Influence of high-intensity ultrasonic treatment on the phase morphology of a Mg-9.0wt.%Al binary alloy

The effect of ultrasonic treatment on the β-phase (Mg17Al12) morphology of an Mg-9.0wt.%Al alloy was studied. The result shows that with high-intensity ultrasonic vibration employed during the solidifying of Mg-9.0wt.%Al, the β-phase in the entire cross section of the billet is significantly refined and also changed from continuous to discontinuous morphology. Spherical β-phase is formed during the solidification of the billet treated with high-intensity ultrasonic vibration.

[1] G. Éskin. Broad prospects for commercial application of the ultrasonic (cavitation) melt treatment of light alloys. , 2001, Ultrasonics sonochemistry.

[2] K. Nogita,et al. Columnar to equiaxed transition of eutectic in hypoeutectic aluminium-silicon alloys , 2002 .

[3] Daniel J. Sakkinen. Physical Metallurgy of Magnesium Die Cast Alloys , 1994 .

[4] Qudong Wang,et al. Fracture behavior of AZ91 magnesium alloy , 2000 .

[5] L. Hogan,et al. The modification of aluminium-silicon alloys with strontium , 1975 .

[6] A. F. Ismail,et al. Effect of superheating temperatures on microstructure and properties of strontium modified aluminium–silicon eutectic alloy , 2005 .

[7] A. K. Dahle,et al. Effects of boron on eutectic modification of hypoeutectic Al-Si alloys , 2003 .

[8] G. Éskin,et al. Effect of Cavitation Melt Treatment on the Structure Refinement and Property Improvement in Cast and Deformed Hypereutectic Al-Si Alloys , 1997 .

[9] O. Abramov. Action of high intensity ultrasound on solidifying metal , 1987 .

[10] T. Srivatsan,et al. The tensile behaviour of rapidly solidified magnesium alloys , 1995, Journal of Materials Science.

[11] Non-linear effects of acoustic generation in solids , 1990 .