Experimental study on stable growth of crack and craze damage in HIPS under tension at room temperature

This study focuses on investigating the stable damage and crack growth process of high impact polystyrene (HIPS) by using the damage mechanics approach and the moire method. Under excessive tensile loading, HIPS will be damaged due to multiple crazing that causes volume dilatation. A damage variable is defined by the dilatation of the representative volume element to characterize the craze-damage. The relationship between the dilatation and the total strain has been determined experimentally. A specimen with a sharp initial discontinuity is tested under tensile force to study the damage and crack growth process. It is observed that an elliptical damage zone is formed in front of the crack tip. The crack propagation is stabilized by the damage zone. Moire fringe patterns show that the deformation within the damage zone is non-uniform. A dynamic configuration of deformation, which comprises the elastic zone, the transition zone, the damage processing zone, and the residual damage zone, has been established. The non-linear strain and stress fields inside the transition zone and the damage processing zone are analyzed. The experimental result also shows that a critical plastic strain criterion may be used to predict the stable growth of macrocracks for HIPS.

[1]  A. Ruina,et al.  Micromechanics of crack growth into a craze in a polymer glass , 1992 .

[2]  A. J. Durelli,et al.  Moiré analysis of strain , 1970 .

[3]  R. Farris,et al.  A predictive model for the mechanical behavior of particulate composites. Part II: Comparison of model predictions to literature data , 1993 .

[4]  E. Kramer,et al.  Molecular weight dependence of the fracture toughness of glassy polymers arising from crack propagation through a craze , 1995 .

[5]  A. Ruina,et al.  Continuum and Discrete Modeling of Craze Failure at a Crack Tip in a Glassy Polymer , 1995 .

[6]  B. Fisa,et al.  A model for filler—matrix debonding in glass‐bead‐filled viscoelastic polymers , 1997 .

[7]  B. Fisa,et al.  Stress‐strain behavior and tensile dilatometry of glass bead‐filled polypropylene and polyamide 6 , 1997 .

[8]  P. Ifju,et al.  High Sensitivity Moiré: Experimental Analysis for Mechanics and Materials , 1995 .

[9]  C. Tang,et al.  Damage mechanics applied to polymers , 1994 .

[10]  P. Hornsby,et al.  Fracture toughness of multiphase polypropylene composites containing rubbery and particulate inclusions , 1997 .

[11]  G. Newaz,et al.  Interrelationship of Damage and Strain in Particulate Composites , 1989 .

[12]  D. S. Dugdale.  Yielding of steel sheets containing slits , 1960 .

[13]  R. Farris,et al.  A predictive model for the mechanical behavior of particulate composites. Part I: Model derivation , 1993 .

[14]  Jean Lemaitre,et al.  A Course on Damage Mechanics , 1992 .

[15]  C. Bucknall,et al.  Rubber-toughening of plastics , 1972 .

[16]  Y. P. Li,et al.  Damage evolution and energy dissipation of polymers with crazes , 1998 .

[17]  A. Argon,et al.  Measurements of craze velocities in polystyrene-polybutadiene blends , 1993 .

[18]  H. Brown.  A molecular interpretation of the toughness of glassy polymers , 1991 .

[19]  C. Tang,et al.  Modelling of non-linear stress–strain behaviour of HIPS with craze damage in tensile loading–unloading process , 2000 .