Organo-Chlorinated Thin Films Deposited by Atmospheric Pressure Plasma-Enhanced Chemical Vapor Deposition for Adhesion Enhancement between Rubber and Zinc-Plated Steel Monofilaments.

A continuous-flow plasma process working at atmospheric pressure is developed to enhance the adhesion between a rubber compound and a zinc-plated steel monofilament, with the long-term objective to find a potential alternative to the electrolytic brass plating process, which is currently used in tire industry. For this purpose, a highly efficient tubular dielectric barrier discharge reactor is built to allow the continuous treatment of "endless" cylindrical substrates. The best treatment conditions found regarding adhesion are Ar/O2 plasma pretreatment, followed by the deposition from dichloromethane of a 75 nm-thick organo-chlorinated plasma polymerized thin film. Ar/O2 pretreatment allows the removal of organic residues, coming from drawing lubricants, and induces external growth of zinc oxide. The plasma layer has to be preferably deposited at low power to conserve sufficient hydrocarbon moieties. Surface analyses reveal the complex chemical mechanism behind the establishment of strong adhesion levels, more than five times higher after the plasma treatment. During the vulcanization step, superficial ZnO reacts with the chlorinated species of the thin film and is converted into porous and granular bump-shaped ZnwOxHyClz nanostructures. Together, rubber additives diffuse through the plasma layer and lead to the formation of zinc sulfide on the substrate surface. Hence, two distinct interfaces, rubber/thin film and thin film/substrate, are established. On the basis of these observations, hypotheses explaining the high bonding strength results are formulated.

[1]  W. Fulton.  Steel Tire Cord-Rubber Adhesion, Including the Contribution of Cobalt , 2005 .

[2]  Thierry Belmonte,et al.  Continuous Deposition of Organo-Chlorinated Thin Films by Atmospheric Pressure Dielectric Barrier Discharge in a Wire-Cylinder Configuration , 2014 .

[3]  W. V. Ooij.  Fundamental Aspects of Rubber Adhesion to Brass-Plated Steel Tire Cords , 1979 .

[4]  Hidekazu Tanaka,et al.  Influence of thermal treatment on the structure and adsorption properties of layered zinc hydroxychloride , 2010 .

[5]  D. K. Kim,et al.  Adhesion of Natural Rubber to Steel Substrates: The Use of Plasma Polymerized Primers , 1999 .

[6]  F. J. Boerio,et al.  Infrared Spectroscopy of Interphases Between Model Rubber Compounds and Plasma Polymerized Acetylene Films , 1995 .

[7]  W. V. Ooij,et al.  Study of Zn-Ni and Zn-Co alloy coatings electrodeposited on steel strips I: Alloy electrodeposition and adhesion of coatings to natural rubber compounds , 1992 .

[8]  R. D'agostino,et al.  Plasma-polymerized thiophene films for enhanced rubber–steel bonding , 2006 .

[9]  W. V. Ooij,et al.  Study of Zn-Ni and Zn-Co alloy coatings electrodeposited on steel strips II: Corrosion, dezincification and sulfidation of the alloy coatings , 1992 .

[10]  V. G. Beshenkov,et al.  AES and factor analysis study of cord‐oxidized brass layers and rubber‐to‐brass interface chemical composition , 1991 .

[11]  A. Bhowmick,et al.  SEM/EDX studies of the influence of a cobalt adhesion promoter on the interface between rubber skim compounds and tire steel cord , 1996 .

[12]  F. J. Boerio,et al.  Molecular structure of interfaces between plasma‐polymerized acetylene films and steel substrates , 1998 .

[13]  F. J. Boerio,et al.  Adhesion of Natural Rubber Compounds to Plasma-Polymerized Acetylene Films , 1997 .

[14]  P. Boden,et al.  Use of Zinc Alloy Coatings on Steel Cord Reinforcement in Vehicle Tyres , 1999 .

[15]  G. Seo,et al.  Effect of Tetrachlorobenzoquinone on the Adhesion between Rubber Compound and Brass-plated Steel Cord , 1999 .

[16]  K. Hendrikse,et al.  Vulcanization of chlorobutyl rubber. II. A revised cationic mechanism of ZnO/ZnCl2 initiated crosslinking , 2000 .

[17]  Graham C. Smith,et al.  Interfacial microanalysis of rubber–tyre-cord adhesion and the influence of cobalt , 2004 .

[18]  E. A. Secco,et al.  Studies on metal hydroxy compounds. I. Thermal analyses of zinc derivatives ϵ-Zn(OH)2, Zn5(OH)8Cl2.H2O, β-ZnOHCl, and ZnOHF , 1967 .

[19]  T. Belmonte,et al.  Comparison of surface cleaning by two atmospheric pressure discharges , 2003 .

[20]  W. V. Ooij,et al.  Adhesion and corrosion properties of a new NiZn/ZnCo-coated steel tire cord , 1992 .

[21]  W. V. Ooij.  Mechanism and Theories of Rubber Adhesion to Steel Tire Cords—An Overview , 1984 .

[22]  G. E. Hammer.  A new look at the steel cord–rubber adhesive interphase by chemical depth profiling , 2001 .

[23]  A. Bhowmick,et al.  Effect of Anion in Cobalt Promoters on the Adhesion between Steel Cord and Rubber Compound , 1994 .

[24]  V. Puech,et al.  Oil removal from iron surfaces by atmospheric-pressure barrier discharges , 1999 .

[25]  P. B. Harakuni,et al.  Adhesion of Steel Tire Cord to Rubber , 2009 .

[26]  G. Seo,et al.  Promotion effect of a chlorotriazine derivative on the adhesion between rubber compounds and a brass-plated steel cord , 2001 .

[27]  J. Beecher.  X‐ray photoelectron spectroscopic studies of the bonding of phenyl sulfides to copper , 1991 .

[28]  W. J. Ooij,et al.  Surface characterization of novel plasma‐polymerized primers for rubber‐to‐metal bonding , 1995 .

[29]  R. Rojas,et al.  On the thermal decomposition of the zinc(II) hydroxide chlorides Zn5(OH)8Cl2·H2O and Β-Zn(OH)Cl , 1994 .

[30]  W. Dekeyser,et al.  Characterization of the Steel Tire Cord - Rubber Interface , 2009 .

[31]  K. Mori,et al.  Characterization of Adhesion Interlayer Between Rubber and Brass by a Novel Method of Sample Preparation , 2007 .

[32]  T. Yoon,et al.  Enhanced adhesion of steel filaments to rubber via plasma etching and plasma-polymerized coatings , 2001 .

[33]  P. D. Volder,et al.  A new powerful transformation for maximum likelihood common factor analysis (MLCFA) , 1995 .