Nanoengineered InAs quantum dot active medium for laser diodes

Nanoengineering approach was used to develop an efficient active medium based on self-assembled InAs/GaAs quantum dots (QDs) for laser diodes operating at elevated temperatures. Photoluminescence (PL), transmission electron microscopy, and electroluminescence were used to study the influence of an overgrowth procedure on the properties of multiple-layer QDs. Optical properties of QDs were optimized by the adjustment of a GaAs overlayer thickness prior to a heating step, responsible for the truncation of the pyramid-shaped QDs. Triple-layer QD edge-emitting lasers with 1220 nm emitting wavelength exhibited a maximum saturated modal gain of 16 cm-1. To use truncated QD active medium for vertical cavity surface emitting lasers, seven layers of QDs with 20 nm of short period superlattice barriers between layers was developed. A wavelength of 1190 nm edge-emitting lasers with 120 nm total thickness 7xQDs active medium showed almost two times higher maximum saturated gain, 31 cm-1. Unfortunately, these lasers with closer distance between QD layers in active medium demonstrated stronger temperature dependence (with To = 110 K) of threshold current density and lasing wavelength. A record high characteristic temperature for lasing threshold, To = 380 K up to 55 C, was measured for edge-emitting laser diodes, which contained triple-layer truncated QD active medium. We believe that AlAs capping in combination with truncation procedure result in significant suppression of carrier transport between QDs within the layer as well as between QD layers.

[1]  A. Larsson,et al.  Large ground-to-first-excited-state transition energy separation for InAs quantum dots emitting at 1.3 μm , 2002 .

[2]  H. Sakaki,et al.  Multidimensional quantum well laser and temperature dependence of its threshold current , 1982 .

[3]  D. Ritchie,et al.  Modification of InAs quantum dot structure by the growth of the capping layer , 1998 .

[4]  Z. R. Wasilewski,et al.  Size and shape engineering of vertically stacked self-assembled quantum dots , 1999 .

[5]  Andreas Stintz,et al.  Transition dipole moment of InAs/InGaAs quantum dots from experiments on ultralow-threshold laser diodes , 2000 .

[6]  Hiroshi Ishikawa,et al.  Effect of homogeneous broadening of optical gain on lasing spectra in self-assembled In x Ga 1-x As/GaAs quantum dot lasers , 2000 .

[7]  J. Merz,et al.  Volmer–Weber and Stranski–Krastanov InAs-(Al,Ga)As quantum dots emitting at 1.3 μm , 2000 .

[8]  G. Park,et al.  Temperature dependence of lasing characteristics for long-wavelength (1.3-μm) GaAs-based quantum-dot lasers , 1999, IEEE Photonics Technology Letters.

[9]  Nikolai N. Ledentsov,et al.  Maximum modal gain of a self-assembled InAs/GaAs quantum-dot laser , 2001 .

[10]  Bowei Xu,et al.  Self-assembled InAs/GaAs quantum dots and quantum dot laser , 2000 .

[11]  Anupam Madhukar,et al.  InAs island‐induced‐strain driven adatom migration during GaAs overlayer growth , 1994 .

[12]  Craig E. Pryor,et al.  Geometry and material parameter dependence of InAs/GaAs quantum dot electronic structure , 1999 .

[13]  A. P. Vasil’ev,et al.  Comparative analysis of long-wavelength (1.3 µm) VCSELs on GaAs substrates , 2001 .

[14]  G. Abstreiter,et al.  Influence of a thin AlAs cap layer on optical properties of self-assembled InAs/GaAs quantum dots , 1999 .

[15]  G. Salamo,et al.  Morphology of InAs self-organized islands on AlAs surfaces , 1999 .

[16]  Vadim Tokranov,et al.  Enhanced thermal stability of laser diodes with shape-engineered quantum dot medium , 2003 .

[17]  O. Shchekin,et al.  Discrete energy level separation and the threshold temperature dependence of quantum dot lasers , 2000 .

[18]  Lin-wang Wang,et al.  Comparison of the electronic structure of InAs/GaAs pyramidal quantum dots with different facet orientations , 1998 .