Quantitative Prediction of Environmentally Assisted Cracking

Abstract It has long been recognized that the stress corrosion cracking (SCC) and corrosion fatigue cracking susceptibility of various alloy and environment systems is dependent upon complex intera...

[1] R. N. Parkins,et al. ENVIRONMENT SENSITIVE FRACTURE—CONTROLLING PARAMETERS , 1980 .

[2] P. Andresen,et al. Characterization of the roles of electrochemistry, convection and crack chemistry in stress corrosion cracking , 1995 .

[3] K. Sieradzki,et al. Stress-corrosion cracking , 1987 .

[4] A. W. Thompson,et al. Effect of hydrogen on behavior of materials , 1976 .

[5] J. H. Westbrook,et al. The Science of hardness testing and its research applications : based on papers presented at a symposium of the American Society for Metals, October 18 to 20, 1971 , 1973 .

[6] F. Ford,et al. Corrosion Fatigue of Pressure Boundary Materials , 2013 .

[7] G. P. Wozadlo,et al. Irradiation-assisted stress corrosion cracking as a factor in nuclear power plant aging , 1988 .

[8] R. Ritchie,et al. Propagation of short fatigue cracks , 1984 .