clusters on lithium peroxide morphology in lithium–oxygen batteries , 2014, Nature Communications.

[30]  Tianpin Wu,et al.  Size-dependent oxidation of Pdn (n ⩽ 13) on alumina/NiAl(110): Correlation with Pd core level binding energies , 2009 .

[31]  M. Arenz,et al.  The effect of particle proximity on the oxygen reduction rate of size-selected platinum clusters. , 2013, Nature materials.

[32]  O. Petrii,et al.  Real surface area measurements in electrochemistry , 1991 .

[33]  P. Ross,et al.  Oxygen reduction on silver low-index single-crystal surfaces in alkaline solution: rotating ring disk(Ag(hkl)) studies. , 2006, The journal of physical chemistry. B.

[34]  K. Mayrhofer,et al.  Hydrogen peroxide electrochemistry on platinum: towards understanding the oxygen reduction reaction mechanism. , 2012, Physical chemistry chemical physics : PCCP.

[35]  W. Jaegermann,et al.  The Electronic Interaction of Pt-Clusters with ITO and HOPG Surfaces upon Water Adsorption , 2014 .

[36]  R. Adzic,et al.  Oxygen reduction on single crystal platinum electrodes in phosphoric acid solutions , 1999 .

[37]  H. Gasteiger,et al.  Oxygen reduction on platinum low-index single-crystal surfaces in sulfuric acid solution. Rotating ring - Pt(hkl) disk studies , 1995 .

[38]  S. Anderson,et al.  Oxygen activation and CO oxidation over size-selected Pt(n)/alumina/Re(0001) model catalysts: correlations with valence electronic structure, physical structure, and binding sites. , 2014, Physical chemistry chemical physics : PCCP.

[39]  Christos Comninellis,et al.  Electrochemical promotion of CO combustion over non-percolated Pt particles supported on YSZ using a novel bipolar configuration , 2011 .

[40]  A. I. Danilov,et al.  Surface and Subsurface Oxygen on Platinum in a Perchloric Acid Solution , 2004 .

[41]  James Thomas.  STUDENT CONSTRUCTION OF A GEL-FILLED AG/AGCL REFERENCE ELECTRODE FOR USE IN A POTENTIOMETRIC TITRATION , 1999 .

[42]  M. Arenz,et al.  The particle size effect on the oxygen reduction reaction activity of Pt catalysts: influence of electrolyte and relation to single crystal models. , 2011, Journal of the American Chemical Society.