An injection molding process for manufacturing highly porous and interconnected biodegradable polymer matrices for use as tissue engineering scaffolds.

In this research, injection molding was combined with a novel material combination, supercritical fluid processing, and particulate leaching techniques to produce highly porous and interconnected structures that have the potential to act as scaffolds for tissue engineering applications. The foamed structures, molded with polylactide (PLA) and polyvinyl alcohol (PVOH) with salt as the particulate, were processed without the aid of organic solvents, which can be detrimental to tissue growth. The pore size in the scaffolds is controlled by salt particulates and interconnectivity is achieved by the co-continuous blending morphology of biodegradable PLA matrix with water-soluble PVOH. Carbon dioxide (CO(2)) at the supercritical state is used to serve as a plasticizer, thereby imparting moldability of blends even with an ultra high salt particulate content, and allows the use of low processing temperatures, which are desirable for temperature-sensitive biodegradable polymers. Interconnected pores of approximately 200 microm in diameter and porosities of approximately 75% are reported and discussed.

[1]  T. Aminabhavi,et al.  Molecular modeling simulations and thermodynamic approaches to investigate compatibility/incompatibility of poly(l-lactide) and poly(vinyl alcohol) blends , 2006 .

[2]  P. Ma,et al.  Polymeric Scaffolds for Bone Tissue Engineering , 2004, Annals of Biomedical Engineering.

[3]  J C Middleton,et al.  Synthetic biodegradable polymers as orthopedic devices. , 2000, Biomaterials.

[4]  R. Reis,et al.  The morphology, mechanical properties and ageing behavior of porous injection molded starch-based blends for tissue engineering scaffolding , 2005 .

[5]  U. Sundararaj.  Phase Morphology Development in Polymer Blends: Processing and Experimental Aspects , 2005 .

[6]  A. Mikos,et al.  Effect of osteoblastic culture conditions on the structure of poly(DL-lactic-co-glycolic acid) foam scaffolds. , 1999, Tissue engineering.

[7]  D J Mooney,et al.  Open pore biodegradable matrices formed with gas foaming. , 1998, Journal of biomedical materials research.

[8]  Linbo Wu,et al.  A "room-temperature" injection molding/particulate leaching approach for fabrication of biodegradable three-dimensional porous scaffolds. , 2006, Biomaterials.

[9]  T. Park,et al.  A novel fabrication method of macroporous biodegradable polymer scaffolds using gas foaming salt as a porogen additive. , 2000, Journal of biomedical materials research.

[10]  J. R. Royer,et al.  High-pressure rheology of polystyrene melts plasticized with CO2: Experimental measurement and predictive scaling relationships , 2000 .

[11]  Dietmar W Hutmacher,et al.  Evaluation of a hybrid scaffold/cell construct in repair of high-load-bearing osteochondral defects in rabbits. , 2006, Biomaterials.

[12]  C. Patrick,et al.  Manufacture of porous biodegradable polymer conduits by an extrusion process for guided tissue regeneration. , 1998, Biomaterials.

[13]  E Wintermantel,et al.  A novel processing method for injection-molded polyether-urethane scaffolds. Part 1: processing. , 2006, Journal of biomedical materials research. Part B, Applied biomaterials.

[14]  Antonios G. Mikos,et al.  Formation of highly porous biodegradable scaffolds for tissue engineering , 2000 .

[15]  David Hui,et al.  A critical review on polymer-based bio-engineered materials for scaffold development , 2007 .

[16]  Scott C. Brown,et al.  A three-dimensional osteochondral composite scaffold for articular cartilage repair. , 2002, Biomaterials.

[17]  R L Reis,et al.  A new approach based on injection moulding to produce biodegradable starch-based polymeric scaffolds: morphology, mechanical and degradation behaviour. , 2001, Biomaterials.

[18]  J M Brady,et al.  Degradation rates of oral resorbable implants (polylactates and polyglycolates): rate modification with changes in PLA/PGA copolymer ratios. , 1977, Journal of biomedical materials research.

[19]  J. Vacanti,et al.  Tissue engineering : Frontiers in biotechnology , 1993 .

[20]  J. Yoon,et al.  Degradation behaviors of biodegradable macroporous scaffolds prepared by gas foaming of effervescent salts. , 2001, Journal of biomedical materials research.

[21]  S. M. Graham.  Application of the Normalization Method to Dynamic Fracture Toughness Testing of Alloy 718 , 2006 .

[22]  G. Stevens,et al.  Production and surface modification of polylactide-based polymeric scaffolds for soft-tissue engineering. , 2004, Methods in molecular biology.

[23]  W. Mark Saltzman,et al.  CHAPTER 19 – CELL INTERACTIONS WITH POLYMERS , 2000 .

[24]  David J Mooney,et al.  Role of poly(lactide-co-glycolide) particle size on gas-foamed scaffolds , 2004, Journal of biomaterials science. Polymer edition.

[25]  Newell R Washburn,et al.  Co-extrusion of biocompatible polymers for scaffolds with co-continuous morphology. , 2002, Journal of biomedical materials research.

[26]  Dietmar W. Hutmacher,et al.  Biodegradable polymers applied in tissue engineering research: a review , 2007 .

[27]  D. Hutmacher,et al.  Scaffolds in tissue engineering bone and cartilage. , 2000, Biomaterials.

[28]  Robert Langer,et al.  Preparation and characterization of poly(l-lactic acid) foams , 1994 .

[29]  Antonios G. Mikos,et al.  CHAPTER 21 – POLYMER SCAFFOLD PROCESSING , 2000 .

[30]  K E Healy,et al.  Engineering bone regeneration with bioabsorbable scaffolds with novel microarchitecture. , 1999, Tissue engineering.

[31]  P. Moldenaers,et al.  Anisotropy and instability of the co-continuous phase morphology in uncompatibilized and reactively compatibilized polypropylene/polystyrene blends , 2007 .

[32]  R Langer,et al.  Novel approach to fabricate porous sponges of poly(D,L-lactic-co-glycolic acid) without the use of organic solvents. , 1996, Biomaterials.

[33]  M. Huneault,et al.  Preparation of interconnected poly(ε-caprolactone) porous scaffolds by a combination of polymer and salt particulate leaching , 2006 .

[34]  Robert Langer,et al.  Biodegradable Polymer Scaffolds for Tissue Engineering , 1994, Bio/Technology.

[35]  Sang Ho Cho,et al.  Fabrication and characterization of hydrophilic poly(lactic-co-glycolic acid)/poly(vinyl alcohol) blend cell scaffolds by melt-molding particulate-leaching method. , 2003, Biomaterials.

[36]  K. Leong,et al.  The design of scaffolds for use in tissue engineering. Part I. Traditional factors. , 2001, Tissue engineering.

[37]  J. Vacanti,et al.  Tissue engineering. , 1993, Science.

[38]  P. Ma,et al.  Biodegradable polymer scaffolds with well-defined interconnected spherical pore network. , 2001, Tissue engineering.

[39]  D J Mooney,et al.  Bioabsorbable polymer scaffolds for tissue engineering capable of sustained growth factor delivery. , 2000, Journal of controlled release : official journal of the Controlled Release Society.

[40]  D. Hutmacher.  Polymers for Medical Applications , 2001 .

[41]  C. M. Agrawal,et al.  Biodegradable polymeric scaffolds for musculoskeletal tissue engineering. , 2001, Journal of biomedical materials research.

[42]  Joo L. Ong,et al.  Diffusion in Musculoskeletal Tissue Engineering Scaffolds: Design Issues Related to Porosity, Permeability, Architecture, and Nutrient Mixing , 2004, Annals of Biomedical Engineering.

[43]  R Langer,et al.  Neocartilage formation in vitro and in vivo using cells cultured on synthetic biodegradable polymers. , 1993, Journal of biomedical materials research.

[44]  R Langer,et al.  Laminated three-dimensional biodegradable foams for use in tissue engineering. , 1993, Biomaterials.

[45]  C. Agrawal,et al.  Basics of polymeric scaffolds for tissue engineering , 2006 .

[46]  A. Mikos,et al.  The Importance of New Processing Techniques in Tissue Engineering , 1996, MRS bulletin.

[47]  Y. Ikada,et al.  Porous biodegradable polyesters. I. Preparation of porous poly(L‐lactide) films by extraction of poly(ethylene oxide) from their blends , 2000 .

[48]  A. Karim,et al.  Development of Biodegradable Polymer Scaffolds Using Co-Extrusion , 2000 .

[49]  D. Mooney.  Tissue engineering with biodegradable polymer matrices , 1996, Proceedings of the 1996 Fifteenth Southern Biomedical Engineering Conference.

[50]  C. Manke,et al.  Effects of Dissolved Gas on Viscoelastic Scaling and Glass Transition Temperature of Polystyrene Melts , 2001, Industrial & Engineering Chemistry Research.

[51]  C. Manke,et al.  Rheology of molten polystyrene with dissolved supercritical and near‐critical gases , 1999 .

[52]  Robert M. Nerem,et al.  CHAPTER 2 – THE CHALLENGE OF IMITATING NATURE , 2000 .

[53]  G. Njus,et al.  Processing Methodologies for Polycaprolactone-Hydroxyapatite Composites: A Review , 2006 .

[54]  B D Boyan,et al.  Role of material surfaces in regulating bone and cartilage cell response. , 1996, Biomaterials.

[55]  Y. Inoue,et al.  Miscibility and phase structure of binary blends of poly(L‐lactide) and poly(vinyl alcohol) , 2001 .

[56]  E. Wintermantel,et al.  MuCell® technology for injection molding: A processing method for polyether-urethane scaffolds , 2005 .

[57]  David J Mooney,et al.  Salt fusion: an approach to improve pore interconnectivity within tissue engineering scaffolds. , 2002, Tissue engineering.