Molecular contamination mitigation in EUVL by environmental control

Abstract EUVL tools operate under vacuum conditions to avoid absorption losses. Under these conditions, the MoSi multilayer mirrors are contaminated, resulting in reduced reflection and thus throughput. We report on experiments on MoSi mirrors exposed to EUV radiation from a synchrotron. To mimic the effects of EUV radiation we also exposed samples using an electron gun. The oxidation rate was found to be ∼0.016 nm/h per mW/mm 2 of EUV radiation under conditions expected for a high throughput EUVL system. This oxidation can to a large extent be suppressed by using smart gas blend strategies during exposure, e.g. using ethanol. A carbon growth rate of 0.25 nm/h was found for a hydrocarbon pressure of 10 −9 mbar Fomblin. We demonstrate that carbonisation can be suppressed by admitting oxygen during electron gun exposure.

[1]  Paul H. Holloway,et al.  Electron-stimulated oxidation of silicon carbide , 2000 .

[2]  J. Coad,et al.  Electron-beam assisted adsorption on the Si(111) surface , 1970 .

[3]  Hiroo Kato,et al.  Investigation of carbon contamination of synchrotron radiation mirrors , 1986 .

[4]  Hans Meiling,et al.  Prevention of MoSi multilayer reflection loss in EUVL tools , 2001, SPIE Optics + Photonics.

[5]  Derrick C. Mancini,et al.  Deposition of carbon on gold using synchrotron radiation , 1990 .

[6]  Frank Scholze,et al.  Lifetime testing of EUV optics using intense synchrotron radiation at the PTB Radiometry Laboratory , 2001, SPIE Optics + Photonics.

[7]  R. Stuik,et al.  Progress in Mo/Si multilayer coating technology for EUVL optics , 2000, Advanced Lithography.

[8]  Namiki,et al.  Molecular-beam study of sticking of oxygen on Si(100). , 1990, Physical review. B, Condensed matter.

[9]  Michael E. Malinowski,et al.  Use of molecular oxygen to reduce EUV-induced carbon contamination of optics , 2001, SPIE Advanced Lithography.

[10]  Frederik Bijkerk,et al.  Determination of the layered structure in Mo/Si multilayers by grazing incidence X-ray reflectometry , 2000 .

[11]  H. Padmore,et al.  Enhancement of Reflectivity of Multilayer Mirrors for Soft-X-Ray Projection Lithography by Temperature Optimization and Ion-Bombardment , 1994 .

[12]  W. Jark,et al.  Investigation of carbon contamination of mirror surfaces exposed to synchrotron radiation , 1983 .

[13]  D. Schmeißer.  A comparative study of O2, H2 and H2O adsorption on Si(100) , 1984 .

[14]  Thomas Engel,et al.  The interaction of molecular and atomic oxygen with Si(100) and Si(111) , 1993 .

[15]  Ian W. Boyd,et al.  Vacuum-Ultra-Violet and Ozone Induced Oxidation of Silicon and Silicon-Germanium , 1993 .

[16]  W. J. Choyke,et al.  Enhanced silicon oxide film growth on Si (100) using electron impact , 1997 .