Preparation and properties of B4C-TiB2 ceramics prepared by spark plasma sintering

By doping titanium hydride (TiH2) into boron carbide (B4C), a series of B4C + x wt% TiH2 (x = 0, 5, 10, 15 and 20) composite ceramics were obtained through spark plasma sintering (SPS). The effects of sintering temperature and the amount of TiH2 additive on the microstructure, mechanical and electrical properties of the sintered B4C-TiB2 composite ceramics were investigated. Powder mixtures of B4C with 0−20 wt% TiH2 were heated from 1400 to 1800 °C for 20 minutes under 50 MPa. The results indicated that higher sintering temperatures contributed to greater ceramic density. With increasing TiH2 content, titanium diboride (TiB2) formed between the TiH2 and B4C matrix. This effectively improved Young’s modulus and fracture toughness of the composite ceramics, significantly improving their electrical properties: the electrical conductivity reached 114.9 S·cm−1 at 1800 °C when x = 20. Optimum mechanical properties were obtained for the B4C ceramics sintered with 20 wt% TiH2, which had a relative density of 99.9 ± 0.1%, Vickers hardness of 31.8 GPa and fracture toughness of 8.5 MPa·m1/2. The results indicated that the doping of fine Ti particles into the B4C matrix increased the conductivity and the fracture toughness of B4C.

[1]  Yi He,et al.  Enhanced strength and ductility of superhard boron carbide through injecting electrons , 2020 .

[2]  T. Goto,et al.  Fabrication of Lu2Ti2O7-Lu3NbO7 solid solution transparent ceramics by spark plasma sintering and their electrical conductivities , 2020 .

[3]  Mingzhi Wang,et al.  A novel non-stoichiometric medium-entropy carbide stabilized by anion vacancies , 2020 .

[4]  J. Reis,et al.  Combination of temperature and electrical conductivity on semiconductor graphite/epoxy composites , 2020 .

[5]  Yong Pan,et al.  Exploring the novel structure, transportable capacity and thermodynamic properties of TiH2 hydrogen storage material , 2020, International Journal of Energy Research.

[6]  B. Kumar,et al.  Sintering and sliding wear studies of B4C-SiC composites , 2020 .

[7]  A. Nishimoto,et al.  Simultaneous Boronizing and Carburizing of Titanium via Spark Plasma Sintering , 2019, MATERIALS TRANSACTIONS.

[8]  S. Yamashita,et al.  Progress in pressureless sintering of boron carbide ceramics – a review , 2019, Advances in Applied Ceramics.

[9]  Xingwang Cheng,et al.  Spark plasma sintering of B4C-TiB2-SiC composite ceramics using B4C, Ti3SiC2 and Si as starting materials , 2018, Ceramics International.

[10]  Sergey N. Grigoriev,et al.  The Effect of TiC Additive on Mechanical and Electrical Properties of Al2O3 Ceramic , 2018, Applied Sciences.

[11]  Z. Fu,et al.  Microstructures and mechanical properties of B4C-TiB2-SiC composites fabricated by ball milling and hot pressing , 2018, Journal of the European Ceramic Society.

[12]  T. Sekino,et al.  Fine Ti‐dispersed Al2O3 composites and their mechanical and electrical properties , 2018 .

[13]  H. G. Zhang,et al.  Fracture behavior of nuclear graphite under three-point bending tests , 2017 .

[14]  A. Mukasyan,et al.  Bulk boron carbide nanostructured ceramics by reactive spark plasma sintering , 2017 .

[15]  Z. Zhong,et al.  High toughness and electrical discharge machinable B4C-TiB2-SiC composites fabricated at low sintering temperature , 2017 .

[16]  L. Sun,et al.  Methodology for measuring fracture toughness of ceramic materials by instrumented indentation test with vickers indenter , 2017 .

[17]  Wei Zhang,et al.  Study of static and dynamic behavior of TiB2–B4C composite , 2016 .

[18]  C. Chen,et al.  Enhancement of sinterability and mechanical properties of B4C ceramics using Ti3AlC2 as a sintering aid , 2015 .

[19]  H. Baharvandi,et al.  Effect of different additives on the sintering ability and the properties of B4C–TiB2 composites , 2015 .

[20]  H. Baharvandi,et al.  Comparing the effects of different sintering methods for ceramics on the physical and mechanical properties of B4C–TiB2 nanocomposites , 2015 .

[21]  Z. Fu,et al.  Microstructure and mechanical properties of B4C densified by spark plasma sintering with Si as a sintering aid , 2015 .

[22]  Manjeet Kumar,et al.  One step reduction of Boric Acid to boron carbide nanoparticles , 2014 .

[23]  R. White,et al.  Mechanical properties and deformation mechanisms of B4C–TiB2 eutectic composites , 2014 .

[24]  Y. Sakka,et al.  Tough and dense boron carbide obtained by high-pressure (300 MPa) and low-temperature (1600°C) spark plasma sintering , 2014 .

[25]  K. Sairam,et al.  Influence of spark plasma sintering parameters on densification and mechanical properties of boron carbide , 2014 .

[26]  K. Oh,et al.  Fabrication of for , 2014 .

[27]  S. Suresh,et al.  Aluminium-Titanium Diboride (Al-TiB2) Metal Matrix Composites: Challenges and Opportunities , 2012 .

[28]  R. Haber,et al.  Boron Carbide: Structure, Properties, and Stability under Stress , 2011 .

[29]  R. White,et al.  Microstructure and hardness scaling in laser-processed B4C–TiB2 eutectic ceramics , 2011 .

[30]  A. Bhowmick,et al.  A review on the mechanical and electrical properties of graphite and modified graphite reinforced polymer composites , 2011 .

[31]  H. Ru,et al.  Synthesis and properties of hot pressed B4C–TiB2 ceramic composite , 2010 .

[32]  P. He,et al.  Kinetic study on nonisothermal dehydrogenation of TiH2 powders , 2009 .

[33]  L. Pei,et al.  B4C/TiB2 composite powders prepared by carbothermal reduction method , 2009 .

[34]  M. Ishihara,et al.  Effects of ion irradiation on the hardness properties of graphites and C/C composites by indentation tests , 2008 .

[35]  S. Yamanaka,et al.  Electrical and thermal properties of titanium hydrides , 2006 .

[36]  A. Fok,et al.  Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens , 2003 .

[37]  G. Neighbour,et al.  Crack growth resistance in nuclear graphites , 2002 .

[38]  V. Krstić,et al.  High strength-high toughness B4C-TiB2 composites , 2000 .

[39]  R. T. Pascoe,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements , 1981 .