Oxidation Resistant of Silicon-Boron Pitch Carbonization Product

The silicon-boron(Si-B) pitch was successfully synthesized by solution-thermal treatment method using coal pitch, polycarbosilane and borane pyridine as starting materials. The B-Si pitch carbonization product was attained by carbonization in the temperature 900°C under flowing argon. The Si-B pitch prepared and its carbonization product were characterized by SEM, FT-IR, TG-DSC and XRD. The results show that the carbonization product has C-Si and C-B bonds and the silicon and boron components of the product is still amorphous when it is treated at 900°C. The weight loss of the Si-B pitch carbonization product at 900°C for 12h in air atmosphere is only 3.76wt%. The weight loss of the product is less than 4 wt% when the oxidation temperature reaches 1180°C. The prepared B-Si pitch carbonization product possesses good anti-oxidation property at high temperature in air atmosphere.