High Potential Excursions during PEM Fuel Cell Operation with Dead-Ended Anode

Operating a proton exchange membrane (PEM) fuel cell with a dead-ended anode may lead to local fuel starvation due to the excessive accumulation of liquid water and possibly nitrogen (because of membrane crossover) in the anode compartment. In this paper, we present experimental results obtained with a segmented, linear cell with reference electrodes along the gas channels, used to record local anode and cathode potentials. By simultaneously monitoring the local potentials and current densities during operation, we assessed the impact of fuel starvation on local fuel cell performance during aging protocols consisting of repeated dead-ended anode operation sequences (with anode outlet closed longer than in real use conditions). During the aging protocols, we observed strong local cathode potential excursions close to the anode outlet. The cathode showed non-uniform ElectroChemical Surface Area (ECSA) losses and performance degradation along the cell area. The damage was more severe in the regions suffering the longest from fuel starvation. Similar experiments performed in different operating conditions and with different membrane thickness showed that water management impacts significantly the cathode potential variations and thus the MEA degradation. Most of the MEA degradation is attributed to local cathode potential excursions above 1.2 V although potential cycling between 0.5 V and 0.7 V also had an impact in the regions well supplied with hydrogen (hydrogen purges were triggered when the fuel cell voltage dropped from about 0.7 V to 0.5 V). According to our results, localized and transient hydrogen starvation events may be difficult to detect by considering only the overall fuel cell performance.

[1]  Göran Sundholm,et al.  In-situ measurements of gas permeability in fuel cell membranes using a cylindrical microelectrode , 2002 .

[2]  In-Hwan Oh,et al.  Effects of Cathode Inlet Relative Humidity on PEMFC Durability during Startup–Shutdown Cycling II. Diagnostic Study , 2010 .

[3]  Gaël Maranzana,et al.  Experimental study of the start-up of a fuel cell stack for backup power application , 2012 .

[4]  Suresh G. Advani,et al.  Experimental investigation of liquid water formation and transport in a transparent single-serpentine PEM fuel cell , 2007 .

[5]  Jason B. Siegel,et al.  Carbon Corrosion in PEM Fuel Cell Dead-Ended Anode Operations , 2011 .

[6]  Bosung Kim,et al.  An experimental study on water transport through the membrane of a PEFC operating in the dead-end mode , 2009 .

[7]  P. Ekdunge,et al.  Oxygen and hydrogen permeation properties and water uptake of Nafion® 117 membrane and recast film for PEM fuel cell , 1997 .

[8]  S. Maaß,et al.  Carbon support oxidation in PEM fuel cell cathodes , 2008 .

[9]  R. Borup,et al.  Influence of the microporous layer on carbon corrosion in the catalyst layer of a polymer electrolyte membrane fuel cell , 2012 .

[10]  J. Jur,et al.  Measuring oxygen, carbon monoxide and hydrogen sulfide diffusion coefficient and solubility in Nafion membranes , 2009, 1108.2438.

[11]  S. D. Fraser,et al.  Polarization study of a PEMFC with four reference electrodes at hydrogen starvation conditions , 2008 .

[12]  Rangachary Mukundan,et al.  Impact of flow rates and electrode specifications on degradations during repeated startups and shutdowns in polymer-electrolyte membrane fuel cells , 2014 .

[13]  Suresh G. Advani,et al.  In situ comparison of water content and dynamics in parallel, single-serpentine, and interdigitated flow fields of polymer electrolyte membrane fuel cells , 2010 .

[14]  Mahlon Wilson,et al.  Scientific aspects of polymer electrolyte fuel cell durability and degradation. , 2007, Chemical reviews.

[15]  H. Takenaka,et al.  Properties of Nafion membranes under PEM water electrolysis conditions , 2011 .

[16]  S. Pitchumani,et al.  Experimental analysis of spatio-temporal behavior of anodic dead-end mode operated polymer electroly , 2011 .

[17]  W. Gu,et al.  Electrochemical Measurement of the Oxygen Permeation Rate through Polymer Electrolyte Membranes , 2013 .

[18]  P. Prenninger,et al.  Electrocatalytic Corrosion of Carbon Support in PEMFC at Fuel Starvation , 2006 .

[19]  A. Wokaun,et al.  The effect of platinum on carbon corrosion behavior in polymer electrolyte fuel cells , 2011 .

[20]  Laetitia Dubau,et al.  Degradation heterogeneities induced by repetitive start/stop events in proton exchange membrane fuel cell: Inlet vs. outlet and channel vs. land , 2013 .

[21]  G. Maranzana,et al.  Internal Currents, CO2 Emissions and Decrease of the Pt Electrochemical Surface Area during Fuel Cell Start-Up and Shut-Down , 2013 .

[22]  L. J. Bregoli,et al.  A Reverse-Current Decay Mechanism for Fuel Cells , 2005 .

[23]  Denise A. McKay,et al.  Measurement of Liquid Water Accumulation in a PEMFC with Dead-Ended Anode , 2008 .

[24]  A. Wokaun,et al.  Local Catalyst Support Degradation during Polymer Electrolyte Fuel Cell Start-Up and Shutdown , 2012 .

[25]  Mike L. Perry,et al.  Systems Strategies to Mitigate Carbon Corrosion in Fuel Cells , 2006 .

[26]  Jérôme Dillet,et al.  Experimental characterization of internal currents during the start-up of a proton exchange membrane , 2011 .

[27]  Agus P. Sasmito,et al.  Effect of operating parameters on the transient performance of a polymer electrolyte membrane fuel cell stack with a dead-end anode , 2014 .

[28]  G. Maranzana,et al.  Time Evolution of Local Potentials During PEM Fuel Cell Operation With Dead-Ended Anode , 2013 .

[29]  C. R. Martin,et al.  Investigations of the O sub 2 reduction reaction at the platinum/Nafion interface using a solid-state electrochemical cell. Technical report , 1991 .

[30]  A. Wokaun,et al.  Quantitative analysis of carbon corrosion during fuel cell start-up and shut-down by anode purging , 2012 .