Effect of interface roughness on gate bias instability of polycrystalline silicon thin-film transistors

The effect of the SiO2/polycrystalline silicon (polysilicon) interface roughness on the stability of n-channel large grain polysilicon thin-film transistors (TFTs) is investigated. The positive gate voltage of 20 V is used in the bias stress experiments, with the source and drain grounded. It is shown that the current through the gate oxide and the stability of the TFT are directly related to the importance of the interface roughness. The evolution of the TFT parameters with stress duration indicates that the turn-on voltage Von and the subthreshold swing voltage S are degraded due to the generation of dangling bond midgap states, while the leakage current IL and the maximum transconductance Gm are degraded due to the generation of strain-bond tail states. Moreover, the parameters Von and IL are found to degrade faster than the parameters S and Gm, respectively, due to electron trapping in the gate oxide.