The Substantiation of the Pre-Polymerization Heating Efficiency of the Dental Nanocomposite Material

Objective:  To evaluate the effect of pre-polymerization heating of nanocomposite filling materials on their strength properties within one manufacture group.  Material and Methods: Two nanocomposite filling materials Enamel Plus HRi Universal Dentin ®  and Universal Enamel ®  were used. The linear thermal expansion coefficient (LTEC), Young's modulus and penetration depth were determined during the tests. Changes in the structure of materials were evaluated using electron scanning microscopy .  Results: Dentin nanocomposite samples after pre-heating and polymerization have higher LTEC after 30°C compared to dentine nanocomposite untreated samples with statistically significance started at 62 °C  (p<0.05) and higher temperature. Pre-polymerization heated samples had a statistically higher LTEC (p<0.05) at 57 ° С . It was revealed that Young's modulus of the dentin nanocomposite samples after thermal processing at 55°C was higher in total after the first heating cycle by 15% compared to the untreated dentin nanocomposite samples (p<0.05). The volume of total porosity after pre-heating decreased to 5-7% (p<0.05) .  Conclusion:  The material that has undergone preliminary heat processing is significantly less deformed under load than the material that does not have thermal processing during the research was established and also has a denser structure.

[1]  Composite layered overlay: micro-invasive approach , 2019, Эндодонтия Today.

[2]  Direct anterior composite restoration – a predictable outcome: сase report , 2019, Эндодонтия Today.

[3]  S. Kunsági-Máté,et al.  Effect of exposure time and pre-heating on the conversion degree of conventional, bulk-fill, fiber reinforced and polyacid-modified resin composites. , 2019, Dental materials : official publication of the Academy of Dental Materials.

[4]  M. Tahriri,et al.  Rheological properties of contemporary nanohybrid dental resin composites: The influence of preheating , 2018, Polymer Testing.

[5]  L. Angeles,et al.  ELECTRONMICROSCOPY INSPIRED SETUP FOR SINGLE-SHOT 4-D TRACE SPACE RECONSTRUCTION OF BRIGHT ELECTRON BEAMS , 2018 .

[6]  R. Hickel,et al.  Academy of Dental Materials guidance-Resin composites: Part II-Technique sensitivity (handling, polymerization, dimensional changes). , 2017, Dental materials : official publication of the Academy of Dental Materials.

[7]  R. Hickel,et al.  Academy of Dental Materials guidance-Resin composites: Part I-Mechanical properties. , 2017, Dental materials : official publication of the Academy of Dental Materials.

[8]  C. Soares,et al.  An Evaluation of the Light Output from 22 Contemporary Light Curing Units. , 2017, Brazilian dental journal.

[9]  W. Palin,et al.  Filler characteristics of modern dental resin composites and their influence on physico-mechanical properties. , 2016, Dental materials : official publication of the Academy of Dental Materials.

[10]  D. Watts,et al.  Stiffness of uncured resin-composites assessed via cavity-packing forces. , 2016, Dental materials : official publication of the Academy of Dental Materials.

[11]  E. Kuyucu,et al.  Effects of Novel Finishing and Polishing Systems on Surface Roughness and Morphology of Nanocomposites. , 2016, Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.].

[12]  D. Edelhoff,et al.  Flexural Strength of Preheated Resin Composites and Bonding Properties to Glass-Ceramic and Dentin , 2016, Materials.

[13]  C. Kumari,et al.  Evaluation of surface roughness of different restorative composites after polishing using atomic force microscopy , 2016, Journal of conservative dentistry : JCD.

[14]  Shi-lang Xu,et al.  Influence of nanoparticles on fluidity and mechanical properties of cement mortar , 2015 .

[15]  C. Estrela,et al.  Pre-heating mitigates composite degradation , 2015, Journal of applied oral science : revista FOB.

[16]  T. Attin,et al.  Pre-heating of high-viscosity bulk-fill resin composites: effects on shrinkage force and monomer conversion. , 2015, Journal of dentistry.

[17]  C. Papadopoulos,et al.  Effect of temperature, curing time, and filler composition on surface microhardness of composite resins , 2015, Journal of conservative dentistry : JCD.

[18]  F. Rueggeberg,et al.  Effect of temperature on composite polymerization stress and degree of conversion. , 2014, Dental materials : official publication of the Academy of Dental Materials.

[19]  Payal Saxena,et al.  Release and toxicity of dental resin composite , 2012, Toxicology international.

[20]  D. Watts,et al.  A method for assessing force/work parameters for stickiness of unset resin-composites. , 2011, Dental materials : official publication of the Academy of Dental Materials.

[21]  S. Deb,et al.  Pre-warming of dental composites. , 2011, Dental materials : official publication of the Academy of Dental Materials.

[22]  U. Lohbauer,et al.  The effect of resin composite pre-heating on monomer conversion and polymerization shrinkage. , 2009, Dental materials : official publication of the Academy of Dental Materials.

[23]  M. Aksu,et al.  Effect of pre-heating resin composite on restoration microleakage. , 2008, Operative dentistry.

[24]  F. Rueggeberg,et al.  Effect of temperature on unpolymerized composite resin film thickness. , 2006, The Journal of prosthetic dentistry.

[25]  R. Giudici,et al.  Polymerization Kinetics of Pre-heated Composite , 2006, Journal of dental research.

[26]  F. Rueggeberg,et al.  Monomer Conversion of Pre-heated Composite , 2005, Journal of dental research.

[27]  Jeffrey W Stansbury,et al.  Use of near-IR to monitor the influence of external heating on dental composite photopolymerization. , 2004, Dental materials : official publication of the Academy of Dental Materials.

[28]  C. Bowman,et al.  Understanding the kinetics and network formation of dimethacrylate dental resins , 2001 .

[29]  J. McCabe,et al.  Influence of dietary simulating solvents on the viscoelasticity of temporary soft lining materials. , 2000, The Journal of prosthetic dentistry.

[30]  C. Bowman,et al.  The Effects of Light Intensity, Temperature, and Comonomer Composition on the Polymerization Behavior of Dimethacrylate Dental Resins , 1999, Journal of dental research.