Plastic shrinkage cracking in cementitious repairs and overlays

A study was undertaken to investigate the influence of mixture proportions on plastic shrinkage cracking in cementitious repairs and overlays. The following variables were studied: water-cement ratio (w/c), sand-cement ratio (s/c) aggregate-cement ratio (a/c), fly-ash content, and the presence of a shrinkage reducing admixture (SRA). A recently developed bonded overlay method was used. In this method, the cementitious material to be investigated is cast on a substrate base with protuberances and the entire assembly is subjected to drying in an environmental chamber. With a high degree of restraint, cracking develops in the overlay over time which is then characterized with the help of magnification device and image analysis software. Results indicate that a lower water-cement ratio significantly reduces crack widths and crack areas and also reduces the ‘time to first crack’. The exact influence of s/c on cracking could not be established. The study further demonstrated that increasing the a/c provided internal restraint and significantly reduced early-age cracking. The addition of Class C fly-ash increased the amount of cracking but also increased the ‘time to first crack.’ This was however true only to a certain threshold value of fly-ash content beyond which fly-ash can be effective in reducing early age shrinkage cracking. Finally, the addition of a shrinkage reducing admixture was effective in reducing cracking but the cracks occurred sooner.

[1]  Alaettin Kılıç,et al.  Strength and shrinkage properties of mortar containing a nonstandard high-calcium fly ash , 2004 .

[2]  Nemkumar Banthia,et al.  Influence of Polypropylene Fiber Geometry on Plastic Shrinkage Cracking in Concrete , 2006 .

[3]  Kolluru V. L. Subramaniam,et al.  Influence of Ultrafine Fly Ash on the Early Age Response and the Shrinkage Cracking Potential of Concrete , 2005 .

[4]  Surendra P. Shah,et al.  Shrinkage cracking of fiber reinforced concrete , 1990 .

[5]  R. Gettu,et al.  Long-term behaviour of concrete incorporating a shrinkage-reducing admixture , 2002 .

[6]  Paul J. Uno,et al.  PLASTIC SHRINKAGE CRACKING AND EVAPORATION FORMULAS , 1998 .

[7]  Sirivivatnanon,et al.  DEVELOPMENT OF HIGH VOLUME FLY ASH CONCRETE FOR PAVEMENTS , 1992 .

[8]  D. Bentz,et al.  Shrinkage-reducing admixtures and early-age desiccation in cement pastes and mortars , 2001 .

[9]  İlker Bekir Topçu,et al.  Influence of concrete properties on bleeding and evaporation , 2003 .

[10]  Zailiang Li,et al.  Crack Width of High-Performance Concrete Due to Restrained Shrinkage , 1999 .

[11]  Arnon Bentur,et al.  Free and Restrained Shrinkage of Normal andHigh-Strength Concretes , 1995 .

[12]  C. Atiş.  High-Volume Fly Ash Concrete with High Strength and Low Drying Shrinkage , 2003 .

[13]  J. Olek,et al.  Characterization of plastic shrinkage cracking in fiber reinforced concrete using image analysis and a modified Weibull function , 2003 .

[14]  Mohammed Maslehuddin,et al.  Effect of mix proportions on plastic shrinkage cracking of concrete in hot environments , 1998 .

[15]  Kihak Lee,et al.  Autogenous shrinkage of high-performance concrete containing fly ash , 2003 .

[16]  N. Banthia,et al.  Shrinkage Cracking in Polyolefin Fiber-Reinforced Concrete , 2000 .

[17]  John H. Tews,et al.  Pavement construction with high-volume Class C and Class F fly ash concrete , 1993 .

[18]  Kenneth C. Hover,et al.  INFLUENCE OF MIX PROPORTIONS AND CONSTRUCTION OPERATIONS ON PLASTIC SHRINKAGE CRACKING IN THIN SLABS , 1988 .

[19]  Michel Pigeon,et al.  Restrained shrinkage cracking in fibre-reinforced cementitious composites , 1993 .

[20]  Turan Özturan,et al.  Effects of cold-bonded fly ash aggregate properties on the shrinkage cracking of lightweight concretes , 2006 .