A concise interface constitutive law for analysis of delamination and splitting in composite materials and its application to scaled notched tensile specimens

A concise constitutive law for cohesive interfaces is proposed in this paper. A new state variable is introduced to track the extent of damage accumulated at the interface. The constitutive equations not only account for mixed-mode delamination propagation in composite materials, but also satisfactorily deal with mode ratio change during the debonding process. The interface model is implemented in the LS-DYNA explicit finite element code. The model has been applied to scaled open hole tension tests on laminated composite material. Comparison between numerical results and experiments shows good correlation for failure modes and strengths for a range of different specimen sizes. Copyright © 2006 John Wiley & Sons, Ltd.

[1]  M. A. Crisfield,et al.  Progressive Delamination Using Interface Elements , 1998 .

[2]  M. Crisfield,et al.  Finite element interface models for the delamination analysis of laminated composites: mechanical and computational issues , 2001 .

[3]  de R René Borst,et al.  On the numerical integration of interface elements , 1993 .

[4]  John C. Brewer,et al.  Quadratic Stress Criterion for Initiation of Delamination , 1988 .

[5]  Ronald Krueger,et al.  Analysis of Ninety Degree Flexure Tests for Characterization of Composite Transverse Tensile Strength , 2001 .

[6]  J. Hutchinson,et al.  The relation between crack growth resistance and fracture process parameters in elastic-plastic solids , 1992 .

[7]  Alberto Corigliano,et al.  Modeling and simulation of crack propagation in mixed-modes interlaminar fracture specimens , 1996 .

[8]  Stephen R Reid,et al.  A continuum damage model for delaminations in laminated composites , 2003 .

[9]  Ronald C. Averill,et al.  Finite Element Interface Technology for Modeling Delamination Growth in Composite Structures , 2002 .

[10]  P.M.S.T. de Castro,et al.  Prediction of compressive strength of carbon–epoxy laminates containing delamination by using a mixed-mode damage model , 2000 .

[11]  Michael R Wisnom,et al.  A combined stress-based and fracture-mechanics-based model for predicting delamination in composites , 1993 .

[12]  E. M. Wu,et al.  CRACK EXTENSION IN FIBERGLASS REINFORCED PLASTICS , 1965 .

[13]  I. Raju.  Calculation of strain-energy release rates with higher order and singular finite elements , 1987 .

[14]  F. L. Matthews,et al.  Predicting Progressive Delamination of Composite Material Specimens via Interface Elements , 1999 .

[15]  W. Cui,et al.  A comparison of failure criteria to predict delamination of unidirectional glass/epoxy specimens waisted through the thickness , 1992 .

[16]  O. Allix,et al.  Some aspects of interlaminar degradation in composites , 2000 .

[17]  Larsgunnar Nilsson,et al.  Modeling of delamination using a discretized cohesive zone and damage formulation , 2002 .

[18]  P. Camanho,et al.  Numerical Simulation of Mixed-Mode Progressive Delamination in Composite Materials , 2003 .

[19]  F. Chang,et al.  Modelling of splitting and delamination in notched cross-ply laminates , 2000 .

[20]  John D. Whitcomb,et al.  Analysis of instability-related growth of a through-width delamination , 1984 .

[21]  Michael R Wisnom,et al.  Size effects in the testing of fibre-composite materials , 1999 .

[22]  M. Kanninen,et al.  A finite element calculation of stress intensity factors by a modified crack closure integral , 1977 .

[23]  Laurent Daudeville,et al.  Delamination analysis by damage mechanics: Some applications , 1995 .

[24]  Antonio Miravete,et al.  Application of the Finite-Element Method to Predict the Onset of Delamination Growth , 2004 .

[25]  Paul Robinson,et al.  Numerical simulation of fatigue‐driven delamination using interface elements , 2005 .