Effects of Voids on the Mechanical Strength and Ultrasonic Attenuation of Laminated Composites

The effects of voids on the mechanical strength and ultrasonic attenuation have been investigated on a number of laminated composite systems containing a wide range of void content. Graphite fiber reinforced specimens were fabricated both from unidirectional tape and woven fabric prepreg and their interlaminar shear strength and frequency dependent ultrasonic attenuation were measured together with a careful study of microstructure. The measured strength and attenuation slope were found to depend not only on the void content but on the void geometry associated with the prepreg structure of composites. A shear fracture criterion similar to the Mar-Lin equation for notched tensile fracture stresses was used successfully to correlate the fracture strength of porous laminates. The unidirectional laminates showed much higher void sensitivity than the fabric laminates, i.e., more reduction in shear strength and higher attenuation slope for a given void content. It was shown that the void content may be estimated from the measured attenuation slope and that a good correlation exists between the attenuation slope and the shear strength of porous composite laminates.

[1]  K. L. Jerina,et al.  Evaluation of porosity in composite aircraft structures , 1993 .

[2]  Kenneth J. Bowles,et al.  Void Effects on the Interlaminar Shear Strength of Unidirectional Graphite-Fiber-Reinforced Composites , 1992 .

[3]  S. R. Ghiorse,et al.  Effect of void content on the mechanical properties of carbon/epoxy laminates , 1993 .

[4]  D.E.W. Stone,et al.  Ultrasonic attenuation as a measure of void content in carbon-fibre reinforced plastics , 1975 .

[5]  N. Hancox.  The effects of flaws and voids on the shear properties of CFRP , 1977 .

[6]  Vinay Dayal,et al.  Leaky Lamb waves in an anisotropic plate. II: Nondestructive evaluation of matrix cracks in fiber-reinforced composites , 1991 .

[7]  D. Hsu.  Ultrasonic Measurements of Porosity in Woven Graphite Polyimide Composites , 1988 .

[8]  Kuen Y. Lin,et al.  Fracture mechanics correlation for tensile failure of filamentary composites with holes , 1977 .

[9]  H. S. Schwartz,et al.  Fundamental Aspects of Fiber Reinforced Plastic Composites. , 1968 .

[10]  Zafer Gürdal,et al.  Effects of processing induced defects on laminate response - Interlaminar tensile strength , 1991 .

[11]  David K. Hsu,et al.  Mechanical Strength Degradation of Graphite Fiber Reinforced Thermoset Composites Due to Porosity , 1988 .

[12]  George S. Springer,et al.  Effects of Cure Pressure on Resin Flow, Voids, and Mechanical Properties , 1987 .

[13]  Analytical Treatment of Polar Backscattering from Porous Composites , 1987 .

[14]  David K. Hsu,et al.  Porosity estimation using the frequency dependence of the ultrasonic attenuation , 1989 .

[15]  David K. Hsu,et al.  Experimental analysis of porosity-induced ultrasonic attenuation and velocity change in carbon composites , 1995 .

[16]  David K. Hsu,et al.  Evaluation of Porosity in Graphite-Epoxy Composite by Frequency Dependence of Ultrasonic Attenuation , 1987 .

[17]  R. Prakash,et al.  Non-destructive testing of composites , 1980 .

[18]  H. Yoshida,et al.  Statistical approach to the relationship between ILSS and void content of CFRP , 1986 .

[19]  R. Anderson,et al.  NONDESTRUCTIVE TESTING OF ADVANCED COMPOSITES. , 1972 .

[20]  Paul A. Lagace,et al.  Notch Sensitivity and Stacking Sequence of Laminated Composites , 1986 .

[21]  Eugene Ryshkewitch,et al.  Compression Strength of Porous Sintered Alumina and Zirconia , 1953 .

[22]  Sérgio Frascino Müller de Almeida,et al.  Effect of void content on the strength of composite laminates , 1994 .

[23]  W. Duckworth.  Discussion of Ryshkewitch Paper , 1953 .

[24]  A. R. Zak,et al.  Crack point stress singularities at a bi-material interface , 1963 .

[25]  R. C. Mcmaster.  Nondestructive testing handbook , 1959 .

[26]  G. Caprino.  On the prediction of residual strength for notched laminates , 1983 .

[27]  David K. Hsu,et al.  A Morphological Study of Porosity Defects in Graphite-Epoxy Composites , 1987 .