Mechanical properties of transparent funcional thin films for flexible displays

The present work investigates the mechanical integrity of multilayer films developed for flexible displays. The layers comprise tin-doped indium oxide (ITO) conductive coatings and alumina barrier coatings sputtered onto high temperature aromatic polyesters. The onset strain for tensile failure and related cohesive strength of the coatings, and their adhesion to the polymer substrate, are analyzed by means of bending tests and fragmentation tests. The former test enables accurate electrical resistivity measurements during bending of film specimens, and correlates the failure of the ITO coating to the abrupt increase of resistivity. In the fragmentation test, the progressive failure of the thin coating is examined in situ in an optical microscope as a function of tensile strain, with simultaneous measurement of the electrical resistance, for the ITO coatings. The results and their analysis enable to determine the influence of internal stresses and layer thickness on the failure mechanisms of the multilayer composite films, despite the occurrence of coupled failure processes between adjacent layers.

[1]  Leonid S. Srubshchik,et al.  Strength measurement of optical fibers by bending , 1999, Other Conferences.

[2]  Y. Leterrier.  Durability of nanosized oxygen-barrier coatings on polymers , 2003 .

[3]  John A. Nairn,et al.  Fracture mechanics analysis of coating/substrate systems Part I: Analysis of tensile and bending experiments , 2000 .

[4]  K. Röll,et al.  Analysis of stress and strain distribution in thin films and substrates , 1976 .

[5]  G. Crawford,et al.  Strain-dependent electrical resistance of tin-doped indium oxide on polymer substrates , 2000 .

[6]  Stephen R. Forrest,et al.  The dawn of organic electronics , 2000 .

[7]  Y. Leterrier,et al.  Internal stresses and adhesion of thin silicon oxide coatings on poly(ethylene terephthalate) , 2001 .

[8]  A. Evans,et al.  The cracking and decohesion of thin films on ductile substrates , 1989 .

[9]  J. Månson,et al.  Adhesion of silicon oxide layers on poly(ethylene terephthalate). I: effect of substrate properties on coating's fragmentation process , 1997 .

[10]  Wei Wang,et al.  The fracture of brittle thin films on compliant substrates in flexible displays , 2002 .

[11]  F. O. Adurodija,et al.  Electrical and structural properties of indium tin oxide films prepared by pulsed laser deposition , 2002 .

[12]  E. Fortunato,et al.  Influence of the Strain on the Electrical Resistance of Zinc Oxide Doped Thin Film Deposited on Polymer Substrates , 2002 .

[13]  N. Hashimoto,et al.  Effect of internal stress on adhesion and other mechanical properties of evaporated indium tin oxide (ITO) films , 1994 .