Effect of replacing polyol by organosolv and kraft lignin on the property and structure of rigid polyurethane foam

BackgroundLignin is one of the three major components in plant cell walls, and it can be isolated (dissolved) from the cell wall in pretreatment or chemical pulping. However, there is a lack of high-value applications for lignin, and the commonest proposal for lignin is power and steam generation through combustion. Organosolv ethanol process is one of the effective pretreatment methods for woody biomass for cellulosic ethanol production, and kraft process is a dominant chemical pulping method in paper industry. In the present research, the lignins from organosolv pretreatment and kraft pulping were evaluated to replace polyol for producing rigid polyurethane foams (RPFs).ResultsPetroleum-based polyol was replaced with hardwood ethanol organosolv lignin (HEL) or hardwood kraft lignin (HKL) from 25% to 70% (molar percentage) in preparing rigid polyurethane foam. The prepared foams contained 12-36% (w/w) HEL or 9-28% (w/w) HKL. The density, compressive strength, and cellular structure of the prepared foams were investigated and compared. Chain extenders were used to improve the properties of the RPFs.ConclusionsIt was found that lignin was chemically crosslinked not just physically trapped in the rigid polyurethane foams. The lignin-containing foams had comparable structure and strength up to 25-30% (w/w) HEL or 19-23% (w/w) HKL addition. The results indicated that HEL performed much better in RPFs and could replace more polyol at the same strength than HKL because the former had a better miscibility with the polyol than the latter. Chain extender such as butanediol could improve the strength of lignin-containing RPFs.

[1]  T. Hatakeyama,et al.  Glass transition of rigid polyurethane foams derived from sodium lignosulfonate mixed with diethylene, triethylene and polyethylene glycols , 2004 .

[2]  J. Saddler,et al.  Organosolv ethanol lignin from hybrid poplar as a radical scavenger: relationship between lignin structure, extraction conditions, and antioxidant activity. , 2006, Journal of agricultural and food chemistry.

[3]  X. Pan.  Atmospheric acetic acid pulping of rice straw. IV. Physico-chemical characterization of acetic acid lignins from rice straw and woods. 2. , 1999 .

[4]  Xuejun Pan,et al.  Atmospheric Acetic Acid Pulping of Rice Straw IV: Physico-Chemical Characterization of Acetic Acid Lignins from Rice Straw and Woods. Part 1. Physical Characteristics , 1999 .

[5]  Wendy A. Warr,et al.  Chemical Structures , 1988 .

[6]  J. Lora,et al.  The ALCELL process--a proven alternative to kraft pulping , 1991 .

[7]  Wolfgang G. Glasser,et al.  Recent Industrial Applications of Lignin: A Sustainable Alternative to Nonrenewable Materials , 2002 .

[8]  S. Kubo,et al.  Miscibility and Hydrogen Bonding in Blends of Poly(ethylene oxide) and Kraft Lignin , 2003 .

[9]  R. Thring,et al.  MOLECULAR WEIGHT EFFECTS OF THE SOFT SEGMENT ON THE ULTIMATE PROPERTIES OF LIGNIN-DERIVED POLYURETHANES , 2004 .

[10]  John N. Saddler,et al.  Pretreatment of Lodgepole Pine Killed by Mountain Pine Beetle Using the Ethanol Organosolv Process: Fractionation and Process Optimization , 2007 .

[11]  A. Ragauskas,et al.  Kraft Lignin-Based Rigid Polyurethane Foam , 2012 .

[12]  M. D’Auria,et al.  Polyurethanes and polyesters from lignin , 2005 .

[13]  Roger M. Rowell,et al.  Handbook of wood chemistry and wood composites. , 2005 .

[14]  T. Hatakeyama,et al.  Lignin Structure, Properties, and Applications , 2009 .

[15]  Warren Mabee,et al.  Biorefining of softwoods using ethanol organosolv pulping: preliminary evaluation of process streams for manufacture of fuel-grade ethanol and co-products. , 2005, Biotechnology and bioengineering.

[16]  Michael Szycher,et al.  Szycher's Handbook of Polyurethanes , 2012 .

[17]  A. Ragauskas,et al.  Ethanol organosolv lignin-based rigid polyurethane foam reinforced with cellulose nanowhiskers , 2012 .

[18]  Shiro Saka,et al.  Bioconversion of hybrid poplar to ethanol and co‐products using an organosolv fractionation process: Optimization of process yields , 2006, Biotechnology and bioengineering.

[19]  R. Thring,et al.  Synthesis of polyurethanes from solvolysis lignin using a polymerization catalyst: Mechanical and thermal properties , 2003 .

[20]  P. Stockburger.  AN OVERVIEW OF NEAR-COMMERICAL AND COMMERCIAL SOLVENT-BASED PULPING PROCESSES , 1993 .

[21]  Xuejun Pan,et al.  Atmospheric Acetic Acid Pulping of Rice Straw IV: Physico-Chemical Characterization of Acetic Acid Lignins from Rice Straw and Woods. Part 2. Chemical Structures , 1999 .

[22]  X. Pan,et al.  Chemistry and Reactions of Forest Biomass in Biorefining , 2011 .

[23]  J. Saddler,et al.  The bioconversion of mountain pine beetle‐killed lodgepole pine to fuel ethanol using the organosolv process , 2008, Biotechnology and bioengineering.

[24]  Xiao Zhang,et al.  Sustainable production of fuels, chemicals, and fibers from forest biomass , 2011 .

[25]  Alírio E. Rodrigues,et al.  Optimization study of lignin oxypropylation in view of the preparation of polyurethane rigid foams , 2009 .

[26]  V. Popa,et al.  Properties of lignin–polyurethane films prepared by casting method , 2004 .

[27]  J. Ralph,et al.  Chapter 6 – Lignin , 2010 .